Aqueous one-component solar energy adsorption coating

A solar energy absorption, one-component technology, applied in the chemical industry, can solve the problems of large-scale application limitations, strict substrate requirements, high cost, etc., and achieve excellent adhesion, energy saving, and excellent moisture and heat resistance.

Active Publication Date: 2010-05-05
CHANGCHUN HUARI PAINT
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although CND, vacuum evaporation, radio frequency sputtering and other processes have been able to prepare light-emitting materials with good spectral selectivity, large-scale application is limited due to the disadvantages of complex process, high cost, and strict requirements on substrates.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 50 kg of acrylic resin modified polysiloxane emulsion, 25 kg of PbS, 20 kg of deionized water, and 8 kg of an alkylammonium salt solution of a polyfunctional polymer were respectively weighed as raw materials.

[0019] Acrylic resin modified polysiloxane emulsion, PbS or FeMnCuO 4 , deionized water, and the alkylammonium salt solution of the multifunctional polymer are stirred in the feeding tank, and the feeding interval is 10 minutes for each feeding in order, and the stirring is stopped after 30-40 minutes after all the feeding is completed.

[0020] After mixing fully, send the mixed paint liquid into the grinder and start grinding. When the fineness is 5 μm (measured by the fineness scraper), the paint liquid is introduced into the paint mixing tank.

[0021] Filter with 200 mesh silk cloth.

Embodiment 2

[0024] Take respectively the acrylic resin modified polysiloxane emulsion of raw material 60kg, the FeMnCuO of 20kg 4 , 30kg of deionized water, 10kg of alkylammonium salt solution of multifunctional polymer.

[0025] Production technology is with embodiment 1.

[0026] Application example: Take the above paint and test it according to the relevant national standards, the solar absorption rate a s is 0.9, the thermal emissivity ε is 0.4, a s / ε is 2.25.

Embodiment 3

[0028] Take respectively the acrylic resin modified polysiloxane emulsion of raw material 55kg, the FeMnCuO of 15kg 4 , 25kg of deionized water, 5kg of alkyl ammonium salt solution of multifunctional polymer.

[0029] Production technology is with embodiment 1.

[0030] Application example: Take the above paint and test it according to the relevant national standards, the solar absorption rate a s is 0.93, the thermal emissivity ε is 0.25, a s / ε is 3.72.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
solar absorptanceaaaaaaaaaa
solar absorptanceaaaaaaaaaa
solar absorptanceaaaaaaaaaa
Login to View More

Abstract

The invention relates to an aqueous one-component solar energy adsorption coating, in particular to an improvement of coating production technology; the raw materials and the proportioning range are that by weight ratio: 50-60 of acrylic resin modified polyorganosiloxane emulsion, 20-30 of deionized water, 20-25 of PbS or FeMnCuO4 and 5-10 of multi-functional-group polymeric alkyl ammonium salt solution; the aqueous one-component solar energy adsorption coating has the beneficial effects that: 1. the coating has the characteristics of noninflammability, no environment pollution and energy saving; 2. the coating has good adhesive force to bottom material, and has good shock resistance, bending resistance and humidity resistance; 3. the coating has good aging resistance and salt fog resistance; 4. the solar energy absorptivity of the coating is high.

Description

technical field [0001] The invention belongs to the technical field of chemical industry and relates to the improvement of a paint production technology. Background technique [0002] Solar energy is the most important source of energy on the earth, and it has many advantages that traditional energy sources cannot match. The total radiant energy from the sun to the ground is as high as 6×10 9 KW is equivalent to more than 50,000 times the total power generation in the world at present, and it is inexhaustible. It is also a kind of clean energy and does not pollute the environment. However, solar energy firstly has energy dispersion and low energy density per unit area; secondly, solar energy is greatly affected by day and night, seasons and climates, which makes the utilization of solar energy encounter various difficulties. [0003] The key to utilizing solar energy is to collect the sun's radiant energy to the maximum extent. From a technical and economic point of view,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D133/00C09D7/12C09D5/32
Inventor 陈冬冬贺浩然张大鹏
Owner CHANGCHUN HUARI PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com