Heat-vulcanization top coating adhesive for bonding metal and natural rubber

A natural rubber, thermal vulcanization technology, used in adhesives, rubber-derived adhesives, adhesive types, etc., and can solve problems such as storage stability

Inactive Publication Date: 2012-12-05
TONGJI UNIV
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims to replace aromatic nitroso compounds, and at the same time solve the problem of storage stability in the combined use of oxidizing agents and nitroso compound precursors, aiming to provide a thermally vulcanized surface coating adhesive for bonding metal and natural rubber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 12 parts of chlorinated polypropylene (50% solids, Eastman, CP343-1) were mixed with 4 parts of chlorinated natural rubber (Bayer, Pergut). 10 parts of xylene was added for dissolution. Then add 4 parts of crosslinking agent (p-benzoquinone dioxime: nano-copper oxide = 1:1, mass ratio), 5 parts of carbon black, 1.5 parts of sulfur, 63.5 parts of mixed xylene, and use a horizontal sand mill for grinding. The fineness is controlled at 5-7μ.

Embodiment 2

[0023] 10 parts of chlorinated polypropylene (50% solids, Eastman, CP343-1) were mixed with 5 parts of chlorinated natural rubber (Bayer, Pergut). 10 parts of xylene was added for dissolution. Then add 4 parts of crosslinking agent (p-benzoquinone dioxime: nano-copper oxide = 1:1, mass ratio), 5 parts of carbon black, 1.5 parts of sulfur, 64.5 parts of mixed xylene, and use a horizontal sand mill for grinding. The fineness is controlled at 5-7μ.

Embodiment 3

[0025] 8 parts of chlorinated polypropylene (50% solids, Eastman, CP343-1) were mixed with 3.5 parts of chlorinated natural rubber (Bayer, Pergut). 10 parts of xylene was added for dissolution. Then add 4 parts of crosslinking agent (p-benzoquinone dioxime: nano-copper oxide = 1:1, mass ratio), 5 parts of carbon black, 1.5 parts of sulfur, 68 parts of mixed xylene, and use a horizontal sand mill for grinding. The fineness is controlled at 5-7μ.

[0026] Test Results

[0027] Example Peel strength (KN / m) damage type stability test 1 13.7 100%R no obvious thickening 2 12.9 100%R no obvious thickening 3 12.4 100%R no obvious thickening

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a heat-vulcanization top coating adhesive for bonding metal and natural rubber. The adhesive consists of the following components in part by weight (the total weight is based on 100 parts): 7.5 to 10 parts of chlorinated polyolefin and halogenated rubber, 3 to 5 parts of cross-linking agent, 5 to 7.5 parts of filler, 1 to 1.5 parts of sulfur and the balance of solvent. The top coating adhesive provided by the invention can replace the conventional aromatic nitroso compounds which serve as a vulcanizing agent and a cross-linking agent; and the problem that the adhesive is low in storage stability in the process of using nitroso precursors to cooperate with an oxidizer is solved.

Description

Technical field [0001] The present invention belongs to the field of rubber and metal bonding, which involves a thermal sulfide coating adhesive for a metal and natural rubber adhesion. Background technique [0002] The adhesion between rubber and metal has a long history, which can be traced back to 1850. The current adhesion method can be divided into direct bonding method, hard rubber method, brass plating method, and adhesive bonding method.Among them, the adhesive method is the most widely used method at present.Phenolic resin, polykeein, and halide polymers are three types of substrate materials commonly used in adhesives. [0003] Phenolic resin is mainly used for polar rubber, and can also be used as a primer material for bonding non -polar rubber (such as Chenlok205).Dylocyanate often refers to trigzyl methane trigemanate. This rubber adhesive is suitable for bonding of polar rubber (NBR, CR) and adhesion to non -polar rubber such as NR and EPDM. The isocyanate is also u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/28C09J115/00C09J11/06C09J11/04
Inventor 钟震叶宽贾梦虹任天斌
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com