Ecological ceramic tile and preparation method of the ecological ceramic tile

A ceramic brick and ecological technology, applied in the field of ecological ceramic bricks and its preparation, can solve the problems of low utilization rate of gold tailings, low utilization rate of tailings, complicated process, etc., and achieve value-added multi-functional, tailings The effect of high utilization rate and simple process

Inactive Publication Date: 2013-02-27
ZHEJIANG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These studies have found ways to reuse gold tailings, but all of them are materials with low added value and single function, and the utilization rate of gold tailings is not high
The inventor also used 5-25% gold tailings combined with bamboo charcoal powder to prepare multifunctional ceramsite in the publication number CN101580349, but the process is slightly complicated and the utilization rate of tailings is still low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1, a kind of ecological pottery brick, be that 70% gold tailings particle, 25% bamboo charcoal, 5% Zijin soil particle form main raw material by weight percentage, to account for main raw material gross weight 2% sodium silicate ( Sodium silicate aqueous solution) as binder, wherein gold tailings, bamboo charcoal, purple gold soil are all≤48μm, the modulus of sodium silicate is 3 and the concentration is 25% (that is, sodium silicate is Na 2 O 3SiO 2 , the mass concentration of sodium silicate in sodium silicate aqueous solution is 25%).

[0018] Its process steps are as follows:

[0019] 1) Add the gold tailings granules, bamboo charcoal granules, and purple gold soil granules of the above ratio into the mixer for mixing for 10 minutes (rotating speed 100 rpm), then add sodium silicate and mix for 60 min (rotating speed 100 rpm), Trapped material (i.e. stacking) 10h; get the mixture;

[0020] 2) Compress the mixture under 30MPa (the length, width, and hei...

Embodiment 2

[0023] Embodiment 2, a kind of ecological ceramic brick, be that 80% gold tailings particle, 10% bamboo charcoal, 10% purple gold soil particle are made up of raw material by weight percentage, with the sodium silicate that accounts for raw material gross weight 3% as bonding Agent, in which gold tailings, bamboo charcoal, and purple gold soil are all ≤48μm, and the modulus of sodium silicate is 3 and the concentration is 20%. Its process steps are as follows:

[0024] 1) Add the gold tailings granules, bamboo charcoal, and purple gold soil granules in the above ratio into the mixer for mixing for 7 minutes, then add sodium silicate and mix for 100 minutes, and then trap for 14 hours to obtain the mixture;

[0025] 2) Compress the mixture at 80MPa, and dry it naturally for 24 hours to obtain a dried molded product;

[0026] 3) Calcining the dried molded product at 1200° C. for 3 hours to obtain ecological ceramic tiles.

[0027] The produced eco-ceramic brick has a destructi...

Embodiment 3

[0028] Embodiment 3, a kind of ecological ceramic tile, be that 85% gold tailings particle, 5% bamboo charcoal, 10% purple gold soil particle are made up of raw material by weight percentage, with the sodium silicate that accounts for 4% of raw material gross weight as bonding Agents, in which gold tailings, bamboo charcoal, and purple gold soil are all ≤48μm, and the modulus of sodium silicate is 3 and the concentration is 30%. Its process steps are as follows:

[0029] 1) Add a certain amount of gold tailings particles, bamboo charcoal, and purple gold soil particles into the mixer for mixing for 15 minutes, then add sodium silicate and mix for 120 minutes, and then trap for 14 hours to obtain the mixture;

[0030] 2) Compress the mixture at 70MPa, and dry it naturally for 20 hours to obtain a dried molded product;

[0031] 3) Calcining the dried molded product at 1150° C. for 4 hours to obtain ecological ceramic tiles.

[0032] The produced eco-ceramic brick has a destruc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ecological ceramic tile. Main raw materials of the ecological ceramic tile comprise 70 to 90 percent of gold tailings particles, 5 to 25 percent of bamboo carbon and 5 to 15 percent of purple gold clay. Aqueous solution of sodium silicate, with the weight of 2 to 4 percent of the total weight of the raw materials, is used as a bonder. A preparation method of the ecological ceramic tile comprises the following steps of: 1, placing the main raw materials into a mixer to mix the main raw materials for 5 to 15 minutes, then adding the aqueous solution of sodium silicate to mix for 60 to 120 minutes and carrying out ageing mixture for 10 to 14 hours to obtain a mixture; 2, carrying out pressure forming on the mixture under the pressure of 30 to 80MPa and then naturally drying the obtained product by 12 to 24 hours to obtain a dried formed product; and 3, sintering the dried formed product for 2 to 4 hours at the temperature of 1,000 to 1,250 DEG C to obtain the ecological ceramic tile. The ecological ceramic tile has functions of ammonia adsorption, far infrared emission and the like.

Description

technical field [0001] The invention relates to an ecological ceramic brick and a preparation method thereof, in particular to a ceramic brick used for an interior wall and a production method thereof. Background technique [0002] In today's society, environmental protection has been deeply rooted in the hearts of the people, but the treatment of gold tailings in industry has always troubled people. A large number of tailings not only pollute the atmosphere, but also occupy arable land. Therefore, the reuse of gold tailings is a hot topic of research. Studies have shown that gold tailings can be used as raw materials for glass, to produce glass-ceramics, aerated concrete, hollow bricks, autoclaved bricks, etc. And the development of its new use has also been explored by people. [0003] Regarding the utilization of gold tailings in building materials, the publication number CN 101054308 uses 30-40% gold tailings to prepare breathable bricks, CN101289325 uses 55-75% to prep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/00C04B35/622B09B3/00
Inventor 郭兴忠李文彦杨辉涂志龙樊先平
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com