Polyphosphazene-sulfone amide material and preparation method thereof

A technology of sulfone amide and polyphosphazene, which is applied in the field of polyphosphazene-sulfone amide material and its preparation, can solve the problems of single material solubility, harsh processing and preparation technology, etc., and achieves good thermal stability and good solubility in polar solution. performance, the effect of good flame retardant properties

Inactive Publication Date: 2012-10-31
SHANGHAI UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For pure PPTA fiber, its processing and preparation process is harsh, and the solubility of the material is single

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphosphazene-sulfone amide material and preparation method thereof
  • Polyphosphazene-sulfone amide material and preparation method thereof
  • Polyphosphazene-sulfone amide material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The synthesis of polyphosphazene-sulfone amide material is realized through the following steps:

[0026] (1) In a 500mL three-neck flask equipped with magnetic rotor stirring, condenser and thermometer, dissolve hexachlorocyclotriphosphazene (17.4g 0.05mol) prepared by multiple sublimation in 50mL tetrahydrofuran (THF) solvent, add dropwise Prepared (2.32g 0.2mol) sodium phenate (under nitrogen protection, (4.6g 0.2mol) sodium metal and (18.822g 0.2mol) phenol reacted in 50mL THF solution at 25°C for 2 hours) THF solution, nitrogen Protected and reacted at 40°C for 12 hours. THF was removed by rotary distillation, washed several times with deionized water, and vacuum-dried at 50°C for 24 hours to obtain a milky white colloid.

[0027] (2) In a 500mL three-neck flask equipped with a magnetic rotor stirring, a condenser, and an HCl absorption device, dissolve the (10.37g 0.018mol) milky white colloid obtained in step (1) in 50mL of THF solvent, and add (9.93 g 0.04mol)...

Embodiment 2

[0030] The synthesis of polyphosphazene-sulfone amide material is realized through the following steps:

[0031] (1) In a 500mL three-neck flask equipped with magnetic rotor stirring, condenser and thermometer, dissolve hexachlorocyclotriphosphazene (13.9g 0.04mol) prepared by multiple sublimation in 50mL tetrahydrofuran (THF) solvent, add dropwise Prepared (1.856g 0.16mol) sodium phenate (under nitrogen protection, (3.68g 0.16mol) metal sodium and (15.06g 0.16mol) phenol reacted in 50mL THF solution at 25°C for 2 hours) THF solution, nitrogen Protected and reacted at 40°C for 12 hours. THF was removed by rotary distillation, washed several times with deionized water, and vacuum-dried at 50°C for 24 hours to obtain a milky white colloid.

[0032] (2) In a 500mL three-necked flask equipped with a magnetic rotor stirring, a condenser, and an HCl absorption device, dissolve the (11.52g 0.02mol) milky white colloid obtained in step (1) in 50mL of THF solvent, and add (9.94 g 0.0...

Embodiment 3

[0035] The synthesis of polyphosphazene-sulfone amide material is realized through the following steps:

[0036] (1) In a 500mL three-neck flask equipped with magnetic rotor stirring, condenser and thermometer, hexachlorocyclotriphosphazene prepared by multiple sublimation (34.8g 0.1mol) was dissolved in 100mL tetrahydrofuran (THF) solvent, and added dropwise Prepared (9.28g 0.4mol) sodium phenate (prepared by reacting (9.2g 0.4mol) metal sodium and (37.64g 0.4mol) phenol in 100mL THF solution at 25°C for 2 hours under nitrogen protection) THF solution, nitrogen Protected and reacted at 40°C for 24 hours. THF was removed by rotary distillation, washed several times with deionized water, and vacuum-dried at 50°C for 24 hours to obtain a milky white colloid.

[0037] (2) In a 500mL three-neck flask equipped with a magnetic rotor stirring, a condenser, and an HCl absorption device, dissolve the (28.81g 0.05mol) milky white colloid obtained in step (1) in 100mL of THF solvent, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polyphosphazene-sulfone amide material and a preparation method thereof. The structural formula of the polyphosphazene-sulfone amide is disclosed in the specification. The polyphosphazene-sulfone amide not only has excellent thermal stability of polyamide, but also is soluble in a high-polarity organic solvent, so that the machining properties are enhanced; the polyphosphazene-sulfone amide material has high carbon residue rate at 600 DEG C; and the polyphosphazene-sulfone amide material is mainly applicable to automobile engine components, mechanical components andaviation equipment components, and provides a new option for mechanical high-temperature solid lubricating materials.

Description

technical field [0001] The invention relates to a polyphosphazene-sulfone amide material and a preparation method thereof. Background technique [0002] The special structure and superior performance of polyphosphazene (HCCP) determine its extensive research and application in many fields. At present, it mainly focuses on nonlinear optical materials, special rubber and elastic materials, separation membranes, flame retardant materials, solid electrolytes, and pharmaceutical and biomedical materials. Chemical Structure: [0003] [0004] Polyterephthalide-p-phenylenediamine (PPTA) fiber, known as aramid 1414 in our country, has heat resistance close to that of inorganic fiber, high dimensional stability at high temperature, and high flame retardancy. It will not shrink when in contact, and can retain the physical properties of the fiber for a long time, and its biggest feature is its low density, so the specific strength and specific modulus are several times higher than...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G69/42C08G79/04C07F9/6593
Inventor 郭强赵正平张四刚张经毅谭孝林孙金亮聂智军
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com