Attapulgite clay porous ceramsite, and preparation method and purpose thereof

A technology of attapulgite clay and attapulgite powder, which is applied to ceramic products, other household appliances, chemical instruments and methods, etc., can solve the problems of being unsuitable for microbial reproduction, difficult to support microorganisms in a film, and clogging of biological filters, etc. Low price, high strength, good water resistance

Active Publication Date: 2011-10-26
HEFEI UNIV OF TECH
View PDF3 Cites 59 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the particles prepared in this technical scheme do not add pore-forming agents, and the prepared particles have small porosity and irregular particles. During the operation of the biofilter, the water flow resistance is large, which may easily cause the blockage of the biofilter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Attapulgite clay porous ceramsite, and preparation method and purpose thereof
  • Attapulgite clay porous ceramsite, and preparation method and purpose thereof
  • Attapulgite clay porous ceramsite, and preparation method and purpose thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] In this embodiment, the raw materials of attapulgite clay porous ceramsite are constituted by mass percentage: attapulgite clay 75%, straw 20%, industrial water glass 5%;

[0032] Attapulgite clay porous ceramsite in this embodiment is prepared according to the following steps:

[0033] a, drying and pulverizing the attapulgite clay ore and passing through a 200-mesh sieve to obtain attapulgite powder;

[0034] B, the straw is crushed through a 200-mesh sieve, mixed with industrial water glass and the attapulgite powder obtained in step a to obtain a mixed powder;

[0035] c. Add water to the mixed powder and stir evenly, the amount of water added is 30% of the mass of the mixed powder, granulate and shape, control the particle size at 5-6mm, then dry naturally, and then calcined in the air at 700°C for 2 hours to obtain attapulgite clay porous ceramsite.

[0036] The attapulgite clay porous ceramsite prepared in this example is used as the carrier of microorganisms i...

Embodiment 2

[0041] The raw material of attapulgite clay porous ceramsite in the present embodiment is constituted by mass percentage: attapulgite clay 80%, leaf 10%, industrial water glass 10%;

[0042] Attapulgite clay porous ceramsite in this embodiment is prepared according to the following steps:

[0043] a, drying and pulverizing the attapulgite clay ore and passing through a 200-mesh sieve to obtain attapulgite powder;

[0044] B, the leaves are pulverized through a 200 mesh sieve, mixed with industrial water glass and the attapulgite powder obtained in step a to obtain a mixed powder;

[0045] c. Add water to the mixed powder and stir evenly. The amount of water added is 40% of the mass of the mixed powder. Granulate and shape, control the particle size at 5-7mm, then dry naturally, and then calcined in the air at 500°C for 2 hours to obtain attapulgite clay porous ceramsite.

[0046] The attapulgite clay porous ceramsite prepared in this example is used as a catalyst carrier:

...

Embodiment 3

[0052] The raw material of attapulgite clay porous ceramsite in the present embodiment is constituted by mass percentage: attapulgite clay 85%, sawdust 10%, industrial water glass 5%;

[0053] Attapulgite clay porous ceramsite in this embodiment is prepared according to the following steps:

[0054] a, drying and pulverizing the attapulgite clay ore and passing through a 200-mesh sieve to obtain attapulgite powder;

[0055] B, the sawdust is pulverized through a 200 mesh sieve, mixed with industrial water glass and the attapulgite powder obtained in step a to obtain a mixed powder;

[0056] c. Add water to the mixed powder and stir evenly, the amount of water added is 50% of the mass of the mixed powder, granulate and shape, control the particle size at 5-7mm, then dry naturally, and then calcined in the air at 550°C for 1 hours to obtain attapulgite clay porous ceramsite.

[0057] The attapulgite clay porous ceramsite prepared in this example is used as a catalyst carrier: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an attapulgite clay porous porous ceramsite, a preparation method of the ceramsite, and a purpose of the ceramsite. The ceramsite is prepared from raw materials of attapulgite clay and biomass, and a binder of industrial soluble glass. The ceramsite is prepared through calcining and oxidizing. The attapulgite clay porous ceramsite prepared by the present invention has advantages of high porosity, large specific surface area, high strength, strong water resistance, high water absorption, high catalytic activity, and the like. The porous ceramsite prepared by the presentinvention can be applied as a carrier for a catalyst, and a filling material for an aerated biological filter.

Description

1. Technical field [0001] The invention relates to the recycling and reuse of agricultural and sideline product wastes, in particular to attapulgite clay porous ceramsite and a preparation method and application thereof. 2. Background technology [0002] As a big agricultural country, my country is rich in biomass resources, mainly rice, wheat, rapeseed straw, and agricultural and sideline products, as well as a small amount of corn straw and other crop straws. Most of the traditional treatment methods are burning in the fields. This treatment method not only seriously pollutes the air, but also causes the death of microorganisms in the land, hardening the land and increasing the amount of chemical fertilizers. In recent years, the state has also promulgated a policy to prohibit the burning of straw and agricultural waste, but in some areas, the phenomenon of straw and agricultural waste is still incinerated. The smoke and dust in the air after the autumn harvest in my coun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/00C04B38/06C02F3/30B01J32/00
Inventor 彭书传鲍腾陈天虎王进岳正波舒林
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com