Optical film and method for producing the same

A manufacturing method and technology of optical films, applied in the field of optical films, can solve the problems of low anti-glare, unclear image display, easy to produce cracks, etc., to improve keystroke durability, improve scratch resistance and mechanical properties, The effect of suppressing oozing

Active Publication Date: 2012-11-14
DAICEL CHEM IND LTD
View PDF10 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, in this anti-glare sheet, since only curable resin is used to form the hard coat layer, external stress cannot be relieved, cracks are likely to occur, and streaks are generated along the bending direction even if it is slightly bent.
In particular, the durability is not sufficient for applications that receive repeated keystrokes like the upper transparent electrode of a touch panel
In addition, the optical characteristics are insufficient, the anti-glare property is low, not only the glare can be seen, but also the display of the transmitted image is not clear
In addition, in order to aggregate a large amount of silica fine particles, it is necessary to use an aggregating agent, which causes bleeding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optical film and method for producing the same
  • Optical film and method for producing the same
  • Optical film and method for producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0175] Using a cellulose triacetate film (manufactured by Fujifilm Co., Ltd., TAC, thickness 80 μm) as a transparent film, the hard coat coating liquid HC-1 was coated on the film with a bar coater #30, and then Dry at 70°C for 1 minute. Ultraviolet irradiation device (manufactured by Ushio Electric Co., Ltd., high-pressure mercury lamp, ultraviolet irradiation amount: 800mJ / cm 2 ) to UV-cure the coating film to form a hard coating with a hard coating and a concave-convex structure. The thickness of the hard coat layer in the obtained optical film was about 10 μm. The surface of the obtained optical film was observed with a laser microscope, and the results are shown in figure 1 .

Embodiment 2

[0177]An optical film was produced in the same manner as in Example 1 except that hard coat coating liquid HC-2 was used instead of hard coat coating liquid HC-1.

Embodiment 3

[0179] An optical film was produced in the same manner as in Example 1 except that hard coat coating liquid HC-3 was used instead of hard coat coating liquid HC-1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

Disclosed is an optical film in which a hard coat layer comprising a curable resin precursor that has been cured, a thermoplastic resin, and microparticles having an average primary particle diameter of 1 to 100 nm is formed on at least one surface of a transparent film. The thermoplastic resin can be a thermoplastic resin (particularly a cellulose derivative) that is nonreactive with the curable resin precursor. The ratio of metal oxide microparticles is 0.5 to 4 parts by weight per 100 parts by weight of the curable resin precursor. The metal oxide microparticles can be at least one type of microparticles selected from the group comprising antimony-containing tin oxide, tin oxide, and zinc oxide. The curable resin precursor can be a precursor having four functional groups or more. The optical film has excellent anti-glare properties or anti-Newton ring properties, and has excellent scratch resistance and mechanical characteristics.

Description

technical field [0001] The present invention relates to an optical film used for a display device in a display portion of an electric or electronic device or a precision device, and a method for producing the same. Background technique [0002] In recent years, liquid crystal displays (LCDs) have made remarkable progress and are rapidly spreading as display devices for television (TV) applications or animation display applications. For example, through the development of liquid crystal materials with high-speed response and the improvement of drive methods such as drive acceleration, we have overcome the animation display that liquid crystals were not good at in the past, and are also advancing production technology innovations to cope with the increase in display size. [0003] For applications such as televisions and monitors, where image quality is important, or video cameras used outdoors where there is strong external light, the surface of these displays is usually trea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B1/10B32B7/02B32B27/18G02B1/11G02F1/1335
CPCG02B1/105Y10T428/256Y10T428/25Y10T428/24413G02B1/16G02B1/14B32B5/16B32B7/02B32B27/18B32B27/26C08F2/48G02B1/00G02B1/10G02F1/1335G02F1/133502
Inventor 牛田浩明林正树
Owner DAICEL CHEM IND LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com