Environment-friendly biological plasticizer for biological specimen preservation

An environmentally friendly technology for biological specimens, applied to the preservation of plants, the preservation of human or animal bodies, and applications. It can solve problems such as damage to the health of operators, high production costs, and cumbersome production processes, and achieve cost reduction and improvement. Specimen stability and volatility are good

Active Publication Date: 2011-07-27
山东聚众数字医学科技开发有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the preservation of biological specimens is mainly soaked in formaldehyde (formalin), or plasticized by silica gel for biological specimens. Formaldehyde is toxic and odorous. Harmful to the human body and pollute the environment
Using silica gel to make biological plasticized specimens, the production process is cumbersome, and the reagents used contain volatile organic solvents and chloroplatinic acid, which will damage the health of the operator during the specific operation
At the same time, they also have problems such as short storage time, easy deformation, and high production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly biological plasticizer for biological specimen preservation
  • Environment-friendly biological plasticizer for biological specimen preservation
  • Environment-friendly biological plasticizer for biological specimen preservation

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0024] The specific embodiment: the specific embodiment of the present invention is described in detail below:

[0025] Raw material preparation:

[0026] Silicone resin: using hydroxyl-terminated methyl silicone oil, its chemical structure is as follows:

[0027]

[0028] n=50~600, molecular weight is 5000~40000.

[0029] Plasticizer: using methyl-terminated methyl silicone oil, its chemical structure is as follows:

[0030]

[0031] n=5~600, molecular weight is 500~40000.

[0032] Catalyst: using organotin, its chemical structure is as follows:

[0033]

[0034] where R 1 for C 2 h 5 ~C 8 h 17 One of the R 2 for C 6 h 13 ~C 12 h 25 One of.

[0035] Cross-linking curing agent: organosiloxane is used, and its chemical structure is as follows:

[0036]

[0037] where R 3 for CH 3 ~C 2 h 5 One of the R 4 for CH 3 ~C 2 h 5 or NH 2 CH 2 CH 2 CH 2 One of.

Embodiment 1

[0038] Embodiment 1: Take 2 kg of hydroxyl-terminated methyl silicone oil (n=50~600 in this embodiment, molecular weight is 5000~40000), methyl-terminated methyl silicone oil (n=5~50 in this embodiment, molecular weight is 500 ~5000) 2 kilograms, organotin (this embodiment R 1 for C 2 h 5 ,R 2 for C 6 h 13 , which is 0.1 kg of tin diethyl dihexanoate) and 0.2 kg of organosiloxane (the present embodiment R 3 for CH 3 ,R 4 for CH 3 , which is tetramethoxysilane) to form a plasticizer.

Embodiment 2

[0039] Embodiment 2: Take 2 kg of hydroxyl-terminated methyl silicone oil (n=50-600 in this embodiment, molecular weight is 500-40000), methyl-terminated methyl silicone oil (n=5100 in this embodiment, molecular weight is 500-10000 ) 0.4 kg, organotin (the present embodiment R 1 for C 8 h 17 ,R 2 for C 12 h 25 , which is 0.01 kg of dioctyltin dilaurate) and 0.04 kg of organosiloxane (the present embodiment R 3 for C 2 h 5 ,R 4 for C 2 h 5 , which is tetraethoxysilane) to form a plasticizer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly biological plasticizer for biological specimen preservation, which is prepared from the following components in parts by weight: 100 parts of silicone resin, 20-100 parts of plasticizer, 0.5-5 parts of catalyst and 2-10 parts of crosslinking and curing agent, wherein the silicone resin is hydroxyl-terminated methyl silicone oil, the plasticizer is methyl-terminated methyl silicone oil, the catalyst is organotin, and the crosslinking and curing agent is organosiloxane. The invention has the advantages of no toxicity, no harm, no smell and no pollution, and is transparent; the specimen plasticized by the plasticizer has the advantages of strong authenticity, good hand feeling and high vividness, and can be stored for a long time; the environment-friendly biological plasticizer for biological specimen preservation can ensure the manufacture of biological specimens to be carried out at ordinary temperature, and avoids using chloro-platinic acid and other noble and highly-corrosive reagents, thereby greatly lowering the cost and reducing the harm to operating personnel; and the invention avoids using a diluter, and simplifies the operation steps.

Description

Technical field: [0001] The invention relates to an environment-friendly biological plasticizer used for preserving biological specimens, and belongs to the technical field of plasticizers. Background technique: [0002] At present, the preservation of biological specimens is mainly soaked in formaldehyde (formalin), or the biological specimens are plasticized with silica gel. Formaldehyde is poisonous and odorous, which is harmful to the human body and pollutes the environment. Using silica gel to make biological plasticized specimens is cumbersome, and the reagents used contain volatile organic solvents and chloroplatinic acid, which will damage the health of the operator during the specific operation. At the same time, they also have problems such as short storage time, easy deformation, and high production cost. Invention content: [0003] The purpose of the present invention is to overcome the deficiencies of the above-mentioned prior art and provide a non-toxic, har...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/06C08L83/04C08K5/5415A01N1/00A01N3/00
Inventor 黄飞张春雷张路萍周帅
Owner 山东聚众数字医学科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com