Chinese red ceramic glaze and glaze technology thereof

A ceramic glaze and raw material technology, which is applied in the field of Chinese red ceramic glaze and its glazing process, can solve the problems of poor water absorption, poor fluidity, and low color of the glaze, and achieve good water absorption and fluidity , High gloss effect

Inactive Publication Date: 2011-06-08
临澧县杰海陶瓷有限责任公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the glaze in the ceramic industry has a single glaze color, low luster, poor water absorption effect and poor fluidity, and the Chinese red glaze with uniform and pure color is extremely difficult to develop.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Proportion of ingredients: Potassium feldspar 32, albite feldspar 23, Shuangfei powder 10, aluminum silicate 2, zinc oxide 4, dolomite 5, quartz 15, pottery red clay 9, golden red 4, peach red 6, cellulose 0.4, water Glass 0.3, sapropel 0.15, water 50.

[0014] Prepare the materials according to the ratio of the above-mentioned Chinese red ceramic glaze, put them into a ball mill, and ball mill for 17 hours, the fineness reaches 425 mesh, and then sieve and set aside;

[0015] Choose high-quality clay to make the green body, let it air-dry or bake dry naturally, take the prepared Chinese red ceramic glaze, dip or spray it on the green body, send the glazed green body into the kiln for 10 minutes, Sintered into ceramic products at a high temperature of 1250°C.

Embodiment 2

[0017] Proportion of ingredients: Potassium feldspar 27, albite 19, Shuangfei powder 8, aluminum silicate 1, zinc oxide 3, dolomite 4, quartz 12, pottery red clay 7, golden red 3, pink 5, cellulose 0.3, water Glass 0.2, sapropel 0.1, water 45.

[0018] Prepare the materials according to the ratio of the above-mentioned Chinese red ceramic glaze, put them into a ball mill, ball mill for 17 hours, and the fineness reaches 400 mesh, and sieve it for later use;

[0019] Choose high-quality pottery clay to make the green body, let it air-dry or bake dry naturally, take the prepared Chinese red ceramic glaze, dip or spray it on the green body, and send the glazed green body into the kiln for 9 minutes. Sintered into ceramic products at a high temperature of 1300 °C.

Embodiment 3

[0021] Proportion of ingredients: Potassium feldspar 37, albite 27, Shuangfei powder 12, aluminum silicate 3, zinc oxide 5, dolomite 6, quartz 18, pottery red clay 11, golden red 5, peach red 6, cellulose 0.5, water Glass 0.5, sapropel 0.2, water 60.

[0022] Prepare the materials according to the ratio of the above-mentioned Chinese red ceramic glaze, put them into a ball mill, ball mill for 17 hours, and the fineness reaches 450 mesh, and sieve it for later use;

[0023] Choose high-quality clay to make the green body, let it air-dry or bake dry naturally, take the prepared Chinese red ceramic glaze, dip or spray it on the green body, and send the glazed green body into the kiln for 14 minutes. Sintered into ceramic products at a high temperature of 1350 °C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to Chinese red ceramic glaze and a glaze technology thereof. The Chinese red ceramic glaze comprises the following raw materials by weight percent: 27-37 potassium feldspar, 19-27 albite, 8-12 coarse whiting, 1-3 aluminum silicate, 3-5 zinc oxide, 4-6 dolomite, 12-18 quartz, 7-11 red mud, 3-5 golden red, 5-6 peach red, 0.3-0.5 cellulose, 0.2-0.5 sodium metasilicate, 0.1-0.2 sodium humate and 45-60 water which are distributed, filled into a globe mill for ball milling, screened, glazed and sintered to obtain a finished product. The invention overcomes the defects of single glazing color, low color degree, poor water suction effect and poor fluidity of the ceramic glaze in the prior ceramic industry. The Chinese red ceramic glaze has even and pure glazing color, high color degree and good water suction effect and fluidity, and ceramic products made from the Chinese red ceramic glaze resist low temperature and high temperature, do not decolor and crack.

Description

technical field [0001] The invention relates to a ceramic glaze and a glazing process thereof, in particular to a Chinese red ceramic glaze and a glazing process thereof. Background technique [0002] With the progress of mankind, the rapid development of economy and society, the improvement of people's quality of life and the change of consumption concept, ceramic products are required to be practical, artistic and ornamental. [0003] At present, the glaze in the ceramic industry has a single glaze color, low luster, poor water absorption effect and poor fluidity of the glaze, and the Chinese red glaze with uniform and pure color is extremely difficult to develop. Contents of the invention [0004] In view of the deficiencies of the above-mentioned similar technologies, the object of the present invention is to provide a Chinese red ceramic glaze with pure color, high gloss and bright colors and its glazing process. [0005] The technical scheme of the present invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/04C04B41/86
Inventor 贺家湘
Owner 临澧县杰海陶瓷有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products