Fast-curing casting resin for bathroom accessories and preparing and using methods thereof

A fast-curing, finished product technology, applied in the production field of sanitary products, can solve the problems of easy scratches on the surface of semi-finished products, low yield rate, and scrapped finished products, and achieve the effects of high strength, energy saving, and less damage

Inactive Publication Date: 2010-09-15
上海澳金玻璃钢制品有限公司
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the semi-finished product needs to be transported before curing, the surface of the semi-finished product is prone to scratches during this process, so that the finished product is scrapped
In addition, the castable used in the traditional casting process is prone to cracking in the mold, which also leads to low yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A casting fast-curing resin for sanitary products, which uses ortho-phthalic unsaturated polyester resin as the base resin, and includes the following components by weight percentage:

[0041] Ortho-phthalic unsaturated polyester resin 19.8%

[0042] (Produced by Changzhou Youbang Paint Co., Ltd., it is an unsaturated polyester resin with phthalic anhydride and diethylene glycol as the main raw materials)

[0043] 200 mesh calcium carbonate 30.8%

[0044] 300 mesh calcium carbonate 24.8%

[0045] Quartz sand 16.5%

[0046] White microbeads 8.1%;

[0047] A small amount of additives are also added to the formula, including accelerator: cobalt isooctanoate (Jiangyin Qianjin Chemical Co., Ltd.); low shrinkage agent: 300 mesh to 400 mesh polyethylene ultrafine powder (Swiss DuPont); curing agent: active oxygen content 9% methyl ethyl ketone peroxide with dimethyl ester as diluent (Luoyang Shuangyue Co., Ltd.). Among them, the addition of the accelerator is 0.6% of the ...

Embodiment 2

[0052] A casting fast-curing resin for sanitary products, which uses ortho-phthalic unsaturated polyester resin as the base resin, and includes the following components by weight percentage:

[0053] Ortho-phthalic unsaturated polyester resin 18.8%

[0054] 200 mesh calcium carbonate 31.3%

[0055] 300 mesh calcium carbonate 22.5%

[0056] Quartz sand 17.6%

[0057] White microbeads 9.8%;

[0058] Accelerator, low shrinkage agent and curing agent are all identical with embodiment 1.

[0059] The addition of accelerator is 0.4% of the weight of o-phthalic unsaturated polyester resin, the addition of low shrinkage agent is 1% of the weight of ortho-phthalic unsaturated polyester resin, and the addition of curing agent is 0.4% of the weight of o-phthalic unsaturated polyester resin. 1.9% by weight of polyester resin.

[0060] The preparation method and use method are all the same as in Example 1.

[0061]

Embodiment 3

[0063] A casting fast-curing resin for sanitary products, which uses ortho-phthalic unsaturated polyester resin as the base resin, and includes the following components by weight percentage:

[0064] Ortho-phthalic unsaturated polyester resin 21.7%

[0065] 200 mesh calcium carbonate 29.6%

[0066] 300 mesh calcium carbonate 25.8%

[0067] Quartz sand 15.3%

[0068] White microbeads 7.6%;

[0069] Accelerator, low shrinkage agent and curing agent are all identical with embodiment 1.

[0070] The addition of accelerator is 0.8% of the weight of o-phthalic unsaturated polyester resin, the addition of low shrinkage agent is 1% of the weight of ortho-phthalic unsaturated polyester resin, and the addition of curing agent is 2.2% by weight of polyester resin.

[0071] The preparation method and use method are all the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to a fast-curing casting resin for bathroom accessories and a preparing method and a using method thereof. In the fast-curing casting resin for the bathroom accessories, o-phenyl type unsaturated polyester resin is used as a matrix resin; and the fast-curing casting resin comprises the following materials in percentage by weight: 18 to 22 percent of o-phenyl type unsaturated polyester resin, 28 to 32 percent of 200-mesh calcium carbonate, 22 to 26 percent of 300-mesh calcium carbonate, 14 to 18 percent of quartz sand and 15 to 10 percent of white micro-bead. A small amount of additive is also added into the formula, and the additive comprises an accelerating agent, a low contraction agent and a curing agent, wherein the addition of the accelerating agent is 0.2 to 0.8 percent of the weight of the o-phenyl type unsaturated polyester resin, the addition of the low contraction agent is 1 to 1.1 percent of the weight of the o-phenyl type unsaturated polyester resin, and the addition of the curing agent is 1.6 to 2.2 percent of the weight of the o-phenyl type unsaturated polyester resin. The demolded semi-finished product of the casting resin does not need the steps of pressing and re-curing, so the energy consumption is greatly reduced. Meanwhile, the surface of the semi-finished product is hardly scratched, and at least 50 percent of labor can be saved.

Description

technical field [0001] The invention belongs to the production field of sanitary products, in particular to a fast-curing casting resin for sanitary products and its preparation and use method. Background technique [0002] The existing sanitary products casting process usually takes the following steps: [0003] Spray the gel coat resin in the mold first, and then cast the body of the bathroom products after the gel coat is cured. After about 30 to 40 minutes, the castable is cured and released from the mold, but the strength of the castable is only 25 to 30 when it is fully cured. %, the product is easily deformed, it needs to be placed on a flat flat shelf, and 3 to 4 sandbags are pressed, each sandbag is 4 to 5 kg, so as to avoid diagonal warping and deformation of the semi-finished product before it is completely cured. After pressing, the semi-finished product still needs to be drilled, ground and other technological steps. Due to the low strength of the semi-finished...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/06C08L23/06C08K13/04C08K3/26C08K3/34C08K5/098C08K5/14C08K7/18C08K3/36C08K3/22B29C39/44
Inventor 王运来
Owner 上海澳金玻璃钢制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com