Environmentally-friendly energy-saving polyurethane spraying composite material with ultralow density

An ultra-low density, polyurethane technology, applied in the direction of fireproof coatings, coatings, etc., can solve the problems of increased production cost and difficult promotion of polyurethane, and achieve the effect of good flame retardancy and good heat preservation

Inactive Publication Date: 2012-03-28
可利亚多元醇(南京)有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The most conventional method is to increase the foam density to 30%, which causes a great increase in the production cost of polyurethane and is difficult to popularize

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An environment-friendly ultra-low-density energy-saving polyurethane spraying composite material, comprising the following components by weight:

[0031] 1) Polyether polyol A with glycerin as the initiator: 35 parts, which is prepared by the addition reaction of epoxy olefins with glycerin as the initiator; 3 functionalities, the hydroxyl value is 40mgKOH / g; the polyether The polyol contains 15% ethylene oxide.

[0032] 2) Flame retardant: 30 parts of tris(1-chloro-ethylpropyl) phosphate (TCPP);

[0033] 3) Amine foaming catalyst: 7 parts of pentamethyldiethylenetriamine;

[0034] 4) Foam stabilizer: B8462 1.0 parts;

[0035] 5) Water: 28 parts;

[0036] 6) Isocyanate: 4,4-xylenemethane diisocyanate with an NCO content of 30~32%, 116 parts.

[0037] The performance indicators of the above-mentioned polyurethane spraying composite materials are shown in Table 1.

[0038]

Embodiment 2

[0040] An environment-friendly ultra-low-density energy-saving polyurethane spraying composite material, comprising the following components by weight:

[0041] 1) Polyether polyol A with glycerin as the initiator: 60 parts, which is obtained by adding glycerol as the initiator through the addition reaction of epoxy olefin; 3 functionalities, the hydroxyl value is 20mgKOH / g; the polyether The polyol contains 20% ethylene oxide.

[0042] 2) Flame retardant: 45 parts of tris(1,3-dichloropropyl) phosphate (TDCP);

[0043] 3) Amine foaming catalyst: 5 parts of bis(dimethylaminohexyl) ether;

[0044] 4) Foam stabilizer: 2.5 parts of B8462;

[0045] 5) Water: 30 parts;

[0046] 6) Isocyanate: 4,4-xylenemethane diisocyanate with an NCO content of 30-32%, 120 parts.

[0047] The performance indicators of the above-mentioned polyurethane spraying composite materials are shown in Table 1.

[0048]

Embodiment 3

[0050] An environment-friendly ultra-low-density energy-saving polyurethane spraying composite material, comprising the following components by weight:

[0051] 1) Polyether polyol A with glycerin as the initiator: 20 parts, which is prepared by the addition reaction of epoxy olefin with glycerin as the initiator; 3 functionalities, the hydroxyl value is 50mgKOH / g; the polyether The polyol contains 10% ethylene oxide.

[0052] 2) Flame retardant: 40 parts of dimethyl methylphosphonate (DMMP);

[0053] 3) Amine foaming catalyst: 5 parts of pentamethyldiethylenetriamine, 5 parts of bis(dimethylaminohexyl) ether;

[0054] 4) Foam stabilizer: 2.0 parts of B8462;

[0055] 5) Water: 24 parts;

[0056] 6) Isocyanate: 4,4-xylenemethane diisocyanate with an NCO content of 30~32%, 95 parts.

[0057]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
densityaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environmentally-friendly energy-saving polyurethane spraying composite material with ultralow density, which comprises the following components in part by weight: 20-60 parts of polyether polyol which takes glycerol as an initiator, 3-10 parts of amine catalyst, 0.5-3.0 parts of foam stabilizer, 22-30 parts of water, 30-45 parts of fire retardant and 95-120 parts of isocyanate. In the environmentally-friendly energy-saving polyurethane spraying composite material, pure water is used for replacing the traditional hydro chlorofluorocarbon (HCFC)-141b foaming agent, and the environmentally-friendly energy-saving polyurethane spraying composite material is an environmentally-friendly energy-saving polyurethane spraying foam with the ultralow density. The polyurethane spraying composite material has the ultralow density which can reach 5-10kg / m3. Because the polyurethane spraying composite material has tapping performance, the sound absorption performance can reach 70%. Meanwhile, the oxygen index of the environmentally-friendly energy-saving polyurethane spraying composite material reaches 23 and can pass the Society of Tool and Manufacturing Engineers (ASTME)-84 authentication.

Description

technical field [0001] The invention relates to a polyurethane spraying composite material, in particular to an environment-friendly ultra-low density energy-saving polyurethane spraying composite material. Background technique [0002] Polyurethane rigid foam is widely used in thermal insulation, refrigeration, and construction industries due to its excellent performance, but with the wide expansion of its application range, its negative impact on the environment has sounded the alarm for people. Among them, polyurethane spray coatings are mainly used in the building insulation industry, and the foaming agents used are mainly HCFC-141b and water. Foaming agents such as HCFC are Freon-type foaming agents. The use of Freon will deplete the atmospheric ozone layer and cause damage to the atmospheric ozone layer, resulting in enhanced ultraviolet radiation and threatening the survival of human beings and other earth creatures. one of the environmental problems. [0003] For t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08C09D5/18C09D7/12C08G18/76C08G18/48C08J9/12
Inventor 金大映权在槿李光雨
Owner 可利亚多元醇(南京)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com