Light noise-reducing modified polypropylene material and preparation method thereof
A polypropylene material and polypropylene technology, applied in the field of lightweight noise-reducing modified polypropylene material and its preparation, can solve the problems of increasing the weight of the final product, and achieve the effects of improving mechanical properties, uniform dispersion, and good material properties
Active Publication Date: 2011-07-20
JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
View PDF4 Cites 14 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, since the density of these inorganic mineral fillers is often higher than that of plastics, adding mineral fillers to plastics will relatively increase the weight of the final product (see Table 1 for the impact of inorganic mineral filler content on the density of polypropylene materials)
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0043] The formulation of the lightweight noise-reducing modified polypropylene material in this embodiment is listed in Table 5-1:
[0044] Table 5-1
[0045]
Embodiment 2
[0047] The formulation of the lightweight noise-reducing modified polypropylene material in this embodiment is listed in Table 5-2:
[0048] Table 5-2
[0049]
Embodiment 3
[0051] The formula of the lightweight noise-reducing modified polypropylene material of this embodiment is listed in Table 5-3:
[0052] Table 5-3
[0053]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
degree of grafting | aaaaa | aaaaa |
Login to view more
Abstract
The invention relates to a light noise-reducing modified polypropylene material and a preparation method thereof. The material is prepared from the following raw materials in percentage by weight: 39 to 93.5 percent of polypropylene, 5 to 45 percent of inorganic filler, 1 to 10 percent of dispersing agent, 0.3 to 5 percent of coupling agent and 0.2 to 1 percent of antioxidant, wherein the inorganic filler is hollow inorganic particles. By adding the hollow particle inorganic filler into the material, the mechanical properties of the material are improved and the low density of the material is kept; meanwhile, due to the special structure of the hollow particles, the material has certain noise reducing function, and has high application value for lightening automobiles, damping and reducing noise. In addition, the light noise-reducing modified polypropylene material is prepared by introducing the inorganic filler into a screw extruder through a plurality of lateral feeding holes at different positions and performing extrusion, so that the hollow structure of the inorganic filler is not easy to break when the inorganic filler is subjected to melt extrusion, the inorganic filler can be more uniformly dispersed in a matrix, and the prepared material has better performance.
Description
technical field [0001] The invention relates to a lightweight noise-reducing modified polypropylene material and a preparation method thereof, which can be applied in the field of automobile manufacturing. Background technique [0002] In the plastic modification industry, inorganic minerals such as talcum powder, mica, calcium carbonate, glass beads, wollastonite, glass fiber, etc. are generally used as filling and reinforcing components, and the polypropylene (PP) is improved by blending modification. ) The rigidity, heat resistance, molding shrinkage and other properties of the material to meet the use requirements of the final plastic product. However, since the density of these inorganic mineral fillers is often higher than that of plastics, adding mineral fillers to plastics will relatively increase the weight of the final product (see Table 1 for the effect of inorganic mineral filler content on the density of polypropylene materials). [0003] Nowadays, non-renewabl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/12C08L51/06C08K13/04C08K7/24C08K7/28C08K5/544C08K5/13C08K5/524B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704B29C2948/92895
Inventor 周英辉孙刚李欣李志平程文超陈延安丁超李国明黄达罗忠富
Owner JIANGSU KINGFA SCI & TECH ADVANCED MATERIALS CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap