Nano-silver anion tide solidifying matte floor board paint

A moisture-curing, nano-silver technology, used in the field of organic polymer material coatings, can solve problems such as inability to play and functional additives cannot be reasonably arranged, and achieve the effect of improving usability, system and formula optimization, and tough paint film.

Active Publication Date: 2011-01-19
GUANGDONG SANVO CHEM IND TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In addition, since the paint film of oil-based paint is mostly a continuous dense paint film, most of the functional additives cannot be reasonably arranged on the surface of the paint film, and the functional additives are buried in the paint film, and often cannot play their due role. the role of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-silver anion tide solidifying matte floor board paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment I

[0039] Component A: composed of moisture-cured polyurethane resin Taiwan Jiehua 6308-60;

[0040] Component B: According to the proportion by weight, put 71.7 parts of butyl acetate and 6 parts of Eastman CAB-531-1 into the dispersion tank, and disperse into Eastman CAB-531 at a speed of 600 rpm -1 Dissolve completely; Add 2 parts of EFKA-4010, 0.3 parts of BYK-141, 0.7 parts of Texogel MP100, 2 parts of Lubrizol 1400SF, 10 parts of Grace C906, and disperse for 25 minutes at a speed of 1500 rpm to fineness ≤30 microns; add 0.3 parts of BYK-323, 5 parts of Longnuo brand G series type II negative ion additive, 2 parts of nano-silver antibacterial additive AGS-MB3000, and disperse for 15 minutes at a speed of 600 rpm to make it component B;

[0041] When in use, the ratio of component A:component B=1:0.7 in parts by weight can be mixed evenly.

Embodiment II

[0043] Component A: composed of moisture-cured polyurethane resin Jiangmen Paint PJ6803-60;

[0044] Component B: Mix 71.6 parts of butyl acetate and 7 parts of Eastman CAB-553-0.4 in parts by weight: put them into the dispersion tank, and disperse them into Eastman CAB-553 at a speed of 700 rpm -0.4 is completely dissolved; add BYK-110 1.5 parts BYK-052 0.4 parts, Bentone SD-1 0.8 parts, Clariant 9615A 2 parts, Grace ED-2 8 parts, and disperse for 20 minutes at 1200 rpm. To a fineness of ≤25 microns; add 0.2 parts of tego-450, 6 parts of Tianshuang brand DMD698 negative ion additive, 2.5 parts of nano-silver antibacterial additive AGS-MB3000, and disperse for 20 minutes at a speed of 500 rpm. component B;

[0045]When in use, the ratio of component A:component B=1:0.5 in parts by weight can be mixed evenly.

Embodiment III

[0047] Component A: composed of moisture-cured polyurethane resin Taiwan Jiehua 6308-60;

[0048] Component B: put 69.0 parts of butyl acetate and 5 parts of Eastman CAB-531-1 into the dispersion tank according to the weight ratio, and disperse at the speed of 600 rpm until Eastman CAB-531-1 is completely Dissolve; add 1.5 parts of EFKA-4010, 0.4 parts of BYK-141, 0.7 parts of Bentone SD-1, 3 parts of Lubrizol 1400SF, 12 parts of Grace C906, and disperse for 30 minutes at a speed of 1300 rpm until fineness ≤25 microns; add 0.4 parts of BYK-323, 5 parts of Longnuo brand G series II negative ion additive, 3 parts of nano-silver antibacterial additive AGS-MB3000, and disperse for 20 minutes at a speed of 500 rpm to make it component B;

[0049] When in use, the ratio of component A:component B=1:0.6 in parts by weight can be mixed evenly.

[0050] Names of main raw materials, technical indicators

[0051] 1. Moisture curing polyurethane resin 6308-60

[0052] Manufacturer: Ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses nano-silver anion tide solidifying matte floor board paint, which is composed of component A and component B and is proportioned in parts by weight when in use as follows: component A: component B equals to 1:0.2-0.8, and then component A and component B are mixed evenly. Component A is tide solidifying polyurethane resin, component B is composed of butylacetate, celluloseacetate butyrate, dispersing agent, defoaming agent, anti-settling agent, handfeel wax powder, flatting powder, micropowder configuration leveling agent, anion additive and nano silver additive AGS-MB3000. The invention has the following advantages: 1. the product contains the component of nano silver antibacterial additive AGS-MB3000 and can effectively kill colon bacillus, staphylococcus aureus, grease moulds and the like; 2. the anions additive contained in the product can continuously release a large number of anions in an instant; 3. the functional effects of each additive can be fully brought into play through the optimization of the auxiliary agent; and 4. the applicability of the product can be improved through the optimization of the system and formula.

Description

technical field [0001] The invention relates to the field of organic polymer material coatings, in particular to nano-silver anion moisture-cured matte floor paint technical background [0002] With the rapid development of social economy and the continuous improvement of people's living standards. People's requirements for the home environment are getting higher and higher. For example, the floor has changed from the original cement board to ceramic tiles, and now the use of wooden floors is a good example. The use of wooden floors is inseparable from the coating of floor paint. The comprehensive performance requirements of floor paint are relatively high, and the coating film must be tough and wear-resistant. At present, tough and wear-resistant floor paints on the market are generally divided into two categories. One is light-cured UV floor paints. This kind of floor paint has better overall performance and a tougher and more wear-resistant coating film. However, this ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D101/14C09D7/12C09D5/14C09D5/00
Inventor 陈炳耀许耀魁
Owner GUANGDONG SANVO CHEM IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com