Prepn process of nanometer tin dioxide rod

A technology of tin dioxide and nanorods, applied in tin oxide, nanostructure manufacturing, nanotechnology, etc., can solve problems such as complex process and long production cycle

Inactive Publication Date: 2007-01-03
EAST CHINA UNIV OF SCI & TECH
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the synthesis methods of tin dioxide nanorods include redox method, microemulsion method, template method, etc., but there are problems such as complicated process and long production cycle.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prepn process of nanometer tin dioxide rod
  • Prepn process of nanometer tin dioxide rod
  • Prepn process of nanometer tin dioxide rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Evaporate tin tetrachloride (3ml / min) at 250°C, hydrogen (1.0m 3 / h) and air preheated to 100°C (3m 3 / h) is passed into the central pipe 301 of the multi-jet combustion reactor after mixing, and the air (1m 3 / h) and hydrogen (1m 3 / h) of the mixed gas, the three-loop pipe is fed with air at a temperature of 25°C (2m 3 / h), carry out the gas phase combustion hydrolysis reaction in the combustion reaction chamber, the flame temperature in the combustion chamber is 800 ° C, the substrate is 3 cm away from the burner outlet, the deposition time is 10 min, and the tail gas is absorbed by the absorption device. The tin dioxide nanorods produced by the reaction have a diameter of 20 nm and an aspect ratio of 9. SEM photo see figure 2 .

Embodiment 2

[0027] Evaporate tin tetrachloride (5ml / min) at 300°C and mix with hydrogen (2.0m 3 / h) and air preheated to 50°C (4m 3 / h) is passed into the center pipe 301 of the multi-jet combustion reactor after mixing, and at the second ring pipe 302, the air (2m 3 / h) and hydrogen (3m 3 / h) mixed gas, the three-ring pipe 303 is fed with air at a temperature of 30°C (10m 3 / h), carry out the gas phase combustion hydrolysis reaction in the combustion reaction chamber, the flame temperature in the combustion chamber is 1500°C, the substrate is 20cm away from the burner outlet, the deposition time is 60min, and the tail gas is absorbed by the absorption device. The tin dioxide nanorods produced by the reaction have a diameter of 50 nm and an aspect ratio of 5. SEM photo see image 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The preparation process of nanometer tin dioxide rod includes the following steps: mixing tin tetrachloride gas with hydrogen and air, introducing the mixture through the central tube of the three-channel jet in the top of the combusting reactor into the combusting reactor, feeding gas mixture of hydrogen and air through the middle ring tube of the three-channel jet into the combusting reactor, feeding air through the out ring tube of the three-channel jet into the combusting reactor, setting inert base board in the outlet of the burning jet, and depositing the produced nanometer tin dioxide rod on the inert base board. The said preparation process is one simple and effective process for preparing nanometer tin dioxide rod.

Description

technical field [0001] The invention relates to a preparation method of tin dioxide nanorods. Background technique [0002] The study of one-dimensional or quasi-one-dimensional nanostructure systems or nanomaterials is one of the most important research frontiers in materials science at home and abroad in recent years. This type of material is not only of great significance for understanding the influence of the dimension and particle size of the material on the physical and chemical properties of the material, but also this type of material is not only the basis for the study of other low-dimensional materials, but also closely related to nanoelectronic devices and micro sensors. , has broad application prospects in the fields of chemistry, physics, electronics, optics and biomedicine. One-dimensional nanomaterials include nanotubes, nanorods, metal and semiconductor nanowires, coaxial nanocables, nanoribbons, etc. [0003] Tin dioxide is a classic semiconductor material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G19/02B82B3/00
Inventor 李春忠胡彦杰顾锋姜海波
Owner EAST CHINA UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com