High-whiteness pure paper and manufacturing technology thereof

A high-white, crafted technology, applied in the field of papermaking, can solve the problems of low paper surface smoothness, dull color, poor printing performance, etc.

Active Publication Date: 2012-06-13
MCC PAPER YINHE
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the passage of time, printers put forward some opinions on the quality indicators of light paper: low smoothness of paper surface, poor printing performance; dull color, unsightly; low printing surface strength, difficult to adapt to multi-color rotary printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] In June 2011, China Metallurgical Paper Galaxy Co., Ltd. adopted the invention in the company's 9 # Machine production 70g / m 2 High-white pure paper, the pulp mass ratio is APMP: NBCTMP: NBKP: LBKP = 50: 15: 20: 15, the degree of tapping APMP pulp is 42°SR, NBCTMP is 47°SR, NBKP is 38°SR, and LBKP is 42° °SR, wet weights are 1.0~1.2g, 5.3~5.5g, 5.3~5.5g, 2.0~2.5g; ISO whiteness is 75~76%, 79~80%, 87~88%, 79~80 %. The specific operation is as follows:

[0018] (1) The slurry is pumped to the slurry mixing tank, and at the same time, the carboxymethyl starch (CMS) solution with a concentration of 0.5% is added to the slurry mixing tank, and the stirring propeller of the slurry mixing tank is started, and the added slurry is Material and carboxymethyl starch solution are stirred and mixed; the add-on of described carboxymethyl starch solution is 2.0kg / t slurry;

[0019] (2) The slurry mixed with the CMS solution in step (1) is pumped to the No. 1 pulp tank, and the slu...

Embodiment 2

[0025] In August 2011, China Metallurgical Paper Galaxy Co., Ltd. adopted the invention in the company's 15 # Machine production 78g / m 2 High-white pure paper, the pulp mass ratio is APMP: NBCTMP: NBKP: LBKP = 55: 15: 20: 10, the degree of beating APMP pulp is 41°SR, NBCTMP is 47°SR, NBKP is 38°SR, and LBKP is 40 °SR, wet weight is 1.0~1.2g, 5.3~5.5g, 5.3~5.5g, 2.0~2.5g, ISO whiteness is 75~76%, 79~80%, 87~88%, 79~80 %. The specific operation is as follows:

[0026] (1) The slurry is pumped to the slurry mixing tank, pumped to the slurry mixing tank, and simultaneously adding a carboxymethyl starch solution with a concentration of 0.45% in the slurry mixing tank, and starting the stirring propeller of the slurry mixing tank, The added slurry and carboxymethyl starch solution are stirred and mixed; the add-on of said carboxymethyl starch solution is 2.5kg / t slurry;

[0027] (2) The slurry mixed with carboxymethyl starch solution in step (1) is pumped to No. 1 pulp tank, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Smoothnessaaaaaaaaaa
Surface strengthaaaaaaaaaa
Bulkaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-whiteness pure paper and a manufacturing technology thereof. In the technology, poplar APMP pulp, needle-leave wood bleached chemical thermomechanical pulp, bleached sulfate needle-leave wood pulp and bleached sulfate broad-leave wood pulp are used for preparing pulp; CMS is added into a pulp preparation pond, wherein due to the water retaining property of the CMS, the dehydration of the high-yield pulp in a net part is slowed down, and the paper uniformity and smoothness are improved; a chelating agent DTPA is added into a white water tank so as to suppress resinaggregation and prevent drop of the pulp whiteness; and before adding the traditional retention aids CPAM and APAM, PAC is added so as to reduce the negative charges of a pulp suspension mainly containing the high-yield pulp, improve the one-pass retention of the manufacturing and increase the paper uniformity and smoothness. The quality indexes of the manufactured high-whiteness pure water are as follows: quantification is 70-80 g / m<2>, the ISO whiteness is 82-86%, the smoothness (front side / back side) is greater than 25 S, the strength of the printing surface is greater than 1.5 m / s, and the bulk is 1.5-1.6 cm<3> / g.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a high-white pure paper and its papermaking process. Background technique [0002] At present, due to the characteristics of high fluorescent whiteness, low bulk and chemical pulp ratio of double-sided offset printing paper, it has been difficult to adapt to the current concept of green environmental protection and low carbon that is vigorously advocated. In recent years, light paper has replaced some high-grade double-sided offset printing paper and has been recognized in the market. However, with the passage of time, printers put forward some opinions on the quality indicators of light paper: low paper surface smoothness, poor printing performance; dull color, visually unsightly; low printing surface strength, difficult to adapt to multi-color rotary printing. Contents of the invention [0003] In order to overcome the above shortcomings, the purpose of the present inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H11/10D21H17/66
Inventor 李树俭曾金枝张小丽田红霞
Owner MCC PAPER YINHE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com