Electronic media material on high power stainless steel plate and its preparation method

An electronic medium, stainless steel plate technology, applied in the direction of heating element materials, etc., can solve the problems of high price and low production efficiency, and achieve the effect of large daily production, cost saving, and large-scale production.

Inactive Publication Date: 2006-11-29
TAIYANG ELECTRONICS DONGGUAN
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Due to the above requirements, many electronic pastes are basically unable to meet them. Although DuPont and other companies have also developed some electronic dielectric pastes to match stainless steel plates, they are expensive and require multiple printings. Adding organic binders and low production efficiency make people discouraged

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Below in conjunction with specific embodiment the present invention is described in further detail:

[0035] Electronic dielectric materials on high-power stainless steel plates, which are mainly made of glass-ceramic powder by high-temperature sintering and melting of non-metal oxides, and then added with water to make it into a slurry. The ratio of glass-ceramic powder to water is (50-90) : (50~10), the electronic dielectric material is composed of glass ceramics, wherein the non-metallic oxide includes the following components by weight percentage:

[0036] SiO2: 20-80%, Al2O3: 0.5-20%,

[0037] Cr2O3: 0.5-8%, CaO: 10-50%,

[0038] TiO2: 0.5-15%, ZrO2: 10-30%,

[0039] ZnO: 1~10%, Na2O: 1~5%,

[0040] K2O: 1-10%, MgO: 0.1-10%.

[0041] The above non-metal oxides are smelted in proportion to obtain glass-ceramic powder, and then water is added to the glass-ceramic powder to obtain electronic dielectric material.

[0042] The preparation method of the electronic d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a high-power electronic medium material on the stainless steel plate with superior insulating properties and good printing characteristics and a method for manufacture, which does not need to be printed and sintered in many times. The first step is to prepare the electronic media materials, match the non-metallic materials according to weight percentage, mix them then to sinter the mixed materials to microcrystal glass powder, then add raw materials and water in the glass powder to get a slurry electronic medium to be sprayed on the stainless steel to be sintered to become an insulated medium layer.

Description

technical field [0001] The invention relates to a dielectric material for a stainless steel plate of a heating element, in particular to an electronic dielectric material on a high-power stainless steel plate and a preparation method thereof. Background technique [0002] At present, the heating series used in the market include positive temperature coefficient thermistor material (referred to as PTC) heating components, carbon slurry electric heating film heating components, but their heating is slow, low power, low temperature and are subject to many restrictions, there are also on the market Many high-power, high-temperature resistance wire heating components and nickel-chromium heating components have short lifespan, low thermal efficiency, and unsafe etc., so that their application fields are subject to many restrictions. Later, many foreign companies developed various Electronic paste, which is applied to non-metallic materials such as ceramic substrates and polymer ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/14C03C12/00C03C10/14C03C3/087
CPCC03C8/04C03C8/16C03C3/093C03C2207/04
Inventor 吴胜红邓泰均
Owner TAIYANG ELECTRONICS DONGGUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com