Moisturizing agent for surgical instrument and preparation method thereof

A technique for surgical instruments and moisturizing agents, which is applied in chemical instruments and methods, surgery, detergent compositions, etc., can solve the problems of rust, increased difficulty in cleaning instruments, and rusted instruments, and achieves low foam volume and moisturizing effect. Good, promote cleaning effect

Active Publication Date: 2011-12-28
SHINVA MEDICAL INSTR CO LTD
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most hospitals in China do not carry out moisturizing treatment, so that the pollutants on the surface of the instrument after surgery will quickly condense and dry, and tightly adhere to the surface of the instrument, making it more difficult to clean the instrument and appear rusty; some hospitals use The caisson method is used for moisturizing, that is, the postoperative instruments are put into the diluted solution of cleaning agent or soft water, although this can play a role in moisturizing, but the problem of rusting of the instruments will occur; while the surgical instrument moisturizer can perfectly eliminate the above The problem is solved, the moisturizer contains moisturizing and moisturizing ingredients, which can cover the blood stains on the surface of the device and prevent the loss of water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisturizing agent for surgical instrument and preparation method thereof
  • Moisturizing agent for surgical instrument and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The formulations of each component of Example 1 are shown in Table 1.

[0020] Formulation table of each component of table 1 embodiment 1

[0021] components

Quality score (%)

distilled water

50％

Glycerin

40％

sodium nitrite

5％

OP-10

3％

protease

1％

Lipase

0.5％

Lipase

0.5％

[0022] The preparation method of the moisturizing agent for surgical instruments: first add water to the container, then add corrosion inhibitor, moisturizing ingredients, wetting ingredients and biological enzymes in turn to mix, stir and dissolve, and filter to obtain; the principle of adding materials is The former one is dissolved and then the latter one is added, the stirring speed is 170±5 rpm, the dissolution temperature is 20°C, and the filter screen adopts a double-layer 200-mesh filter screen.

[0023] The surgical instrument moisturizer prepared in Example 1 is clear, transpare...

Embodiment 2

[0025] The formulation of each component of embodiment 2 is shown in table 2.

[0026] Formulation table of each component of table 2 embodiment 2

[0027] components

Quality score (%)

distilled water

70％

Glycerin

15％

Sodium silicate

5％

sodium nitrite

5％

SDBS

2％

OP-10

1％

protease

1％

Lipase

0.5％

Amylase

0.5％

[0028] The preparation method of the moisturizing agent for surgical instruments: first add water to the container, then add corrosion inhibitor, moisturizing ingredients, wetting ingredients and biological enzymes in turn to mix, stir and dissolve, and filter to obtain; the principle of adding materials is The former one is dissolved and then the latter one is added, the stirring speed is 170±5 rpm, the dissolution temperature is 15°C, and the filter screen adopts a double-layer 200-mesh filter screen.

[0029] The surgical instrumen...

Embodiment 3

[0031] The formula of each component of embodiment 3 is shown in table 3.

[0032] Table 3 embodiment 3 each component formula table

[0033] components

Quality score (%)

distilled water

60％

NL-50

30％

Sodium silicate

6％

OP-10

2％

protease

1％

Lipase

0.5％

Amylase

0.5％

[0034] The preparation method of the moisturizing agent for surgical instruments: first add water to the container, then add corrosion inhibitor, moisturizing ingredients, wetting ingredients and biological enzymes in turn to mix, stir and dissolve, and filter to obtain; the principle of adding materials is The former one is dissolved and then the latter one is added, the stirring speed is 180±5 rpm, the dissolution temperature is 25°C, and the filter screen adopts a double-layer 200-mesh filter screen.

[0035] The surgical instrument moisturizer prepared in Example 3 is clear, transparent, free of pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of moisture preservation of medical instruments, and relates to a surgical instrument moisturizing agent and a preparation method thereof. The surgical instrument moisturizing agent consists of the following components in percentage by mass: 50 to 70 percent of water, 15 to 40 percent of moisturizing component, 0.5 to 4 percent of moistening component, 5 to 10 percent of corrosion inhibitor and 0.5 to 4 percent of biological enzyme. The moisturizing agent has the advantages of good moisturizing effect, low foam output, low cost and good washing effect; and the preparation method is simple and practicable and is easy to realize and control.

Description

technical field [0001] The invention belongs to the technical field of moisturizing of medical instruments, and relates to a moisturizing agent for surgical instruments and a preparation method thereof. Background technique [0002] The surface of surgical instruments in hospitals will be contaminated with a lot of blood and tissue after use. If these dirt are placed in the environment without treatment, they will quickly solidify and dry up, which increases the difficulty of cleaning. Foreign research departments have found that fresh blood adhered to the surface of the device will quickly condense and dry out, and after two hours of washing with water, corrosive marks will be left on the metal surface. At present, most hospitals in China do not carry out moisturizing treatment, so that the pollutants on the surface of the instrument after surgery will quickly condense and dry, and tightly adhere to the surface of the instrument, making it more difficult to clean the instru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L31/14A61L31/06A61L31/02C11D10/02
Inventor 隋本健杜嫣王久儒钟善
Owner SHINVA MEDICAL INSTR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com