Acroleic acid polymerization solution and preparation thereof
A technology of acrylic polymerization and acrylate, applied in the direction of coating, etc., can solve the problems of low wear resistance, dull color, easy decolorization, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Embodiment 1: according to the formula, the weight is 10% of acrylate polymer, 2.5% of ethanolamine and 27% of water to form the first component; 28% of butyl acrylate, 8% of styrene, 2.26% of dimethyl ester, emulsifier 5% and 12% of water make up the second component; 0.24% of initiator and 5% of water make up the third component.
[0017] The preparation process of the above-mentioned acrylic acid polymerization solution is as follows: the first step, mixing the materials of the above-mentioned first component evenly; the second step, mixing the materials of the above-mentioned second component and heating to 80°C; the third step, adding In the second component mixture, add 1 / 5 unit weight of the first component mixture and 1 / 3 unit weight of the third combination mixture, and react at a constant temperature of 80 ° C for 45 minutes; the fourth step . Fill in the remaining first component mixture and the remaining third combined mixture at a uniform speed within 2 hou...
Embodiment 2
[0058] Embodiment 2: According to the formula, the weight is 12% of acrylate polymer, 2% of ethanolamine and 28% of water to form the first component; 23% of butyl acrylate, 8.7% of styrene, 3% of dimethyl ester, emulsifier 6% and 12% of water make up the second component; 0.3% of initiator and 5% of water make up the third component.
[0059]The preparation process of the above-mentioned acrylic acid polymerization solution is as follows: the first step, mixing the materials of the above-mentioned first component evenly; the second step, mixing the materials of the above-mentioned second component and heating to 80°C; the third step, adding In the second component mixture, add 1 / 5 unit weight of the first component mixture and 1 / 3 unit weight of the third combination mixture, and react at a constant temperature of 80 ° C for 45 minutes; the fourth step . Fill in the remaining first component mixture and the remaining third combined mixture at a uniform speed within 2 hours. A...
Embodiment 3
[0061] Embodiment 3: take by weight according to formula and be that acrylate polymer 8%, ethanolamine 3% and water 26% form the first component; Get butyl acrylate 29%, styrene 8.6%, dimethyl ester 2.5%, emulsifier 5.5% and 12% of water make up the second component; 0.4% of initiator and 5% of water make up the third component.
[0062] The preparation process of the above-mentioned acrylic acid polymerization solution is as follows: the first step, mixing the materials of the above-mentioned first component evenly; the second step, mixing the materials of the above-mentioned second component and heating to 80°C; the third step, adding In the second component mixture, add 1 / 5 unit weight of the first component mixture and 1 / 3 unit weight of the third combination mixture, and react at a constant temperature of 80 ° C for 45 minutes; the fourth step . Fill in the remaining first component mixture and the remaining third combined mixture at a uniform speed within 2 hours. After ...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com