Preparation method of under-glaze red pottery tableware

Abstract

The present invention provides a preparation method of under-glaze red pottery tableware, including following steps: (1) select materials; (2) producing red ceramic clay; (3) biscuit firing, baking inoxidizing atmosphere with temperature of 950-1000 DEG, time 7.5-8 hours, heat insulation 7-8 hours; (5) cladding glaze, surface decoration processing; (6) baking color and drying in kiln, with a temperature of 740-760 DEG, time 3-4 hours, heat insulation 9-10 hours; (7) cladding transparent glaze, glaze firing with a temperature of 1050-1100 DEG, time 9-10 hours, heat insulation 11-12 hours; (8)checkout, packaging, warehousing. Applying the present invention, the red pottery tableware is provided with advantages of light weight, low baking temperature, low energy consumption, products easilyweathering when breakage, reducing pollution to ecologic environment; and thermal stability of products is preferable, better preservation, high manufacturing yield; employing under-glaze decorationart, bright in color, fastness, elegant quality, conforming to life requirement of modern people.

Description

technical field [0001] The invention relates to a preparation method of daily tableware, in particular to a preparation method of underglaze red pottery tableware. Background technique [0002] Daily tableware is mainly made of ceramics, mainly including reinforced porcelain, high white porcelain, bone china, beautiful quality porcelain and other ceramic products. Although these ceramic products have good strengthening performance, impact resistance and high temperature resistance, their disadvantage is the firing temperature. High, high energy consumption, heavy weight, general freshness preservation and health care performance, and the product cannot be weathered and degraded after being fired at high temperature, and it is easy to cause environmental pollution when discarded after use, especially the waste and defective products generated in the production process form ceramic waste, which is even more Pollution and harm to the ecological environment. Although the terrac...

AI Technical Summary

Problems solved by technology

[0002] Daily tableware is mainly made of ceramics, mainly including reinforced porcelain, high white porcelain, bone china, beautiful quality porcelain and other ceramic products. Although these ceramic products have good strengthening performance, impact resistance and high temperature resistance, their disadvantage is the firing temperature. High, high energy consumption, heavy weight, general freshness preservation and health care performance, and the product cannot be weathered and degraded after being fired at high temperature, and it is easy to cause environmental pollution when discarded after use, especially the waste and defective products generated in the production process form ceramic waste, which is even more Pollution and harm to the ecological environment

Although the terracotta products produced with laterite porcelain clay have light weight, low firing temperature, low energy consumption, and easy weathering after product damage, they are only used in tea sets and handicrafts because of their brittle texture. Applied to daily tableware, the application field is limited