Problems solved by technology

[0015] However, in high-efficiency welding using smaller-diameter flux-cored wires and high-efficiency manufacturing processes for producing smaller-diameter flux-cored wires, the problem of such burrs is as described above, both in welding quality and manufacturing. Efficiency has become a problem that must be solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making a flux cored wire
  • Method for making a flux cored wire
  • Method for making a flux cored wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0095] Hereinafter, examples of the present invention will be described. Using the aforementioned Figure 5-8 The butt joint forming process and conditions shown, the flux-cored wire manufacturing process and conditions shown in Fig. 9(a), and the manufacturing Flux-cored wire of product diameter.

[0096] At this time, a hoop made of commercially available mild steel plate was used, a flux containing Fe-Cr and zircon sand was used as the main component, and the above-mentioned lubricant containing molybdenum disulfide was used as a sulfur-based extreme pressure agent to manufacture the hoop. W: 12mm, thickness t: 0.96mm.

[0097] Here, in the butt joint forming process, as described above Figure 5-8 In the preferred process conditions shown, on the butt joint forming line (workbench) 20, the hoops 1, 1 are butted with the burrs 2, 2 on both sides facing upward, and the raw material hoops that are joined by welding the butt joints 1, 1, in this state, make the burrs 2, 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

the ends of strip steels are butt-jointed with each other in the longitudinal direction in order and are connected by welding, when such long strip steel raw material is used for continuously making a thin flux-cored wire, the burr generated due to the shearing of the steel plate and continuously existing at the end of the width direction of the strip steel along the whole longitudinal direction of the strip steel faces the upper part of the connecting strip steels, then the ends of strip steels are butt-jointed with each other in the longitudinal direction, and are connected by welding, no burr toward the outside of the thin flux-cored wire exists. By adopting the method, the circularity of the flux-cored wire can be ensured, in case of thin flux-cored wire, no bad influence on the supply of the extending-out welding wire in the welding construction for a welding machine is caused, and the supply is good.

Description

technical field [0001] The present invention relates to a method of manufacturing a flux-cored welding wire. Background technique [0002] Among arc welding wires for automatic or semi-automatic welding, flux-cored wire (also called flux cored wire, FEW) filled with flux in a tubular outer belt steel is widely used. In this FEW, hoops targeted by the present invention include a type having a seam (hereinafter also referred to as seam) and a seamless type without a seam. Since the latter seamless type is expensive to manufacture, FCW with seams is generally used. The seamed FCW is described later figure 2 As shown in FIG. 9( b ), it refers to a welding wire in a closed state without joining the seam by welding or the like. Hereinafter, this seamed flux-cored wire is simply referred to as a flux-cored wire or FCW. [0003] As a general manufacturing method of flux-cored welding wire, as shown in Fig. 9 (a) and (b) described later in detail, the following steps are continuo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/40B23K35/00
CPCB21C23/085B21C37/08B23K9/0282B23K35/0266B23K35/406
Inventor 池上彻
Owner KOBE STEEL LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com