A thermos bottle and gall pad technology, which is used in household appliances, heat-insulating utensils, applications, etc., can solve the problems of asbestos piercing into the cavity wall of the respiratory tract and inflammation of the respiratory tract of operators, and achieve the effect of eliminating harm and simple production process.

Inactive Publication Date: 2012-12-19
王晓鸿
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, asbestos is the main ingredient used in thermos liner pads, and its material form is fiber and powder. Due to the special form of asbestos, during a series of production processes such as preparation, molding, and drying, asbestos fibers or The

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1:

[0029] A thermos flask bottle liner pad, its formula composition and weight are:

[0030] Alumina fiber: 550g

[0031] Light calcium carbonate: 50g

[0032] Clay: 1900g

[0033] Montmorillonite: 250g

[0034] Quartz: 550g

[0035] Deionized water: 1000g.

[0036] Preparation method: fully stir and mix alumina fiber, light calcium carbonate, clay, montmorillonite and quartz at a stirring speed of 1500 rpm, stirring for 10 minutes to obtain a mixed material; add deionization to the mixed material Continue to stir the water for 30 minutes, the stirring speed is 1000 rpm, and then pour the material into the mold to dry and shape, the drying temperature is 60 ℃, the drying time is 15 minutes, and the bottle gasket can be obtained after demolding .

Example Embodiment

[0037] Example 2:

[0038] A thermos flask bottle liner pad, its formula composition and weight are:

[0039] Alumina fiber: 1000g

[0040] Light calcium carbonate: 240g

[0041] Clay: 3000g

[0042] Montmorillonite: 750g

[0043] Quartz: 1000g

[0044] Deionized water: 2500g.

[0045] Preparation method: fully stir and mix alumina fiber, light calcium carbonate, clay, montmorillonite, and quartz at a stirring speed of 2000 rpm, stirring for 30 minutes to obtain a mixed material; add deionization to the mixed material The water continues to stir for 60 minutes, the stirring speed is 1500 rpm, and then the material is poured into the mold to dry and shape, the drying temperature is 200 ℃, the drying time is 5 minutes, and the bottle gasket can be obtained after demolding .

Example Embodiment

[0046] Example 3:

[0047] A thermos flask bottle liner pad, its formula composition and weight are:

[0048] Alumina fiber: 150g

[0049] Light calcium carbonate: 30g

[0050] Clay: 570g

[0051] Montmorillonite: 100g

[0052] Quartz: 150g

[0053] Deionized water: 350g.

[0054] Preparation method: fully stir and mix alumina fiber, light calcium carbonate, clay, montmorillonite, and quartz at a stirring speed of 2000 rpm, stirring for 20 minutes to obtain a mixed material; add deionization to the mixed material Continue to stir the water for 450 minutes, the stirring speed is 1500 rpm, and then pour the material into the mold to dry and shape, the drying temperature is 120 ℃, the drying time is 10 minutes, after demolding, the bottle gasket can be prepared .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a bottle liner pad of a thermos bottle. The bottle liner pad comprises the following formula consisting of components in parts by weight: 10 to 20 parts of alumina fiber, 1 to 4.8 parts of light-mass calcium carbonate, 40 to 60 parts of clay, 5 to 15 parts of montmorillonite, 10 to 20 parts of quartz and 20 to 50 parts of deionized water. The bottle liner pad is extremely high in hardness and has certain flexibility; raw materials are harmless to human bodies; the production process is simple; the pollution is avoided in the production process; other harmful chemical components are not required to be added, namely the production process and the using process do not influence the human bodies; particularly, the harm of asbestic dust to the respiratory tract and the whole body of an operator is avoided; and therefore, the bottle liner pad meets the environment-friendly requirement.

Description

technical field [0001] The invention relates to a liner pad for a thermos bottle. Background technique [0002] At present, asbestos is the main ingredient used in thermos liner pads, and its material form is fiber and powder. Due to the special form of asbestos, during a series of production processes such as preparation, molding, and drying, asbestos fibers or The powder is easily scattered in the air and inhaled by the operator into the respiratory tract, causing inflammation of the operator's respiratory tract, and even fibrous asbestos penetrates into the cavity wall of the respiratory tract, resulting in silicosis. Because asbestos is carcinogenic, there is the possibility of infecting cancerous mesothelioma and lung cancer in the serious environment of asbestos dust. Therefore, the production of this liner liner needs to be improved. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a thermos liner liner, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A47J41/00C04B28/00
Inventor 王晓鸿王怀河
Owner 王晓鸿
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap