Preparation method of low-carbon asphalt mixture

A mixture and carbon asphalt technology, which is applied in the field of low-carbon asphalt mixture preparation, can solve the problems of reducing asphalt mixture mixing temperature and paving temperature, reducing carbon dioxide, and large emissions

Active Publication Date: 2010-09-22
SHANGHAI TONGJI CONSTR QUALITY INSPECTION STATION
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the hot mix asphalt carbon dioxide (CO 2 ) discharge amount is big, consumes many deficiencies in energy, the purpose of the present invention is to provide a kind of preparation method of low-carbon asphalt mixture, it is by directly adding low-carbon agent in asphalt or adding low-carbon agent in asphalt mixture mixing process agent, thereby reducing carbon dioxide (CO 2 ) emission, which reduces the mixing temperature and paving temperature of asphalt mixture, reduces fuel consumption per unit output, and reduces energy consumption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of low-carbon asphalt mixture
  • Preparation method of low-carbon asphalt mixture
  • Preparation method of low-carbon asphalt mixture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1: the preparation of low carbon asphalt mixture AC-13 (do not add fiber stabilizer)

[0035] (1) Detection of performance of low carbon agent modified asphalt, selection of aggregate and gradation

[0036] In this example, the dosage of low-carbon agent is 3%, and the binder is 70# matrix asphalt. The required 70# matrix asphalt is required to meet the relevant requirements of "Technical Specifications for Highway Asphalt Pavement Construction" (JTG F40-2004). Firstly, the basic performance of the modified asphalt mixed with low carbon agent was tested, and the test results are shown in Table 1.

[0037] Table 1 The basic performance test results of 70# base asphalt + 3% low carbon agent

[0038]

[0039]

[0040] The coarse aggregate used is basalt and the fine aggregate is limestone, both of which meet the relevant requirements of "Technical Specifications for Construction of Highway Asphalt Pavement" (JTG F40-2004). For this example, the gradation...

Embodiment 2

[0063] Embodiment 2: the preparation of low-carbon asphalt mixture SMA-13 ​​(add fiber stabilizer)

[0064] (1) Detection of properties of low carbon agent modified asphalt, selection of fiber stabilizer, aggregate and gradation

[0065] In this example, the dosage of low-carbon agent is 5%, and the binder is SBS modified asphalt. The selected SBS modified asphalt is required to meet the relevant requirements of "Technical Specifications for Highway Asphalt Pavement Construction" (JTG F40-2004). Firstly, the basic properties of the modified asphalt mixed with low carbon agent were tested, and the test results are shown in Table 6.

[0066] Table 6 Basic performance test results of SBS modified asphalt + 5% low carbon agent

[0067]

[0068]

[0069] The coarse aggregate used is diabase, the fine aggregate is limestone, and the filler is mineral powder obtained by grinding limestone. After inspection, they all meet the relevant requirements of "Technical Specifications ...

Embodiment 3

[0082] Embodiment 3: Preparation of low-carbon asphalt mixture OGFC-13

[0083] (1) Detection of performance of low carbon agent modified asphalt, selection of aggregate and gradation

[0084] In this example, the dosage of low-carbon agent is 6.5%, and the binder is 70# matrix asphalt. The required 70# matrix asphalt is required to meet the relevant requirements of "Technical Specifications for Highway Asphalt Pavement Construction" (JTG F40-2004). Firstly, the basic properties of the modified asphalt mixed with low carbon agent were tested, and the test results are shown in Table 10.

[0085] Table 11 Basic performance test results of 70# base asphalt + 6.5% low carbon agent

[0086]

[0087] The target porosity of the drainage pavement is generally set at 18% to 25%, and the target porosity of this example is set at 20%. The purpose of selecting the initial test gradation is to determine a reasonable gradation that satisfies the target void ratio under the initial test...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
melting pointaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of highways and urban roads, and in particular relates to a preparation method of a low-carbon asphalt mixture. The preparation method comprises the concrete step of directly adding a low-carbon agent into modified asphalt or substrate asphalt, which reduces the emission of carbon dioxide, the mixing temperature and the paving temperature of the asphalt mixture and the consumption of energy sources. The mixing temperature is generally 110-140DEG C and the compaction temperature is generally 80-100DEG C; and compared with the hot mixing asphalt mixture, the emission of the carbon dioxide is reduced by over 45 percent and the consumption of the energy sources can be reduced by 12-18 percent. The preparation method can play roles of reducing the emission of the carbon dioxide and saving the energy sources, is a preparation method of the asphalt mixture with greenness, environmental protection and energy saving and can be applied to paving the urban roads, various grades of highways and other pavement engineering.

Description

technical field [0001] The invention belongs to the technical field of roads and urban roads, and in particular relates to a preparation method of low-carbon asphalt mixture. Background technique [0002] At present, air pollution and energy shortage are common challenges faced by mankind. Climate scientists say the world must stop increasing greenhouse gas emissions and start reducing them between 2015 and 2020, as scientists estimate that global greenhouse gas emissions will need to be reduced by 100% by 2050 if the global average temperature is to rise by 2°C. 80% of 1990 levels. How to protect the living environment and save natural resources while developing the economy has become a topic faced by countries all over the world. As early as September 8, 2007, at the 15th Asia-Pacific Economic Cooperation (APEC) Leaders' Meeting, Chinese President Hu Jintao clearly advocated "developing a low-carbon economy" based on a highly responsible attitude towards human beings and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28B1/00
Inventor 叶奋周基钊武金婷周孔
Owner SHANGHAI TONGJI CONSTR QUALITY INSPECTION STATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com