Ultrahigh strength cold rolled steel strip for automobile seat

Abstract

The invention relates to an ultrahigh strength cold rolled steel strip for an automobile seat, which comprises the following components in percentage by mass: 0.17 to 0.23 percent of C, below 0.01 percent of P, below 0.01 percent of S, 0.15 to 0.35 percent of Si, 0.60 to 0.90 percent of Mn, 0.15 to 0.35 percent of Mo, 0.40 to 0.65 percent of Cr, 0.40 to 0.70 percent of Ni, and the balance of Fe. The yield strength 6s of the ultrahigh strength cold rolled steel strip is 300 to 400MPa, the tensile strength 6b is 350 to 550MPa, the elongation rate delta is more than or equal to 30 percent, and the hardness is 75 to 85; and the ultrahigh strength cold rolled steel strip has high flanging performance.

Description

technical field [0001] The invention relates to an ultra-high-strength cold-rolled steel plate, in particular to an ultra-high-strength cold-rolled steel strip for automobile seats. Background technique [0002] In recent years, affected by the demand for lightweight automobiles, ultra-high-strength cold-rolled steel sheets with a tensile strength of 880-1170MPa are gradually being used in the framework of automobile seats. Since the car seat frame is manufactured by stamping, the ultra-high-strength cold-rolled steel sheet is required to have an excellent flanging performance with a hole expansion rate of more than 75% after punching as stipulated in JFST1001-1996. [0003] On the other hand, ultra-high-strength cold-rolled steel sheets with a tensile strength of 880 MPa or more are now used as reinforcement materials for shock absorbers and doors. In order to improve its processing performance and welding performance, various researches have been carried out. For example...

AI Technical Summary

Problems solved by technology

Therefore, at best, the hole expansion rate stipulated in JFSTIOO-1996 is about 50%, which cannot be applied to the manufacture of car seat frames by stamping.

Images