Novel milling liquid for four-roll mill and preparation method thereof

A four-roll rolling mill and rolling fluid technology, applied in the petroleum industry, lubricating compositions, etc., can solve the problems of short fluid change cycle, impact on production, high comprehensive cost of emulsion, etc., and achieve the effect of saving electricity consumption

Active Publication Date: 2013-01-09
JIANGMEN RIYING STAINLESS STEEL MATERIALS MANUFACTORY
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Before the fully synthetic rolling fluid was used, the process lubricant used in the four-high rolling mill was usually an emulsion, but the surface quality after rolling was poor, and the temperature control equipment needed to be turned on and maintained at a temperature of 45-55 °C, and stirring was required. Prevent spoilage and rancidity
Another point is that the four-roll rolling mill uses the emulsion to change the liquid, the period is short, and it only takes 1 to 2 months to replace it all. Frequent liquid changes have an impact on production, and the overall cost of using the emulsion is high. Emulsion for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel milling liquid for four-roll mill and preparation method thereof
  • Novel milling liquid for four-roll mill and preparation method thereof
  • Novel milling liquid for four-roll mill and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] N,N-Diethylethanolamine 35%

[0045] Pentaerythritol 20%

[0046] Potassium Hydroxide 10%

[0047] Sulfurized Fatty Acid Soap 3%

[0048] A mixture of triethanolamine and borate in a 1:1 weight ratio 0.4%

[0049] Formaldehyde 1.0%

[0050] Triethanolamine Oleate 5%

[0051] Simethicone 0.4%

[0052] Put 35% of N,N-diethylethanolamine, 3% of sulfurized fatty acid soap, 20% of pentaerythritol, and 10% of potassium hydroxide in a reaction vessel, heat and stir at 70°C to dissolve, until the solution is evenly mixed , then add 0.4% of triethanolamine and borate mixture in a 1:1 weight ratio, 1.0% formaldehyde, 5% oleic acid triethanolamine, heat and stir to dissolve at 70°C, and wait until the solution is mixed After uniformity, add 0.4% simethicone oil to obtain the finished rolling solution.

Embodiment 2

[0054] N,N-Dimethylethanolamine 30%

[0055] Lauryl Alcohol 25%

[0056] Potassium Hydroxide 5%

[0057] Sulphurized Fatty Acid Soap 5%

[0058] A mixture of triethanolamine and borate in a 1:1 weight ratio 0.4%

[0059] Formaldehyde 1.8%

[0060] Triethanolamine Oleate 10%

[0061] Simethicone 0.3%

[0062] Put 30% of N,N-dimethylethanolamine, 5% of sulfurized fatty acid soap, 25% of lauryl alcohol, and 5% of potassium hydroxide in a reaction vessel, heat and stir at 75°C to dissolve until the solution is evenly mixed Finally, add 0.4% triethanolamine and borate in a 1:1 weight ratio mixture, 1.8% formaldehyde, 10% oleic acid triethanolamine, heat and stir to dissolve at 70°C, and wait for the solution After mixing evenly, add 0.3% simethicone oil to obtain the finished rolling liquid.

Embodiment 3

[0064] N-Methyl Glycolamine 35%

[0065] Pentaerythritol 20%

[0066] Sodium Hydroxide 8%

[0067] Sulfurized Fatty Acid Soap 8%

[0068] A mixture of triethanolamine and borate in a 1:1 weight ratio 0.3%

[0069] Formaldehyde 1.5%

[0070] Triethanolamine Oleate 9%

[0071] Simethicone 0.3%

[0072] Put 35% of N-methylglycolamine, 8% of sulfurized fatty acid soap, 20% of pentaerythritol, and 8% of sodium hydroxide in a reaction vessel and heat and stir at 75°C to dissolve. After the solution is evenly mixed, Then add 0.3% triethanolamine and borate mixture in a 1:1 weight ratio, 1.5% formaldehyde, 9% oleic acid triethanolamine, heat and stir to dissolve at 75°C, and wait for the solution to mix evenly Finally, add 0.3% simethicone oil to obtain the finished rolling solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel milling liquid for a four-roll mill and a preparation method thereof. The novel milling liquid for the four-roll mill at least comprises the following components by volume percent: 15 to 25% of polyols, 25% to 35% of trithylenetramine, 5% to 10% of inorganic alkali, 8% to 10% of additive and the balance of water. The novel milling liquid for the four-roll mill changes emulsion into completely synthesized liquid, has long service life which is 6 to 7 times longer than that of the emulsion; and the liquid can not easily generate degeneration, rancidity or bacteria and completely contains no emulsifier or mineral oil.

Description

technical field [0001] The invention relates to a rolling liquid for metal processing and a preparation method thereof, in particular to a novel four-high rolling mill rolling liquid and a preparation method thereof. Background technique [0002] Before the fully synthetic rolling fluid was used, the process lubricant used in the four-high rolling mill was usually an emulsion, but the surface quality after rolling was poor, and the temperature control equipment needed to be turned on and maintained at a temperature of 45-55 °C, and stirring was required. Inhibit deterioration and rancidity. Another point is that the four-roll rolling mill uses the emulsion to change the liquid, the period is short, and it only takes 1 to 2 months to replace it all. Frequent liquid changes have an impact on production, and the overall cost of using the emulsion is high. Emulsions are improved. Contents of the invention [0003] The purpose of the present invention is to overcome the defec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M173/02C10M177/00C10N40/24C10N30/16C10N30/12
Inventor 李耀如
Owner JIANGMEN RIYING STAINLESS STEEL MATERIALS MANUFACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com