Dual-component aqueous polyurethane paint with scrawling resistance and pasting resistance and preparation thereof

A water-based polyurethane and anti-graffiti technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve problems that affect city appearance and landscape, consume large funds, and damage substrates

Inactive Publication Date: 2012-06-27
CENT SOUTH UNIV +1
View PDF4 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In recent years, the loss caused by malicious graffiti pasting has attracted more and more people's attention. It not only affects the city appearance and landscape, but also takes time and effort to remove graffiti and various pastes, which is easy to cause damage to the substrate and consumes a lot of money.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dual-component aqueous polyurethane paint with scrawling resistance and pasting resistance and preparation thereof
  • Dual-component aqueous polyurethane paint with scrawling resistance and pasting resistance and preparation thereof
  • Dual-component aqueous polyurethane paint with scrawling resistance and pasting resistance and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The two-component waterborne polyurethane anti-graffiti and anti-stick coating is composed of A and B components.

[0031] The components A and B are composed in parts by weight as follows:

[0032] A component

[0033]

[0034] B component

[0035] Bayhydur XP2547 20.

[0036] The manufacturing method is as follows: the two-component waterborne polyurethane anti-graffiti and anti-stick coating is prepared by mixing components A and B. The preparation method of component A is: divide the polyacrylic acid resin dispersion into two parts according to the total amount added in a weight ratio of 3:2, namely dispersion 1 and dispersion 2, first add dispersion 1, defoamer win The product Airex901W, wetting agent, dispersant, deionized water, and pigment of Chuang Degussa Company are placed in the dispersing kettle, and the speed is adjusted to 2500 rpm, fully dispersed for 20 minutes, and the fineness is controlled to be ≤ 20um; the speed is adjusted to 1500 rpm , add ...

Embodiment 2

[0041] The two-component waterborne polyurethane anti-graffiti and anti-stick coating is composed of A and B components.

[0042] The components A and B are composed in parts by weight as follows:

[0043] A component

[0044]

[0045]

[0046] B component

[0047] Bayhydur XP2547 20.

[0048] The manufacturing method and film-making method are the same as in Example 1.

[0049] The basic performance test results of the paint film are shown in Table 1.

[0050] Table 2 shows the test results of anti-graffiti and anti-sticking properties of the paint film.

Embodiment 3

[0052] The two-component waterborne polyurethane anti-graffiti and anti-stick coating is composed of A and B components.

[0053] The components A and B are composed in parts by weight as follows:

[0054] A component

[0055]

[0056] B component

[0057] Bayhydur XP2547 20.

[0058] The manufacturing method and film-making method are the same as in Example 1.

[0059] The basic performance test results of the paint film are shown in Table 1.

[0060] Table 2 shows the test results of anti-graffiti and anti-sticking properties of the paint film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a dual-component aqueous polyurethane paint with scrawling resistance and pasting resistance, and a preparation method thereof. The dual-component aqueous polyurethane paint with scrawling resistance and pasting resistance is prepared by using aqueous hydroxy-containing polyacrylic resin dispersion and fatty group polyisocyanate as main film forming substances, adding organosilicon resin emulsion, deionized water, antifoaming agent, wetting agent, dispersant, pigment, dulling agent, wax emulsion and thickening agent and carrying out high speed disperse. The paint has characteristics of high crosslinking density, low surface tension, strong permeability resistance, good scratch resistance, substantial scrawling resistance and pasting resistance, excellent performances of low VOC content, high hardness, good weatherability, brushing resistance and chemical resistance, and is suitable for application fields of municipal public facility, building paint and terrace paint coating, etc.

Description

technical field [0001] The invention belongs to the field of two-component water-based polyurethane coatings, and relates to a functional water-based polyurethane coating with anti-graffiti and anti-sticking properties and a preparation method thereof. Background technique [0002] In recent years, the loss caused by malicious graffiti paste has attracted more and more attention. It not only affects the city appearance and landscape, but also takes time and effort to remove graffiti and various pastes, which is easy to cause damage to the substrate and consumes a lot of money. Random graffiti paste phenomenon occurs from time to time, it is difficult to avoid, therefore, it is necessary to develop coatings with anti-graffiti and anti-sticking functions. [0003] The main difference between anti-graffiti and anti-sticking coatings and other coatings is that the surface adhesion of the substrate coated by it is low, and it is difficult to be adhered by pollutants. To reduce t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D183/04C09D7/12
Inventor 李芝华王亚周斌周子鹄
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com