Process for manufacturing a galvannealed steel sheet by DFF regulation

A steel sheet and coating technology, which is applied in the direction of manufacturing tools, coatings, hot-dip galvanizing, etc., can solve problems such as the cost impact of steel sheets

Active Publication Date: 2010-08-18
ARCELORMITTAL INVESTIGACION Y DESARROLLO SL +1
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this has the major drawback that high levels of tensile strength, i.e. around 800 MPa, can only be achieved when the carbon content is increased
However, this has an impact on the cost of the steel sheet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for manufacturing a galvannealed steel sheet by DFF regulation
  • Process for manufacturing a galvannealed steel sheet by DFF regulation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0054] The invention will now be illustrated by way of an example provided in a non-limiting manner and with reference to FIGS. 1 and 2 .

[0055] Tests were carried out using samples A and B from 0.8 mm thick sheets made of steel sheets with the composition shown in Table I.

[0056] Samples A and B were preheated from ambient temperature (20°C) to 750°C in a direct-fired furnace, and they were subsequently and continuously annealed in a radiant tube furnace in which they were heated from 750°C to 800°C, then soak them at 800°C for 60s, and finally cool them down to 460°C. The atmosphere in the radiant tube furnace contains 30% by volume of hydrogen, the balance being nitrogen and unavoidable impurities.

[0057] After cooling, samples A and B were hot-dip galvanized in a molten zinc-based bath containing 0.12% by weight of aluminum, the balance being zinc and unavoidable impurities. The temperature of the bath was 460°C. After sweeping with nitrogen and cooling the zinc-b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention deals with a process for manufacturing a hot-dip galvannealed steel sheet having a TRIP microstructure, and comprising, by % by weight, 0.01 <= C <= 0.22%, 0.50 <= Mn <= 2.0%, 0.5 < Si <= 2.0%, 0.005 <= Al <= 2.0%, Mo < 0.01 %, Cr <=1.0%, P < 0.02%, Ti <= 0.20%, V <= 0.40%, Ni <= 1.0%, Nb <= 0.20%, the balance of the composition being iron and unavoidable impurities resulting from the smelting, said process comprising the steps consisting in: - oxidizing said steel sheet in order to form a layer of iron oxide on the surface of the steel sheet, and to form an. internal oxide of at least one type of oxide selected from the group consisting of Si oxide, Mn oxide, Al oxide, complex oxide comprising Si and Mn, complex oxide comprising Si and Al complex oxide comprising Al and Mn, and complex comprising Si, Mn and Al, - reducing said oxidized steel sheet in order to reduce the layer of iron oxide, - hot-dip galvanising said reduced steel sheet to form a zinc-based coated steel sheet, and - subjecting said zinc-based coated steel sheet to an alloying treatment to form a galvannealed steel sheet.

Description

technical field [0001] The present invention relates to a method of manufacturing a hot-dip galvanized annealed steel sheet having a TRIP microstructure. Background technique [0002] In order to meet the need to lighten the structure of powered land vehicles, it is known to use TRIP steels (the term TRIP stands for Transformation Induced Plasticity), which combine high mechanical strength with the possibility of very high deformation levels. TRIP steels have a microstructure comprising ferrite, retained austenite and optionally martensite and / or bainite, which allows them to achieve tensile strengths of 600-1000 MPa. This type of steel is widely used in the production of energy absorbing parts such as structural and safety parts such as longitudinal members and reinforcements. [0003] Steel sheets are usually coated with a zinc-based coating by hot-dip galvanizing before being sent to the car manufacturer in order to improve corrosion resistance. After leaving the zinc b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/02C23C2/06C23C2/28
CPCC23C2/02C21D9/46C21D9/561C23C2/28C23C2/06C23C2/40C22C1/002C21D1/52C22C1/11C23C2/0222C23C2/0224C23C2/261
Inventor J-M·马泰格纳F·波特兰德
Owner ARCELORMITTAL INVESTIGACION Y DESARROLLO SL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com