Method for rapidly testing casting blank segregation by utilizing direct-reading spectrometer

A technology of direct-reading spectrometer and direct-reading spectrum, which is applied in the field of metallurgical analysis and detection, can solve the problems of high detection cost, long inspection cycle, and complex sample preparation for in-situ analysis, and achieve the effect of overcoming the complexity of sample preparation

Inactive Publication Date: 2011-01-19
HBIS COMPANY LIMITED HANDAN BRANCH COMPANY
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for quickly inspecting slab segregation by using a direct-reading spectrometer, which is suitable for use in production plants. Shortcomings such as high cost, meet the quantitative detection of the general requirements for casting slabs in continuous casting production, and solve the above-mentioned problems in the background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for rapidly testing casting blank segregation by utilizing direct-reading spectrometer
  • Method for rapidly testing casting blank segregation by utilizing direct-reading spectrometer
  • Method for rapidly testing casting blank segregation by utilizing direct-reading spectrometer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described through the embodiments below in conjunction with the accompanying drawings.

[0019] A method for quickly inspecting slab segregation by using a direct-reading spectrometer, using a direct-reading spectrometer to simulate the in-situ analyzer to detect the segregation of the cast slab, the direct-reading spectrometer to dot the sample in sections, and the simulated in-situ analyzer to test the sample Analysis, to quantify the macro-segregation of the continuous casting slab.

[0020] Embodiment Test condition: 1, apparatus and equipment: ARL3460 direct-reading spectrometer (thermo group ARL company), test equipment CWY-II-5KW AC voltage stabilizer (produced in Guangdong); CZN-4 type argon purifier (produced in Sichuan); BS01-03 automatic sample grinding machine (made in Germany); HB-3000 automatic sample grinding machine (made in Germany); ZYM-2 rotary polishing machine (made in Beijing); HS-FF automatic sample milling ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for rapidly testing casting blank segregation by utilizing a direct-reading spectrometer, which is suitable for the quantitative and trending detection in the casting blank segregation, belonging to the technical field of metallurgy analyzing and detecting. In the method, the direct-reading spectrometer is adopted to simulate an in-situ analyzer to detect the casting blank segregation; and the direct-reading spectrometer segments and dots a test sample, and simulates the in-situ analyzer to analyze the test sample, so as to quantitatively detect the continuously cast blank macrosegregation. The method can overcome the defects that the in-situ analysis sample preparation is complex, the testing period is long, the detection cost is high and the like, satisfies the generalized quantitative detection to the casting blank in the continuous casting production, and provides a good popularization and reference method for the iron and steel enterprises owning rapid spectrum analyzers in the trending and quantitative detection of the continuously cast blank segregation. Compared with the traditional pickling method for detecting the casting blank segregation, the method has the same trend on the description of the casting blank segregation as that of the pickling method; the casting blank segregation result detected by the direct-reading spectrometer not only can describe the casting blank segregation condition, simultaneously can clearly describe the component segregation curve of each element, and has the visual digitized function.

Description

technical field [0001] The invention relates to a method for rapidly inspecting slab segregation by using a direct-reading spectrometer, and is especially suitable for quantitative and trend detection of slab segregation in iron and steel enterprises. The invention belongs to the technical field of metallurgical analysis and detection. Background technique [0002] With the rapid development of rapid detection technology, the application of rapid spectral analysis in iron and steel enterprises has been rapidly promoted. Due to its convenience, speed and accuracy, rapid spectral analysis has played an important role in efficient production, energy saving and consumption reduction. It has been well applied in the rapid detection of components. At present, the daily inspection method for the internal quality inspection of continuous casting slabs is to carry out sulfur stamping or pickling inspection for each casting. The detection of defects cannot meet the digital quantitat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N21/67G01N1/28
Inventor 李金波胡志刚李兰群朱开军尹艳清范佳刘红艳
Owner HBIS COMPANY LIMITED HANDAN BRANCH COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products