Hemostatic material of new type pore-borne molecular sieve and preparation method

A technology of mesoporous molecular sieves and hemostatic materials, which is applied in the field of mesoporous molecular sieve hemostatic materials and its preparation, and achieves the effects of cheap and easy-to-obtain raw materials, mild reaction conditions, and simple and easy operation

Inactive Publication Date: 2007-10-31
FUDAN UNIV
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there are no domestic and foreign patent literature reports on the application of mesoporous materials in blood coagulation materials, wound treatment and trauma repair, and the combination of mesoporous materials with medical bandages and medical adhesives in different forms for trauma repair

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hemostatic material of new type pore-borne molecular sieve and preparation method
  • Hemostatic material of new type pore-borne molecular sieve and preparation method
  • Hemostatic material of new type pore-borne molecular sieve and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 2.08g (10mmol) TEOS was dissolved in 10g ethanol, 0.5g water and 0.4g 0.1M HCl were added to the solution, stirred at room temperature for 1 hour, mixed evenly and then mixed with 0.9g triblock copolymer surfactant P123 (EO 20 PO 70 EO 20 ), stirred at room temperature for 1 hour and mixed with ethanol solution. Transfer the above-mentioned clear solution to a large petri dish, and remove the solution ethanol by natural volatilization (complete drying, generally takes 1 day), and a colorless, transparent and soft thick film is obtained. After the film was separated from the bottom of the petri dish, put it into a 100ml polytetrafluoroethylene bottle, add about 70ml of water, and conduct a hydrothermal treatment in an oven at 100°C for 72 hours. A white opaque thick film was obtained, separated by suction filtration, dried at room temperature and calcined at 500°C for 6 hours to remove the surfactant, and a two-dimensional hexagonal phase (p6mm structure) pure silica ...

Embodiment 2

[0039] 0.40g EO at room temperature 39 BO 47 EO 39 (B50-6600) was dissolved in 30g of 0.5mol / L HCl solution, and 2.08g of TEOS was added to the resulting clear solution. The molar ratio of each reactant was TEOS / EO 39 BO 47 EO 39 / HCl / H 2 O=1:0.0074:6:166. After the reactant was stirred at room temperature for one day, it was hydrothermally heated at 100° C. for one day. The resulting white precipitate was filtered, washed three times with deionized water, and dried at room temperature. Baking at 550° C. in an air atmosphere for 6 hours to remove the template agent, the heating rate was controlled at 2° C. / min, and finally a three-dimensional cubic phase (Im3m structure) pure silica mesoporous molecular sieve powder material was obtained. Its coagulation effect is good.

Embodiment 3

[0041] 4.0g nonionic surfactant EO 20 PO 70 EO 20 (P123), 1.4g calcium nitrate (Ca(NO 3 ) 4 4H 2 O), 6.7g tetraethyl orthosilicate (TEOS) was dissolved in 60g ethanol, then added 1.0g 0.5M hydrochloric acid solution, stirred at room temperature for 24h, poured into a petri dish, and aged for about 72h to make the hydrolysis-polycondensation reaction fully Proceed to form a gel and place the gel in a desiccator. The gel block obtained after drying is calcined at 700° C. for 5 hours in a muffle furnace to obtain a two-dimensional hexagonal phase (p6mm structure) silicon oxide mesoporous molecular sieve material containing calcium oxide. Its coagulation effect is good.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

A styptic mesoporous molecular sieve material is synthesized by sol-gel method where the self-assembling property and template action of surfactant are used. Its advantages are regulatable and uniform nano-pores, high specific surface area and pore volume, and regulatable component chosen from SiO2, calcium oxide, aluminium oxide, etc. Its preparing process is also disclosed.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, and specifically relates to a class of mesoporous molecular sieve hemostatic materials with different mesoscopic structures, compositions, shapes, etc. and a preparation method thereof. technical background [0002] In 1992, researchers from Mobil Corporation successfully synthesized the world's first M41S series silica (aluminum)-based ordered mesoporous molecular sieve material with uniform and adjustable pore size and large specific surface area by using the self-assembly and template function of surfactants. Mesoporous silica materials represented by MCM-41 and SBA-15 have aroused widespread interest, and research on mesoporous materials continues to deepen and expand. Because mesoporous materials have high surface area and pore volume, uniform and adjustable pore size, highly ordered and easily adjustable mesoporous structure (such as pore size, dimension, channel connection mod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L15/18A61L15/42C01B37/00
Inventor 余承忠严晓霞赵东元
Owner FUDAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com