Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Process for preparing hyaluronic acid-chitosan crosslinked biocompatible materials

A technology of chitosan cross-linking and hyaluronic acid, applied in the field of biochemistry, can solve the problems of non-biocompatibility, single function, and no multiple biological functions, and achieve the effect of expanding application fields and high biological stability

Inactive Publication Date: 2008-04-30
JIANGNAN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the derivatives of hyaluronic acid cross-linked by this method have a single function and do not have multiple biological functions, especially such biological materials are not completely biocompatible

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing hyaluronic acid-chitosan crosslinked biocompatible materials
  • Process for preparing hyaluronic acid-chitosan crosslinked biocompatible materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 0.2g (0.5mM) hyaluronic acid and 0.2g (1.25mM) chitosan were respectively dissolved in 20ml 0.1M HCl solution and stirred overnight. Add NaCl solid to the dissolved hyaluronic acid hydrochloric acid solution, so that the final concentration of NaCl in the solution is 2M, stir well to dissolve. Weigh 0.0956g (0.5mM) EDC and 0.0575g (0.5mM) NHS, dissolve them in 5ml ultrapure water, then pour into the hyaluronic acid hydrochloric acid solution, and stir for 30min. Then inject the chitosan hydrochloric acid solution into the hyaluronic acid hydrochloric acid solution, and constantly and fully stir. When the solution is stable and uniform, slowly add liquid N,N,N',N'-tetramethylethylenediamine to the mixed solution to adjust the pH to 5.0. Stir at room temperature for 12h. The stirred product was loaded into a dialysis bag with a molecular weight cut-off of 14,000, dialyzed in 1M NaCl solution for 2 days, and then dialyzed in ultrapure water for one day. The dialysis pro...

Embodiment 2

[0021] 0.1 g of hyaluronic acid and 0.2 g of chitosan were dissolved in 20 ml of 0.1 M HCl solution and stirred overnight. Add NaCl solid to the dissolved hyaluronic acid hydrochloric acid solution, so that the final concentration of NaCl in the solution is 2M, stir well to dissolve. Weigh 0.0478g EDC and 0.0288g NHS, dissolve them in 5ml ultrapure water, then pour into the hyaluronic acid hydrochloric acid solution, and stir for 30min. Then inject the chitosan hydrochloric acid solution into the hyaluronic acid hydrochloric acid solution, and constantly and fully stir. When the solution is stable and uniform, slowly add liquid N,N,N',N'-tetramethylethylenediamine to the mixed solution to adjust the pH to 4.5. Stir at room temperature for 9h. The stirred product was loaded into a dialysis bag with a molecular weight cut-off of 14,000, dialyzed in 1M NaCl solution for 2 days, and then dialyzed in ultrapure water for one day. The dialysis product was freeze-dried to obtain a ...

Embodiment 3

[0023] 0.2 g of hyaluronic acid and 0.1 g of chitosan were dissolved in 20 ml of 0.1 M HCl solution, and stirred overnight. Add NaCl solid to the dissolved hyaluronic acid hydrochloric acid solution, so that the final concentration of NaCl in the solution is 2M, stir well to dissolve. Weigh 0.0956g EDC and 0.0575g NHS, dissolve them in 5ml ultrapure water, then pour into the hyaluronic acid hydrochloric acid solution, and stir for 30min. Add liquid N,N,N',N'-tetramethylethylenediamine to the two polysaccharide solutions respectively to adjust the pH to 4.0. Then the chitosan hydrochloric acid solution was injected into the hyaluronic acid hydrochloric acid solution and stirred at room temperature for 6 h. The stirred product was loaded into a dialysis bag with a molecular weight cut-off of 14000, dialyzed in 1M NaCl solution for 2 days, and then dialyzed in ultrapure water for 1 day. The dialysis product was freeze-dried to obtain a mesh material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for preparation of hyaluronic acid -chitose cross compatible material belongs to the biochemical technical sphere. The invention selects water-soluble carbodiimide as cross linker and N-hydroxy succinimide as active agent, adjusts PH value with N,N,N',N'-tetramethylethylenediamine, then makes the hyaluronic acid and the chitose perform cross-linking reaction, finally prepares the hyaluronic acid -chitose cross compatible material by dialysis and cryodesiccation. The material has a good application prospect in domains of drug embedment, tissue pack, film material and so on.

Description

technical field [0001] The invention discloses a preparation method of a hyaluronic acid-chitosan cross-linked biocompatible material, which belongs to the technical field of biochemistry. Background technique [0002] Both hyaluronic acid and chitosan are polysaccharides with excellent biocompatibility, and they have special biochemical effects in living organisms. For example, hyaluronic acid can be used as a joint lubricant and a wound healing agent; chitosan also has an antibacterial effect as a wound healing agent. The above two polysaccharides can also be applied in the fields of drug carriers and tissue fillers. [0003] Since all organisms contain hyaluronidase, ordinary hyaluronic acid is extremely easy to decompose in the organism. For this reason, scholars at home and abroad have proposed chemical modification methods to improve the anti-degradation performance of hyaluronic acid. Most of them choose the method of cross-linking small molecular chemical substanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L5/08C08J3/24C08K5/20A61K47/36
Inventor 陈坚邓禹刘龙堵国成李秀芬刘登如
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com