Hard paint film

A hard coating film and hard coating technology, which is applied in the field of film materials, can solve the problems of unstable formulation and surfactant precipitation, etc., to prevent cracking or curling, inhibit adhesion, and maintain scratch resistance and wear resistance Effect

Inactive Publication Date: 2008-06-25
BAODING LUCKY POLYMER MATERIAL TECH DEV +1
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although adding surfactant can solve the problem of coating ills, adding too much will cause problems such as surfactant precipitation
More importantly, due to different construction techniques, not paying attention to the choice of diluent will cause the instability of the formula

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] 5 parts of 1,6-hexanediol acrylate,

[0043] 15 parts of dipentaerythritol hexa(meth)acrylate,

[0044] Acrylic resin Soluryl-70 5 parts,

[0045] Irgacure184 5 parts,

[0046] Silicone CN9800 5 parts,

[0047] 15 parts of butyl acetate.

[0048] Add 5 parts of thermoplastic acrylic resin Soluryl-70 (Korean Hanwha Company) to 5 parts of 1,6-hexanediol acrylate (Sartomer), 15 parts of dipentaerythritol hexa(meth)acrylate (Sartomer) company) and 5 parts of Irgacure 184 (Ciba) and 5 parts of organic silicon CN9800 (Sartomer) were stirred and mixed, and then 15 parts of butyl acetate were added and stirred to obtain a hard coating agent coating solution.

[0049] The hard coat agent was applied to one surface of a polyethylene terephthalate film having a thickness of 150 µm with a wire bar, and then butyl acetate was evaporated to form a hard coat layer. Then, it was cured by ultraviolet irradiation of a high-pressure mercury lamp (120w / cm) to obtain a hard coating fil...

Embodiment 2

[0051] Polyurethane acrylate 6145-100 15 parts,

[0052] 5 parts of 1,6-hexanediol acrylate,

[0053] 10 parts of trimethylolpropane triacrylate,

[0054] Acrylic resin A-01 2 parts,

[0055] Irgacure 907 2 servings,

[0056] Silicone Rad2700 0.2 parts,

[0057] 5 parts of butyl acetate,

[0058] 5 parts of methyl ethyl ketone.

[0059] Add 2 parts of thermoplastic acrylic resin A-01 (Tricyclic Resin Company) to urethane acrylate 6145-100 containing 15 parts (Changxing Company), 5 parts of 1,6-hexanediol acrylate (Changxing Company), 10 parts Trimethylolpropane triacrylate (Changxing Company) and 2 parts of Irgacure 907 (Ciba Company) and 0.2 parts of acrylic modified reactive silicone Rad2700 (DEGO Company) are stirred and mixed, and then 5 parts of butyl acetate are added Ester and 5 parts of methyl ethyl ketone, stir to obtain the hard coating agent to coat and repair the cloth liquid.

[0060] Using method is the same as Example 1, and the results are shown in Table...

Embodiment 3

[0062] Polyester acrylate CN2203 10 parts,

[0063] Polyurethane acrylate CN9010 40 parts,

[0064] 20 parts of neopentyl glycol di(meth)acrylate,

[0065] Acrylic resin Soluryl-70 10 parts,

[0066] Irgacure 1173 8 parts,

[0067] Silicone CN9800 15 parts,

[0068] 30 parts of diisobutyl ketone,

[0069] 30 parts of butyl acetate.

[0070] 10 parts of thermoplastic acrylic resin Soluryl-70 (Korean Hanwha Company) are added to 10 parts of polyester acrylate CN2203 (Sartomer Company), 40 parts of polyurethane acrylate CN9010 (Sartomer Company), 20 parts of bis(methyl) ) neopentyl glycol acrylate (Sartomer Company) and 8 parts of UV curing initiator Irgacure 1173 (Ciba Company) and 15 parts of acrylic acid modified reactive silicone CN9800 (Sartomer Company) in the solution of stirring After mixing, 30 parts of diisobutyl ketone and 30 parts of butyl acetate were added and stirred to obtain a hard coating agent coating liquid.

[0071] Using method is the same as Example ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hard coating film to solve the problem of film cracking or curling. The technical proposal is that: the hard coating film comprises a support body and a hard coating; the hard coating has the compositions and weight portions as follows: 20 to 90 portions of UV curing acrylate, 2 to 20 portions of thermoplastic resin, 2 to 15 portions of photoinitiator, 0.2 to 15 portions of silicone, and 10 to 90 portions of solvent. The invention can inhibit cracking or curling caused by curing shrinkage, prohibit fingerprints or dusts, etc. from attaching on the surface of the film where attached fingerprints and dusts can be easily wiped off, and maintain the scratch resistance and wear resistance of the hard coating film.

Description

technical field [0001] The invention relates to a film material, in particular to a hard coating film. Background technique [0002] In recent years, the application of plastic products has become more and more extensive. Since the surface of most plastic products is easily scratched, in order to impart scratch resistance, it is necessary to stick a hard coat film or apply a protective paint layer before use. In addition, even for existing glass products, plastic films are increasingly attached to prevent scattering, but since the surface hardness of the film is insufficient, work to form a hard coat on the surface is widely carried out. [0003] The hard coat film is usually obtained by forming a thin coating film of about 2 to 10 μm on a transparent plastic film substrate using a thermosetting resin, an ultraviolet curable resin, or other composite materials. As a method of increasing the hardness of the hard coat layer, it is possible to increase the layer thickness of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/06C09D133/04C09D167/00C09D161/00C09D183/07
Inventor 李卫平刘瀛梁笑丛
Owner BAODING LUCKY POLYMER MATERIAL TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com