High hydroxy alkyd resin for polyurethane curing agent and preparation method thereof

A technology of polyurethane curing agent and high-hydroxy alkyd, applied in polyurea/polyurethane coatings, coatings, etc., can solve the problems of reduced effective NCO group content, reduced cross-linking reactivity, and reduced hardness of curing agent to achieve effective NCO Increased content, good cross-linking density, and increased hardness

Active Publication Date: 2011-08-17
CARPOLY CHEM GRP
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, when using the existing hydroxyl-containing alkyd resin and the isocyanate monomer containing NCO group to add reaction under certain reaction conditions to generate a two-component modified polyurethane curing agent containing active NCO group, the hardness of the curing agent itself is reduced, The effective NCO group content is reduced, and the crosslinking reaction activity is reduced, the crosslinking density is reduced, and the hardness is reduced when forming a film with a hydroxyl-containing paint component.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High hydroxy alkyd resin for polyurethane curing agent and preparation method thereof
  • High hydroxy alkyd resin for polyurethane curing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] The present invention will be described in detail below in conjunction with specific embodiments. The description in this part is only exemplary and explanatory, and should not have any limiting effect on the protection scope of the present invention.

[0046] It should be noted that: the lauric acid, benzoic acid, phthalic anhydride, pentaerythritol, glycerol, hypophosphorous acid, 2,6-di-tert-butyl-4-methylphenol, xylene and ethyl acetate used in the following examples are domestic Industrial grade raw materials.

[0047] The preparation method of the high hydroxyl alkyd resin of following embodiment all adopts the identical process that comprises following steps, just the proportioning difference of each raw material:

[0048] 1. Pre-pass N into a clean reactor 2 ↑5min (flow: 4m 3 / h);

[0049] 2. Add lauric acid, glycerin, benzoic acid, phthalic anhydride, pentaerythritol, hypophosphorous acid, 2,6-di-tert-butyl-4-methylphenol, xylene in sequence according to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high hydroxy alkyd resin for modifying a polyurethane curing agent, which is prepared from the following raw materials in parts by weight: 9-15 parts of lauric acid, 8-14 parts of benzoic acid, 16-22 parts of phthalic anhydride, 6-10 parts of pentaerythritol, 9-15 parts of glycerol, 0.05-0.1 part of hypophosphorous acid, 0.05-0.1 part of 2,6-ditertiary butyl-4-methylphenol, 9-13 parts of xylene and 22-28 parts of ethyl acetate. According to the formula, a small amount of lauric acid, and large amounts of aromatic polybasic acids containing benzene ring structure (benzoic acid and phthalic anhydride) are added to the alkyd resin, so that the resin has high glass transition temperature; and in addition, excessive polybasic alcohols are added to the resin, so that the content of effective hydroxyl groups in the molecular structure of the resin is high.

Description

technical field [0001] The invention relates to the technical field of curing agents, in particular to high-hydroxyl alkyd resins used for preparing polyurethane curing agents, and a preparation method thereof. Background technique [0002] At present, some alkyd resin manufacturers use hydroxyl-containing alkyd resins for the manufacture of two-component modified polyurethane curing agents. Due to the addition of a large amount of saturated fatty acids, such as lauric acid, and aromatic hard monomer polyacids The addition amount is small, so that the glass transition temperature of this type of hydroxyl-containing alkyd resin itself is low; and the excess of polyhydric alcohol in the resin formula is small, so that the effective hydroxyl content in the molecular structure of the resin is low. Therefore, when using the existing hydroxyl-containing alkyd resin and the isocyanate monomer containing NCO group to add reaction under certain reaction conditions to generate a two-c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/47C08G18/42C09D175/06
Inventor 朱建锋
Owner CARPOLY CHEM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com