A technology of mirror silver and ink, applied in the field of ink, can solve the problems of high cost, pollution, large corrosive substances, etc.
Active Publication Date: 2014-08-20
SHENZHEN TCL NEW-TECH CO LTD
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, these two methods are extremely expensive, and produce a large amount of corrosive substances, causing serious pollution
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0023] 1. Preparation of mirror silver ink
[0024] Step 1, by the content of each component specified in Table 1, the following components: SiO 2 、Al 2 o 3 、Cr 2 o 3 , Ca 3 (PO 4 ) 2 、Na 2 SiF 6 Grind in an environment of 200-300°C to form uniform inorganic mixed particles, and cool naturally to room temperature;
[0025] Step 2, pulverizing and grinding the cooled inorganic mixture particles into a powdered inorganic mixture with a particle size of 6 μm-10 μm;
[0026] Step 3. According to the content of each component specified in Table 1, add the following components: pigments, fillers, additives, and solvents to the powdered inorganic mixture, and stir evenly at 20-30°C, and then use The grinding process grinds into a fluid mixture with a particle size of 6 μm-10 μm, and the fluid mixture is mirror silver ink.
[0027] 2. Use and performance test of mirror silver ink
[0028] Step 1. Provide a plastic part (TV panel), silk screen fixture, and fix the above pla...
Embodiment 2
[0033] Repeat the method of Example 1 according to the content of each component specified in Table 1, and the surface brightness, silver color, and metallic texture of the plastic part printed by the silk screen of this example; Temperature tolerance, the measurement results are shown in Table 2.
Embodiment 3
[0035] Repeat the method of Example 1 according to the content of each component specified in Table 1, and the surface brightness, silver color, and metallic texture of the plastic part printed by the silk screen of this example; Temperature tolerance, the measurement results are shown in Table 2.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses mirror silver ink and a preparation method thereof, wherein the mirror silver ink comprises following components in part by mass: 70-80 parts of inorganic composite material and 20-30 parts of organic high molecular material; the inorganic composite material comprises following components: 1.4-2.5 parts of SiO2, 20-30 parts of Al2O3, 24-38 parts of Cr2O3, 2-10 parts of Ca3 (PO4) and 3-5 parts of Na2SiF6; and the organic high molecular material comprises following components: 10-24 parts of pigment, 1.6-5 parts of filler, 0.25-1 part of assistant and 2.5-4 parts of solvent. In the mirror silver ink and the preparation method, provided by the invention, the mirror silver ink prepared by the preparation method can be directly silkscreened on the surface of a plastic part, so that the surface of the plastic part has effects of mirror surface, metallic feeling and strong silvery reflection.
Description
technical field [0001] The invention relates to the technical field of inks, in particular to a mirror silver ink and a preparation method thereof. Background technique [0002] At present, when the mirror silver ink on the market is screen-printed on the back of transparent materials (acrylic, PVC, glass), the directional arrangement of silver powder scales can be achieved. Due to the directional arrangement, the surface of the transparent material depends on the refraction of the material itself and the reflection of the surface to reflect the mirror surface. Metallic, silver reflective effect. However, if this mirror silver ink is printed on the surface of plastic parts, the surface of the plastic parts does not have a bright metallic feel, and this ink has low adhesion, is not wear-resistant, and is not resistant to high temperatures. [0003] In order to make the surface of the plastic parts achieve the effect of mirror surface, metallic feeling, and strong silver refl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.