A technology of emulsified asphalt and permeable layer, which is applied to building components, building insulation materials, buildings, etc. It can solve the problems of fast emulsified asphalt demulsification, hinder the penetration of asphalt droplets, and poor permeability, so as to prolong the demulsification speed and reduce the Low viscosity and low volatility

Active Publication Date: 2011-05-11
CHINA PETROLEUM & CHEM CORP +1
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing emulsified asphalt for penetration layer generally has the problem of poor permeability, mainly because: 1. The high viscosity of emulsified asphalt hinders the penetration of asphalt droplets; 2. The emulsified asphalt demulsification speed is fast, and the emulsified asphalt has not fully penetrated. When it goes down, it breaks the emulsion and forms an oil skin on the surface of the base layer that can be stuck by the truck and paver
Although adding diluents such as gasoline and kerosene to emulsified asphalt can increase the permeability of emulsified asphalt, it will bring about a significant increase in cost and environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing penetrated emulsified asphalt
  • Method for preparing penetrated emulsified asphalt
  • Method for preparing penetrated emulsified asphalt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Tahe light residual oil 200g, lubricating oil furfural refined extract oil mixed with FCC oil slurry 1:1 for a total of 15g, emulsifier JYR3 and octadecylamine mixed with a ratio of 10:2 for a total of 6g, CaCl 2 0.5g, emulsifier and stabilizer, add water to 260g, cationic SBR latex 25g. 75% of the above materials by figure 1 As shown, the product is emulsified through a colloid mill with a mill gap of 10 μm, and the obtained product directly enters the finished product tank, and the colloid mill gap is adjusted to 5 μm, and the remaining 25% of the material is emulsified through a colloid mill with a mill gap of 5 μm, and then enters the finished product tank and mixes with the previous product evenly That is the finished product. The finished product meets the requirements of JTG F40-2004 cationic emulsified asphalt for penetration, and its main properties are shown in Table 2.

Embodiment 2

[0031] Maoming 70# asphalt 200g, four-line and fatty acid leftovers mixed 1:1 for a total of 40g, emulsifier JYR5 and 1631 mixed in a ratio of 10:1 for a total of 8.25g, NH 4 Add water to Cl 1.0g to 235g, cationic SBR latex 25g. 50% of the above materials are emulsified through a colloid mill with a mill gap of 15 μm, and the resulting product enters the finished product tank directly; the colloid mill gap is adjusted to 4 μm, and the remaining 50% of the material is emulsified through a colloid mill with a mill gap of 4 μm, and then enters the finished product tank with the previous The product is mixed evenly to obtain the finished product. The finished product meets the requirements of JTGF40-2004 cationic emulsified asphalt for penetration, and its main properties are shown in Table 2.

[0032] Table 1 Technical indicators of cationic SBR latex for modified asphalt

[0033] project name

technical indicators

Exterior

milky

Solid content (%) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing penetrated emulsified asphalt. The method comprises the following steps of: (1) preparing aqueous solution by using an asphalt emulsifier and a stabilizer; (2) heating and melting asphalt and / or residual oil, and mixing the melt and a diluent; (3) adding cationic styrene butadiene rubber (SBR) latex to increase the adhesiveness of residues; and (4) emulsifying partial materials in the steps (1), (2) and (3) through a colloid mill with a larger mill clearance, filling obtained products into a finished product tank, turning down the mill clearance of the colloid mill, emulsifying the remaining part of the materials through the colloid mill, filling obtain products into the finished product tank, and uniformly mixing the obtained products and the previous products to obtain a final finished product. By the method, an emulsifying machine meets requirements on different mill clearances, equipment cost is saved compared with that of two colloidmills; and the permeability of the prepared high-permeable penetrated emulsified asphalt is improved, and the indexes such as ductility, sticky toughness and the like are improved at the same time. The penetrated emulsified asphalt can be used in the fields of penetrated oil, cold regeneration of asphalt pavements, slurry sealing and the like.

Description

technical field [0001] The invention relates to a method for preparing emulsified asphalt, in particular to a method for preparing emulsified asphalt with low cost and strong permeability. Background technique [0002] The permeable layer located on the surface of the asphalt pavement base layer plays the role of consolidation, stability, waterproof, and connection of various road structural layers, which is crucial to the quality and life of the pavement. The penetration depth of the penetrating layer oil determines whether the asphalt surface layer can be well combined with the non-asphalt material base. Commonly used penetrating layer oils include coal tar, diluted asphalt and emulsified asphalt. Coal tar is highly permeable but toxic, and is basically not used at home and abroad; diluted asphalt has good penetration, but the cost is high, and at the same time, it will pollute the environment due to too much oil content, and there are hidden dangers to the impact on the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L9/08C08J3/02
Inventor 张静程国香宁爱民李志军郭皎河刘树华陈保莲
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap