Pure-copper-ammonia jacquard fabric and production method thereof

A fabric and pure copper technology, applied in the field of textile fabrics, can solve the problems of low wet strength and large wet elongation of cupro fibers, and achieve the effect of solving easy breakage, reducing production difficulty and high overall strength

Active Publication Date: 2014-01-01
NINGBO XINDACHANG WEAVING
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the characteristics of low wet strength and high wet elongation of cupro fiber, the difficulty in the production process of pure cupro fabric lies in its weaving process, which is not mentioned in this patent application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0016] A method for producing pure cupro ammonia jacquard fabric, comprising the following steps: 1) selecting 75D to 150D cupro ammonia filaments as raw materials; 2) warping, using batch warping machines for warping, and the unwinding tension during warping greater than the winding tension, the difference in thickness of the copper ammonia wires wound on the warping beam after the warping is completed is not more than 5mm; The speed of the roller, the speed of the yarn drawing roller is 90m / min; 4) Coaxial; 6) weaving on the upper machine, the loom used for weaving is an electronic dobby shuttleless loom, the width of the shuttleless loom is 55-57 inches, and its rotating speed is 650 rpm.

[0017] Wherein, the formula of the slurry used in the above step 3 is: by weight percentage, the main material is 99% 0588PVA, the auxiliary material is 1% antistatic agent, the number of warping threads of the warping machine in the above step 2 It is 720 pieces.

Embodiment 3

[0019] A method for producing pure cupro ammonia jacquard fabric, comprising the following steps: 1) selecting 75D to 150D cupro ammonia filaments as raw materials; 2) warping, using batch warping machines for warping, and the unwinding tension during warping greater than the winding tension, the difference in thickness of the copper ammonia wires wound on the warping beam after the warping is completed is not more than 5mm; The speed of the roller, the speed of the yarn drawing roller is 110m / min; 4) parallel axis; 5) according to the warp density and weft density of the fabric and the warp density and weft density required by the position of the pattern. 6) weaving on the upper machine, the loom used for weaving is an electronic dobby shuttleless loom, the width of the shuttleless loom is 55-57 inches, and its rotating speed is 500 rpm.

[0020] Wherein, the formula of the slurry used in the above step 3 is: by weight percentage, the main material is 98% 0588PVA, the auxilia...

Embodiment 4

[0022] A method for producing pure cupro ammonia jacquard fabric, comprising the following steps: 1) selecting 75D to 150D cupro ammonia filaments as raw materials; 2) warping, using batch warping machines for warping, and the unwinding tension during warping greater than the winding tension, the difference in thickness of the copper ammonia wires wound on the warping beam after the warping is completed is not more than 5mm; The speed of the roller, the speed of the yarn drawing roller is 100m / min; 4) parallel axis; 5) according to the warp density and weft density of the fabric and the warp density and weft density required by the pattern location 6) weaving on the upper machine, the loom used for weaving is an electronic dobby shuttleless loom, the width of the shuttleless loom is 55-57 inches, and its rotating speed is 580 rpm.

[0023] Wherein, the formula of the slurry used in the above step 3 is: by weight percentage, the main material is 98% 0588PVA, the auxiliary mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses pure-copper-ammonia jacquard fabric consisting of warps and wefts in a woven manner. Both the warps and the wefts are 75-150D (denier) pure-copper-ammonia filaments. The warp-wise density ranges from 429 / 10cm to 600 / 10cm, the weft-wise density ranges from 310 / 10cm to 429 / 10cm. Meanwhile, the invention further discloses a production method of the pure-copper-ammonia jacquard fabric. The production method includes the following steps of firstly, selecting the copper ammonia filaments as raw materials; secondly, beaming until the thickness of copper ammonia filaments wound on a beaming shaft is not more than 5mm; thirdly, pulping and keeping the speed of a yarn guide roll of a pulping machine lower than the speed of a pulping roll during pulping; fourthly, shaft integrating; fifthly, threading harness wires and inserting reed; and sixthly, weaving on the machine. Compared with the prior art, the pure-copper-ammonia jacquard fabric is soft and smooth in touch, low in cost and breakage and higher in integral strength than the like products and meets the requirement of environment friendliness. The production method is simple to operate, effectively solves the problem of easiness in copper ammonia fibers during production and reduces production difficulty of the pure-copper-ammonia jacquard fabric.

Description

technical field [0001] The invention relates to a textile fabric, in particular to a pure copper ammonia jacquard fabric, and also relates to a production method of the fabric. Background technique [0002] Cupro fiber is a kind of regenerated cellulose fiber. It is made by dissolving natural cellulose raw materials such as cotton linters in a concentrated ammonia solution of copper hydroxide or alkaline copper salt to prepare a spinning solution. Cellulose molecular chemicals are decomposed to regenerate cellulose, and the resulting hydrated cellulose is post-processed to obtain cupro ammonia fiber. The cross-section of cupro fiber is round, without sheath-core structure, and the monofilament produced is relatively thin, so the cupro fiber fabric is soft to the touch, soft in luster, has a real silk feel, and has good hygroscopicity. However, its wet strength is low and its wet elongation is high, so it is difficult to process the cupro fabric, and the cupro fiber is easy ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D03D13/00D02H13/14D06B23/20D06M15/333D03D15/225D03D15/30D03D15/50
Inventor 周刚明
Owner NINGBO XINDACHANG WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap