Organic hybridized telluride having photocatalytic performance and preparation thereof

A technology of organic hybridization and photocatalytic activity, applied in organic chemistry, organic compound/hydride/coordination complex catalysts, chemical/physical processes, etc., can solve the problems of incomplete degradation of organic dyes and limited photocatalytic applications , to achieve the effect of good repeatability and simple process

Inactive Publication Date: 2012-10-03
YULIN NORMAL UNIVERSITY
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the research on photocatalytic degradation of organic dye wastewater mainly focuses on oxygen-containing semiconductor photocatalysts such as titanium dioxide and zinc oxide. However, these catalysts tend to form stable intermediates during the degradation of some organic dyes and cannot be completely degraded. Organic dyes, therefore, it is necessary to prepare and optimize new catalysts according to the photocatalytic degradation mechanism of different types of organic pollutants
In addition, oxygen-containing semiconductor photocatalysts generally have a large band gap (for example, the band gaps of titanium dioxide and zinc oxide are 3.20eV and 3.37eV, respectively), and only in the ultraviolet range (less than 5% of the total solar energy) Responsive, but non-responsive in the visible light range (about 43% of the total solar energy), which greatly limits their photocatalytic applications under visible light irradiation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic hybridized telluride having photocatalytic performance and preparation thereof
  • Organic hybridized telluride having photocatalytic performance and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1. Compound Preparation

[0023] InCl 3 0.0179g (0.07936mmol), Te 0.0057g (0.04467mmol), MgCl 2 ·6H 2 O0.0206g (0.1015mmol) and 3ml of diethylenetriamine were added to a hard glass tube, and the two ends of the glass tube were sealed. Keep at 170°C for 7 days, then cool down to room temperature naturally. Blocky crystals appeared. The crystal sample was taken out, washed with ethanol three times, and dried in a desiccator to obtain 0.0390 g of diethylenetriamine monohydrate indium telluride crystal. Yield 40% (based on tellurium).

Embodiment 2

[0025] InCl 3 0.0179g (0.07936mmol), Te0.0057g (0.04467mmol), MgCl 2 ·6H 2 O0.0206g (0.1015mmol) and 3ml of diethylenetriamine were added to a hard glass tube, and the two ends of the glass tube were sealed. Keep at 160°C for 7 days, then cool down to room temperature naturally. Blocky crystals appeared. The crystal sample was taken out, washed with ethanol three times, and dried in a desiccator to obtain 0.0390 g of diethylenetriamine monohydrate indium telluride crystal. Yield 40% (based on tellurium).

Embodiment 3

[0027] InCl 3 0.0179g (0.07936mmol), Te0.0057g (0.04467mmol), MgCl 2 ·6H 2 O0.0206g (0.1015mmol) and 3ml of diethylenetriamine were added to a hard glass tube, and the two ends of the glass tube were sealed. Keep at 180°C for 7 days, then cool down to room temperature naturally. Blocky crystals appeared. The crystal sample was taken out, washed with ethanol three times, and dried in a desiccator to obtain 0.0390 g of diethylenetriamine monohydrate indium telluride crystal. Yield 40% (based on tellurium).

[0028] The prepared diethylenetriamine indium telluride monohydrate crystal was scanned in the ω-θ mode with Mo Kα (λ=0.071073nm) rays monochromated by a graphite monochromator on a Bruke smart APEXII CCD diffractometer. At 296K, a total of 1271 diffraction spots were collected. By the full matrix least squares method for F 2 The modified structural analysis was done with the SHELXL-97 software package. The molecular formula of the compound is C 8 h 16 In 6 N 6 o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an organic hybridized telluride having photocatalytic performance and a preparation thereof. The organic hybridized telluride having photocatalytic performance has a chemical name of monohydrate divinyl triamine indium telluride. A preparation method comprises the following steps: preparing crystals through solvothermal synthesis method; taking InCl3, MgCl2.6H2O and Te with molar ratio of 1.6: 1: 5 as raw materials; utilizing diethylenetriamine as solvent; reacting at 160-180 degrees centigrade for 7 d to obtain yellow rodlike crystals; cooling; washing with ethanol; and drying at constant temperature to obtain the compound that is monohydrate divinyl triamine indium telluride. According to the invention, the preparation method provided by the invention has the advantages of simple processes and good repeatability. The compound provided by the invention has the advantages that the compound is not dissolved in general solvent easily.

Description

technical field [0001] The invention relates to a compound with photocatalytic performance and its preparation, in particular to an organic hybrid telluride with photocatalytic performance and its preparation. Background technique [0002] Since Japanese scholars Fujishima and Honda discovered in 1972 that titanium dioxide photocatalysts can actually split water to produce hydrogen, people have been interested in photocatalytic technology. Photocatalytic technology not only shows attractive applications in photocatalytic decomposition of water to produce hydrogen and photocatalytic reduction of carbon dioxide to prepare organic matter, but also it is a new type of modern environmental pollution control technology, because it has obvious effects on the main organic pollutants in the environment. Excellent degradation effect, easy control of operating conditions, strong oxidation ability, no secondary pollution, has obvious advantages. Therefore, photocatalysts with photocata...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07F5/00B01J31/22C02F1/32
CPCY02W10/37
Inventor 周健刘星胡飞龙李荣平
Owner YULIN NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com