Method for manufacturing uranolite glass

A production method and glass technology, applied in the field of art glass, can solve the problems of low closeness between glass paint and glass structure, inconspicuous refraction, low brightness, etc., so as to achieve tight structure between meteorite paint and glass, good refraction effect, and high brightness. high brightness effect

Inactive Publication Date: 2009-05-13
ZHANGJIAJIE YONGXING GLASS
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing meteorite glass is limited by the production process, the closeness between the glass paint and the glass structure is not high, the meteorite layer is easy to fall off, and the brightness is not high, the refraction is not obvious, and its brightness gradually decreases with time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The present invention will be described in detail below in conjunction with the examples. The specific method is:

[0012] (1) Cut the glass into the required shape, wash with water or alcohol, sprinkle with double fly powder, rub back and forth with a cotton cloth for 1-2 minutes to remove the double fly powder, and knead the ultra-thin film the same size as the glass into texture Shape, the film used is PET film;

[0013] (2) Coat the prepared meteorite glass paint evenly on the glass surface, and spread the textured PET film on the surface of the glass meteorite paint, so that the meteorite paint flows with the texture lines on the PET film and solidifies naturally. Dry for 8-10 hours at 28~30℃, and remove the PET film; the glass meteorite paint is made by Guangdong Jiangmen Pule Chemical Co., Ltd., and the quality of the meteorite paint A and B The ratio is 2:1;

[0014] (3) Spray 2 to 3 times of glass brightener evenly on the surface of the meteorite paint that has for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for manufacturing meteorite glass. The meteorite glass is manufactured by the following steps: prepared glass meteorite paint is evenly coated on the surface of glass, a PET film which is kneaded into a texture shape is paved on the surface of the glass meteorite paint to ensure that the glass meteorite paint flows with the texture on the PET film, 2 to 3 times of glass brighteners are evenly sprayed on the surface of the meteorite paint which forms the texture shape after natural solidification and drying, then a pearl powder solution is sprayed, the glass meteorite paint is baked for 2 hours in a baking oven with a temperature of between 60 and 70 DEG C, and finally a colorless varnish is sprayed for bottom sealing. The method adopts a process different from that of the prior meteorite glass, particularly the different preparation of the pearl powder solution and the more reasonable control of the baking time, thereby ensuring that the meteorite paint and a glass structure are closer, the brightness of the surface is higher, the refraction effect is good, a meteorite paint layer can not fall off after being placed for a long time, and the brightness and the refraction effect can also not be changed.

Description

Technical field [0001] The invention relates to the field of artistic glass, and specifically provides a method for making meteorite glass. Background technique [0002] Meteorite glass is a kind of artistic glass that has appeared in recent years. It is named after its surface is similar to natural glass meteorite. It is made by lacquering meteorite glass to show texture and striated structure on the glass surface. Due to the limitation of the production process, the tightness of the glass paint and the glass structure of the existing meteorite glass is not high, the meteorite layer is easy to fall off, and the brightness is not high, the refraction is not obvious, and its brightness gradually decreases with time. Summary of the invention [0003] The purpose of the present invention is to provide a manufacturing process of meteorite glass, the meteorite layer and the glass structure are close, the brightness is high, and the refraction effect is good. [0004] In order to achi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C23/00
Inventor 屈国聪
Owner ZHANGJIAJIE YONGXING GLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products