Glaze material with fluxing agent

A technology of flux and glaze, applied in the field of glaze with flux added, can solve the problems of large dosage, high cost of zinc oxide, increase product cost, etc., and achieve the effects of ensuring quality, reducing expansion coefficient and improving thermal stability

Inactive Publication Date: 2012-04-25
TANGSHAN HUALI CERAMICS CO LTD
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at the high cost and large dosage of zinc oxide in the glaze, which increases the product cost, and provides an additive additive that can reduce the production cost while ensuring the thermal stability of the product. flux glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Embodiment 1: The optimum raw material ratio (parts by weight) for forming the glaze is: 31.6 parts of quartz, 27.5 parts of potassium feldspar, 3 parts of aluminum oxide, 14.6 parts of calcite, 4.3 parts of dolomite, and 1.5 parts of zinc oxide parts, 4 parts of kaolin, 1.5 parts of flux, 10 parts of zirconium silicate, and 2 parts of frit.

[0009] The chemical composition of this glaze and the weight percentage of each composition are: I.L 8.76, SiO 2 57.41, Al 2 o 3 9.34, Fe 2 o 3 0.13, TiO 2 0.07, CaO 9.68, MgO 1.36, K 2 O 3.25, Na 2 O 1.05, ZnO 1.55, ZrO 2 6.68, BaO 0.1, B 2 o 3 0.61.

[0010] The chemical composition of the fluxing agent in the glaze disclosed by the present invention and the percentage by weight of each composition are: I.L 0.23, SiO 2 45.21, Al 2 o 3 19.54, Fe 2 o 3 0.02, TiO 2 0.01, CaO 4.63, MgO 7.42, K 2 O 2.5, Na 2 O 7.64, ZnO 0.1, BaO 6.84, B 2 o 3 15.65.

Embodiment 2

[0011] Embodiment 2: The raw material ratio (parts by weight) of forming the glaze is: 30 parts of quartz, 25 parts of potassium feldspar, 2 parts of aluminum oxide, 15 parts of calcite, 4 parts of dolomite, 1 part of zinc oxide, 4.5 parts of kaolin, 2.5 parts of flux, 9 parts of zirconium silicate, and 1 part of frit.

Embodiment 3

[0012] Embodiment 3: The raw material ratio (parts by weight) of forming the glaze is: 32 parts of quartz, 29 parts of potassium feldspar, 4 parts of aluminum oxide, 13 parts of calcite, 6 parts of dolomite, 2.5 parts of zinc oxide, 3 parts of kaolin, 1 part of flux, 11 parts of zirconium silicate, 2.5 parts of frit.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glaze material used in the production process of ceramic products, in particular to a glaze material with fluxing agent. The glaze material comprises the following raw materials in parts by weight: 30-32 parts of quartz, 25-29 parts of potash feldspar, 2-4 parts of aluminium oxide, 13-15 parts of calcite, 4-6 parts of dolomite, 1-2.5 parts of zinc oxide, 3-4.5 parts of kaoline, 1-2.5 parts of fluxing agent, 9-11 parts of zirconium silicate and 1-2.5 parts of fusion cake. A part of zinc oxide is replaced with finished products in the ceramic glaze material disclosed by the invention so that the aim of greatly reducing the production cost while ensuring thermal stability is ensured is achieved. The ceramic glaze in which the fluxing agent is added has the advantages that the added fluxing agent plays a fluxing role, the expansion coefficient of the glaze material is reduced, the thermal stability of ceramic products is improved, and the quality of the ceramic products can be ensured.

Description

technical field [0001] The invention relates to a glaze used in the production process of ceramic products, in particular to a glaze added with flux. Background technique [0002] At present, the main function of zinc oxide in the glaze used in the production process of ceramic products is to flux, which can reduce the expansion coefficient of the glaze and improve the thermal stability of the product. However, the price of zinc oxide is expensive. In the mass production of ceramic products, due to the need to use a large amount of zinc oxide for fluxing, the production cost of ceramic products is greatly increased. the burden of production costs. Contents of the invention [0003] The present invention aims at the high cost and large dosage of zinc oxide in the glaze, which increases the product cost, and provides an additive additive that can reduce the production cost while ensuring the thermal stability of the product. Flux glaze. [0004] The technical solution ado...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 冯荣光穆长久田海武穆建民徐鹏俊
Owner TANGSHAN HUALI CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com