Application of asymmetric structure regulator containing nitrogen and oxygen heteroatoms

A structure regulator and heteroatom technology, which is applied in the field of butadiene anionic polymerization, can solve the problems of temperature sensitivity and large dosage, achieve high coupling efficiency, solve large dosage, and facilitate the coupling reaction

Inactive Publication Date: 2010-09-29
BEIJING UNIV OF CHEM TECH
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention aims at the problems that the adjustment function of the existing ether and amine structure regulators is sensitive to temperature and the dosage is relatively large, and develops a new type of N-alkyltetrahydrofurfurylamine microstructure regulator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of asymmetric structure regulator containing nitrogen and oxygen heteroatoms
  • Application of asymmetric structure regulator containing nitrogen and oxygen heteroatoms
  • Application of asymmetric structure regulator containing nitrogen and oxygen heteroatoms

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

Embodiment 2

Embodiment 3

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses the application of an asymmetric structure regulator containing nitrogen and oxygen heteroatoms; the regulator is an N- alkyl tetrahydro bran amine compound, and the structural formula thereof is as follows: wherein R1 is alkyl which comprises 1 to 4 carbons and R2 is the alkyl which comprises 1 to 4 carbons; the regulator can be applied to controlling the microstructures of butadiene homopolymer and copolymer, and the molar ratio R of the regulator to an initiator is 0.01 to 6; if N, N-tetrahydro furfuryl dimethyl amine serves as the regulator, when R is 0.65 AT 50DEG C, the content of the butadiene 1, 2 structure reaches 72.3 percent, thereby solving the problem of large used amount of the regulator in industry, having small impact on the reaction activity, facilitating coupling reaction and having high industrial application valve.

Description

technical field The invention relates to an asymmetric structure regulator containing nitrogen and oxygen heteroatoms and its application in controlling the microstructure of butadiene homopolymers and copolymers, belonging to the field of butadiene anion polymerization. Background technique A variety of homopolymers and copolymers of butadiene can be synthesized by anionic polymerization, and their microstructure has a great influence on the performance of the product. For example, in terms of homopolymers, the content of 1,2-structure of low cis-butylene, butylated hydroxy and butyl carboxyl gum, medium vinyl and high vinyl polybutadiene is ~10%, <40%, 35%, respectively. %~65% and >70%, the 1,2 structure determines that they have different uses. It can be seen that it is very important to effectively adjust and control the microstructure of the formed product in the research and production process of butadiene anionic polymerization. The polymer microstructure main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F136/06C08F236/10C08F2/38
Inventor 韩丙勇陈成鑫鲁建民
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com