Jun porcelain composite antiseep glaze and preparation method thereof

A technology of anti-leakage and glaze, which is applied in the field of Jun porcelain composite anti-leakage glaze and its preparation, can solve the problems of serious environmental pollution, poor quality, and excessive materials, and achieve uniform color, high yield and glazed surface hypertrophic effect

Inactive Publication Date: 2018-02-16
禹州市华盛钧窑有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary daily-use porcelain products are of low grade and poor quality. At the same time, they consume a lot of energy, use a lot of materials, and cause serious environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: A kind of Jun porcelain composite anti-leakage glaze, which is prepared from the following raw materials in parts by weight:

[0013] 47 parts of yellow feldspar, 43 parts of quartz, 36 parts of porcelain stone, 7 parts of calcite, 6 parts of zinc oxide, and 3 parts of plant ash.

[0014] The preparation method of the Jun porcelain composite anti-leakage glaze comprises the following steps:

[0015] Step 1: (1) Coarsely crush the stone raw materials with a wheel mill; (2) Stack the soil materials in the open air and weather them through perennial wind, sun, rain, freezing, etc.; (3) Pre-burn the yellow feldspar for 10 hours to 20 hours;

[0016] Step 2: Put the well-proportioned glaze into the ball mill, add water with a total weight of 30-45% of the mixed raw materials, start the wet mill for 10-25 hours, and take out the glaze slurry from the ball mill after reaching the specified fineness;

[0017] Step 3: Sieve the wet-milled slurry through a 200-300...

Embodiment 2

[0018] Embodiment 2: A kind of Jun porcelain composite anti-leakage glaze, which is prepared from the following raw materials in parts by weight: 45 parts of feldspar, 40 parts of quartz, 30 parts of porcelain stone, 5 parts of calcite, and 5 parts of zinc oxide , 1 part of plant ash.

[0019] The preparation method of the Jun porcelain composite anti-leakage glaze comprises the following steps:

[0020] Step 1: (1) Coarsely crush the stone raw materials with a wheel mill; (2) Stack the soil materials in the open air and weather them through perennial wind, sun, rain, freezing, etc.; (3) Pre-burn the yellow feldspar for 10 hours to 20 hours;

[0021] Step 2: Put the well-proportioned glaze into the ball mill, add water with a total weight of 30-45% of the mixed raw materials, start the wet mill for 10-25 hours, and take out the glaze slurry from the ball mill after reaching the specified fineness;

[0022] Step 3: Sieve the wet-milled slurry through a 200-300-mesh sieve into...

Embodiment 3

[0023] Embodiment 3: A kind of Jun porcelain composite anti-leakage glaze, which is prepared from the following raw materials in parts by weight: 50 parts of feldspar, 45 parts of quartz, 40 parts of porcelain stone, 8 parts of calcite, and 7 parts of zinc oxide , 5 parts of plant ash.

[0024] The preparation method of the Jun porcelain composite anti-leakage glaze comprises the following steps:

[0025] Step 1: (1) Coarsely crush the stone raw materials with a wheel mill; (2) Stack the soil materials in the open air and weather them through perennial wind, sun, rain, freezing, etc.; (3) Pre-burn the yellow feldspar for 10 hours to 20 hours;

[0026] Step 2: Put the well-proportioned glaze into the ball mill, add water with a total weight of 30-45% of the mixed raw materials, start the wet mill for 10-25 hours, and take out the glaze slurry from the ball mill after reaching the specified fineness;

[0027] Step 3: Sieve the wet-milled slurry through a 200-300-mesh sieve int...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a jun porcelain composite antiseep glaze and a preparation method thereof. The jun porcelain composite antiseep glaze is prepared from the following raw materials in parts byweight: 45 to 50 parts of melilite, 40 to 45 parts of quartz, 30 to 40 parts of chinastone, 5 to 8 parts of calcite, 5 to 7 parts of zinc oxide, and 1 to 5 parts of plant ash. In the ingredients of the glaze, even though the adopted raw materials are common raw materials, the raw materials have a synergistic effect through reasonable raw material composition and quantity adjustment, a glaze layeris tight so as to be prevented from seeping, the glazing color is uniform and bright, the fluidity is moderate, and jun porcelain prepared by a glaze formula provided by the invention is uniform in color, good in glossiness, uniform in colour and lustre, thick in glaze surface, unique in artistic effect, mild and bright in impression, uniform in glaze hacking, and high in yield.

Description

technical field [0001] The invention relates to the field of Jun porcelain, in particular to a Jun porcelain composite anti-leakage glaze and a preparation method thereof. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family is rich, but it is not as good as a piece of Jun porcelain". With its simple shape, exquisite craftsmanship, complex glaze matching, the magical kiln transformation of "one color in the kiln, thousands of colors out of the kiln", lakes and mountains, clouds and mist, human beings, animals, flowers, birds, insects and fish, etc. Known as the first of China's "Five Famous Porcelains". [0003] The traditional technology uses coal to directly fire the kiln to produce ordinary daily-use porcelain. Ordinary daily-use porcelain ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/16C03C1/04C04B41/86
CPCC03C8/16C03C1/04C04B41/5022C04B41/86
Inventor 任合超
Owner 禹州市华盛钧窑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More