Method for manufacturing unsaturated polyester resin reinforced glass bead plate

A technology of reinforced glass and polyester fiber, applied in the direction of flat products, other household appliances, household appliances, etc., can solve the problems of lack of sound insulation, corrosion resistance, reduced mechanical strength of plates, limited use scope, etc., to reduce fire hazards, Good mechanical properties and a wide range of effects

Active Publication Date: 2012-07-18
ZHEJIANG WAZAM NEW MATERIAL CO LTD
View PDF11 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent document CN 2350456Y discloses "a kind of sound insulation board", which can achieve sound insulation effect, but its fireproof performance is poor, which limits its application range
However, due to the existence of pores, the mechanical strength of the plate will be greatly reduced, and it is difficult to use it as some high-strength support structures.
Publication number CN201877680U discloses "isolating switch insulating board", which can be used for insulating switch parts such as electrical equipment, but it does not have sound insulation, corrosion resistance and other properties, and its application field is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing unsaturated polyester resin reinforced glass bead plate
  • Method for manufacturing unsaturated polyester resin reinforced glass bead plate
  • Method for manufacturing unsaturated polyester resin reinforced glass bead plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The mass parts batching of each component of unsaturated polyester resin paste is as follows:

[0039] Table 1

[0040] Ortho-phthalic unsaturated polyester resin

90Kg

Low Shrinkage Additive Polyethylene

10Kg

p-benzoquinone

1Kg

Zinc stearate

4Kg

BYK Dispersant

4Kg

tert-butyl peroxybenzoate

1Kg

Hollow glass microspheres (10μm)

150Kg

Aluminum hydroxide (5μm)

0Kg

35% magnesium oxide paste

1.2Kg

[0041]1) According to Table 1, pour 90Kg of o-phthalic unsaturated polyester resin and 10Kg of low-shrinkage additive polyethylene into the glue mixing tank and stir evenly, then add 1Kg of p-benzoquinone, 4Kg of zinc stearate, 4Kg of BYK dispersant, 1Kg of tert-butyl peroxybenzoate was stirred evenly, then added 150Kg of hollow glass microspheres (10 μm) through surface modification and stirred evenly, the present embodiment did not have aluminum hydroxide, all adopted hollow glass...

Embodiment 2

[0053] table 3

[0054] Ortho-phthalic unsaturated polyester resin

90Kg

Low Shrinkage Additive Polyethylene

10Kg

o-benzoquinone

1Kg

Zinc stearate

4Kg

BYK Dispersant

3Kg

tert-butyl peroxybenzoate

1Kg

Hollow glass microspheres (10μm)

120Kg

Aluminum hydroxide (5μm)

30Kg

35% magnesium oxide paste

1.4Kg

[0055] 1) According to the above table 3, pour 90Kg of o-phthalic unsaturated polyester resin and 10Kg of low-shrinkage additive polyethylene into the glue mixing tank and stir evenly, then add 1Kg of o-benzoquinone, 4Kg of zinc stearate, and 3Kg of BYK dispersant , 1Kg of tert-butyl peroxybenzoate and stir evenly, then add 120Kg of hollow glass microspheres (10 μm) and 30Kg of aluminum hydroxide (5 μm) through surface modification and stir evenly, the particle diameter of hollow glass microspheres and aluminum hydroxide Ratio 2:1, mass ratio 4:1, finally add 1.4Kg of 35% magnesium ...

Embodiment 3

[0065] table 5

[0066] Ortho-phthalic unsaturated polyester resin

[0067] 1) According to the above table 5, pour 90Kg of o-phthalic unsaturated polyester resin and 10Kg of low-shrinkage additive polystyrene into the glue mixing tank and stir evenly, then add 1Kg of p-benzoquinone, 4Kg of zinc stearate, BYK dispersant 2Kg, 1Kg of tert-butylperoxy-2-ethylhexanoate and stir evenly, then add 100Kg of surface-modified hollow glass microspheres (10μm) and 50Kg of aluminum hydroxide (5μm) and stir evenly, the hollow glass microspheres The particle size ratio to aluminum hydroxide is 2:1, and the mass ratio is 2:1. Finally, 1.5 kg of 35% magnesium oxide paste is added and stirred evenly to obtain an unsaturated polyester resin paste.

[0068] 2) The above resin paste is coated on the upper and lower sides of the glass fiber three-dimensional fabric respectively, and covered with a PET carrier film as a prepreg. The weight of glass fiber three-dimensional fabric is select...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Gram weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for manufacturing an unsaturated polyester resin reinforced glass bead plate. The method comprises the following steps of: 1, pouring an unsaturated polyester resin and a low shrinkage additive into a glue blending tank, stirring uniformly, adding a polymerization inhibitor, a release agent, a curing agent and a viscosity reducer, stirring uniformly, adding hollow glass microspheres and aluminum hydroxide, stirring uniformly, adding a thickening agent, and stirring uniformly to obtain unsaturated polyester resin paste; 2, coating the unsaturated polyester resin paste on the surfaces of a glass fiber mat or a glass fiber three-dimensional fabric, and coating by using polyester (PET) carrier films to obtain a prepreg; 3, drying the prepreg obtained in the step 2 in a drying room at the temperature of between 30 and 50DEG C for 12 to 24 hours; 4, removing the PET carrier films after the prepreg is dried, and cutting the prepreg; and 5, pressing a piece of prepreg in a hot-pressing mold, or overlapping a plurality of pieces of prepregs, and pressing the overlapped prepregs in the hot-pressing mold to obtain the unsaturated polyester resin reinforced glass bead plate.

Description

technical field [0001] The invention belongs to the technical field of manufacturing flame-retardant sound-insulating insulating boards, and in particular relates to a manufacturing method of unsaturated polyester fiber-reinforced glass bead boards. Background technique [0002] At present, sound insulation panels are required in many occasions, such as cinemas, hotels, highway sound-reducing noise-reducing walls and many other public places. After retrieval, the Chinese patent literature discloses some technical proposals related to the sound insulation board. For example: Chinese patent document CN 1070024A discloses a "sandwich heat preservation and sound insulation structural part of double-layer reinforced concrete slab and light concrete web". Although the sound insulation board of this technical solution has a certain sound insulation effect, the overall structure is heavy and The scope of application is narrow. Chinese patent document CN 2350456Y discloses "a sound...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C70/46B29K67/00B29L7/00
Inventor 董辉沈宗华郭江程周育波
Owner ZHEJIANG WAZAM NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com