Method and equipment for measuring total solid matter content of natural rubber latex

A technology of natural rubber latex and total solids, applied in the field of natural rubber, can solve the problems of time-consuming, cumbersome operation, power consumption, etc., and achieve the effect of expanding the area, high measurement accuracy and convenient operation

Inactive Publication Date: 2011-11-23
刘光辉 +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the field of natural rubber measurement and analysis, the determination of the total solid content in latex requires more accurate oven drying, but this method is time-consuming (8-12 hours), power-consuming, and cumbersome to operate. Only suitable for measuring a small number of samples
For a long time, it has been difficult for technicians in this field to find a so-called ideal rapid total solids content determination method that is fast, easy to operate, strong in anti-interference, and the accuracy is closest to the standard oven drying method.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and equipment for measuring total solid matter content of natural rubber latex
  • Method and equipment for measuring total solid matter content of natural rubber latex
  • Method and equipment for measuring total solid matter content of natural rubber latex

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1: Operation method

[0030] 1. Use a disposable syringe to drop a small amount of latex sample into a numbered container of rated weight (including foam metal with a weight of ω 0 ), weigh the total weight ω of the sample and the vessel 1 , prepare several samples to be determined according to this method;

[0031] 2. Place the prepared vessel on the heat source in the vacuum system, turn on the vacuum switch, and make the system reach a negative pressure state.

[0032] 3. Use the temperature controller to set the heating temperature to 180-350°C, set a few minutes, and vacuum dry the sample;

[0033] 4. Weigh and measure the dried sample together with the vessel to obtain the weight ω 2 ;Use the following formula to calculate the total solid content α of the sample:

[0034] .

Embodiment 2

[0036] A kind of measuring equipment of the total solid content of natural rubber latex, comprise the metal container 6 that is made of metal foam of rated weight, the electric heating plate 5 of heating metal container 6, described measuring equipment also includes the described metal container 6. A sealed box 1 for vacuuming. The measuring equipment also includes temperature, vacuum and other function control knobs 3. The temperature, vacuum and other function control knobs 3 control the electric heating plate 5 and the vacuum pump 2. Control, the measuring device also includes a plate weighing system 4, and the measuring device also includes a digital display 7. The metal foam is covered with metal foil 8 on its side and bottom.

[0037]

Embodiment 3

[0039] The samples were fresh natural rubber latex purchased from the purchase point of the rubber factory on the same day.

[0040] 1. Determination of total solids content by standard oven drying method: use a disposable syringe to take 2 to 3 grams of latex for determination, drying temperature is 70 ° C, time is 10 hours, and three groups of sample tests are done;

[0041] ω 0 : vessel weight;

[0042] ω 1 : The total weight of the container and latex before measurement;

[0043] ω2 : The total weight of the container and latex after drying;

[0044]

[0045] 2. Determination of total solids content by vacuum drying method (using the method of Example 1 and the equipment of Example 2): use a disposable syringe, take 0.2 to 2 grams of latex for measurement, drying temperature 200 ° C, vacuum degree -0.09 Mpa, time 3 minutes, do three sets of sample tests;

[0046] ω 0 : vessel weight;

[0047] ω 1 : The total weight of the container and latex before measurement; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for measuring total solid matter content of natural rubber latex. The method is accurate, quick and easy to operate and can replace a standard oven drying method. The invention also provides equipment for measuring the total solid matter content of the natural rubber latex.

Description

technical field [0001] The invention relates to the technical field of natural rubber, in particular to a method and equipment for measuring the total solid content of natural rubber latex. Background technique [0002] At present, in the field of natural rubber measurement and analysis, the determination of the total solid content in latex requires more accurate oven drying, but this method is time-consuming (8-12 hours), power-consuming, and cumbersome to operate. Only suitable for measuring small samples. For a long time, it has been difficult for those skilled in the art to find a so-called ideal rapid total solids content determination method that is fast, easy to operate, strong in anti-interference, and the accuracy is closest to the standard oven drying method. Contents of the invention [0003] The purpose of the present invention is to provide a kind of assay method of natural rubber latex total solid content, and this method is accurate, fast, easy to operate, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N5/04
Inventor 刘光辉刘威
Owner 刘光辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products