ABS / attapulgite composite material and preparation method thereof

A technology of attapulgite and composite materials, which is applied in the field of ABS/attapulgite composite materials and their preparation, and can solve the problems of unfavorable market promotion and application of ABS/PMMA composite materials, high preparation cost and high price of ABS/PMMA composite materials, etc. problems, to achieve good environmental benefits and social value, good hardness, and easy operation

Inactive Publication Date: 2012-08-08
宁波康德新材料有限公司
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technical scheme improves the surface hardness, tensile strength and bending performance of the ABS / PMMA composite material by adding PMMA and MBS to the ABS resin, and has higher gloss, but the price of PMMA is very high, which leads to the ABS / PMMA The preparation cost of composite materials is very high, which is not conducive to the market promotion and application of ABS / PMMA composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS / attapulgite composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] 1) Vacuum drying the attapulgite (200 mesh, Jingyuan, Gansu) at 80°C for 4 hours to obtain the dried attapulgite;

[0046] 2) Weigh 6.5 kg of ABS (Toray, Japan, T-300, melt index is 10), 2.5 kg of dried attapulgite and maleic anhydride grafted polypropylene (353D, DuPont, USA, grafting rate 1.0) 1.0 kilograms are premixed in a premixer (200 revs / min) to obtain a mixed material;

[0047] 3) Adding the mixed materials into a twin-screw extruder for melt blending, extruding and granulating to obtain a granular ABS / attapulgite composite material. Among them, the temperature of each section of the mixed material in the twin-screw extruder is respectively: the temperature of the feeding section is 210°C, the temperature of the compression section is 220°C, the temperature of the metering section is 225°C, the temperature of the head is 225°C, the speed of the twin-screw extruder is 300 rpm. The screw length-to-diameter ratio of the twin-screw extruder was 40:1.

[0048] Th...

Embodiment 2

[0050] 1) Vacuum drying the attapulgite (200 mesh, Jingyuan, Gansu) at 80°C for 4 hours to obtain the dried attapulgite;

[0051] 2) Weigh 6.5 kilograms of ABS (Toray, Japan, T-300, melt index is 10), 3.0 kilograms of dried attapulgite and maleic anhydride grafted polypropylene (353D, DuPont, USA, graft ratio 1.0) respectively 0.5 kilograms are premixed in a premixer (200 revs / min), to obtain a mixed material;

[0052] 3) Adding the mixed materials into a twin-screw extruder for melt blending, extruding and granulating to obtain a granular ABS / attapulgite composite material. Among them, the temperature of each section of the mixed material in the twin-screw extruder is respectively: the temperature of the feeding section is 210°C, the temperature of the compression section is 220°C, the temperature of the metering section is 225°C, the temperature of the head is 225°C, the speed of the twin-screw extruder is 300 rpm. The screw length-to-diameter ratio of the twin-screw extru...

Embodiment 3

[0055] 1) Vacuum drying the attapulgite (200 mesh, Jingyuan, Gansu) at 80°C for 4 hours to obtain the dried attapulgite;

[0056] 2) Weigh 6.5 kilograms of ABS (Toray, Japan, T-300, melt index is 10), 3.2 kilograms of dried attapulgite and maleic anhydride grafted polypropylene (353D, Dupont, USA, grafting rate 1.0) respectively 0.3 kilograms are premixed in a premixer (200 revs / min) to obtain a mixed material;

[0057] 3) Adding the mixed materials into a twin-screw extruder for melt blending, extruding and granulating to obtain a granular ABS / attapulgite composite material. Among them, the temperature of each section of the mixed material in the twin-screw extruder is respectively: the temperature of the feeding section is 210°C, the temperature of the compression section is 220°C, the temperature of the metering section is 225°C, the temperature of the head is 225°C, the speed of the twin-screw extruder is 300 rpm. The screw length-to-diameter ratio of the twin-screw extr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ABS / attapulgite composite material, comprising the following materials, by weight: 49%-70% of ABS, 15%-35% of attapulgite, 3%-20% of compatilizer and 0%-1% of ubricant. Attapulgite is a natural mineral, which belongs to the rod-like structure, and is beneficial to improving the smoothness of surface of the ABS / attapulgite composite material, and the compatibilizer improves compatibility of the ABS and the attapulgite, so as to endow the ABS / attapulgite composite material of the invention with advantages of high hardness, good bending strength; therefore, the composite material shows excellent mechanical properties. The invention also discloses a preparation method of the ABS / attapulgite composite material. The method is simple and easy to operate, can uniformly harmonize the attapulgite and the ABS through simple steps and prepare the ABS / attapulgite composite material with excellent performances.

Description

technical field [0001] The invention relates to the field of plastic materials and their preparation, in particular to an ABS / attapulgite composite material and a preparation method thereof. Background technique [0002] With the rapid development of the plastic industry, its use has penetrated into various fields of the national economy and is widely used. China produces about 5 million tons of waste plastic every year. Acrylonitrile-butadiene-styrene terpolymer (ABS), as an important kind of plastic material, has also been widely used, mainly because ABS is a copolymer of acrylonitrile, butadiene and styrene, It has good comprehensive performance, good chemical corrosion resistance and good processing fluidity, as well as high heat resistance, toughness, impact resistance and rigidity. [0003] ABS is mainly used in household appliances, mechanical parts, office supplies, electronic devices, automobile industry and other fields, such as panels for the manufacture of elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L51/06C08K3/34C08K5/20B29C47/92B29C48/92
CPCB29C48/04B29C48/40
Inventor 康建训朱松波刘建海
Owner 宁波康德新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com