High-damping magnesium alloy containing quasicrystal reinforcing phase

A reinforcement phase and magnesium alloy technology, applied in the field of materials, can solve the problems of low strength, poor corrosion resistance, poor strength and corrosion resistance, etc.

Inactive Publication Date: 2012-05-30
NORTHWESTERN POLYTECHNICAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Among many metals, pure magnesium has the best damping performance, but due to its poor strength and corrosion resistance, it cannot be used as a structural material
At present, there are only a few common binary high-damping alloys such as magnesium-zirconium and magnesium-nickel, but they still have disadvantages such as low strength and poor corrosion resistance during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] In this embodiment, a magnesium-zinc-yttrium-zirconium quaternary magnesium alloy containing 0.90% by weight of zinc, 0.15% by weight of yttrium and 0.6% by weight of zirconium is used as an alloy element to prepare a high damping magnesium alloy. Zinc is added by industrial pure zinc, alloy elements yttrium and zirconium are added by master alloy, and the composition of master alloy is magnesium-30% yttrium and magnesium-30% zirconium.

[0016] When preparing:

[0017] The first step is to preheat the crucible to 250°C and paint;

[0018] In the second step, the crucible is heated to 300°C, pure magnesium is added to the crucible and the protective gas is started;

[0019] In the third step, when magnesium is completely melted, add magnesium-yttrium, magnesium-zirconium master alloy and pure zinc at 700°C;

[0020] The fourth step is to continue to heat up to 720 ° C, keep warm and stir to fully melt the master alloy and zinc;

[0021] The fifth step is to carry out...

Embodiment 2

[0025] In this embodiment, a magnesium-zinc-yttrium-zirconium quaternary magnesium alloy containing 1.0% by weight of zinc, 0.2% by weight of yttrium, and 0.6% by weight of zirconium is used as an alloy element to prepare a high-strength, high-damping, corrosion-resistant New magnesium alloy. Zinc is added by industrial pure zinc, alloy elements yttrium and zirconium are added by master alloy, and the composition of master alloy is magnesium-30% yttrium and magnesium-30% zirconium.

[0026] When preparing:

[0027] The first step is to preheat the crucible to 250°C and paint;

[0028] In the second step, the crucible is heated to 300°C, pure magnesium is added to the crucible and the protective gas is started;

[0029] In the third step, when magnesium is completely melted, add magnesium-yttrium, magnesium-zirconium master alloy and pure zinc at 710°C;

[0030] The fourth step is to continue to heat up to 720 ° C, keep warm and stir to fully melt the master alloy and zinc; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-damping magnesium alloy containing quasicrystal reinforcing phase and a preparation method thereof. The alloy is a magnesium zinc yttrium zirconium quaternary magnesium alloy which comprises 0.90 wt% of zinc, 0.15 wt% of yttrium and 0.6 wt% of zirconium. The added zinc adopts the technical pure zinc. The added alloy elements yttrium and zirconium adopt an intermediate alloy which comprises 30% of magnesium, 30% of yttrium and magnesium and zirconium. The high-damping magnesium alloy containing the quasicrystal reinforcing phase is prepared by preheating, smelting and moulding. The invention takes the zinc, yttrium and zirconium as alloy elements, forms icosahedral quasicrystal which has special crystal structure by controlling the atom content of zinc and yttrium in the alloy, so that the interface combination is stable, thus the slippage of dislocation and the expansion of the twin crystal are prevented. The high-damping magnesium alloy of the invention plays good strengthening function, effectively overcomes the contradictoriness between the strength and the damping performance in the magnesium base high-damping structure material, has favourable anti-corrosion performance and is a magnesium alloy with comprehensive performance.

Description

1. Technical field: [0001] The invention relates to the field of materials, in particular to a high-damping magnesium alloy containing a quasi-crystal reinforcement phase and a preparation method thereof. 2. Background technology: [0002] Vibration and noise are one of the important public hazards that accompany the rapid development of modern industry. Over the years, various fields of modern industry have been adopting various means to control the harm caused by vibration and noise, and damping and vibration reduction technology has emerged as the times require. There are three main methods of damping, that is, system damping, structural damping and material damping. Material damping relies on the high damping characteristics of the material itself to achieve the purpose of vibration reduction. Using the material's own damping can reduce design costs and make the system lighter. Therefore, the development of new low-density, high-strength and high-damping structural ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/04C22C1/03C22C1/06B22D21/04
Inventor 王锦程万迪庆杨根仓杨长林
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com