Fibre veneer board and its production method

A production method and plywood technology, applied in the field of fiber plywood, can solve the problems of uneven thickness, low strength, and large strength fluctuation of plywood, and achieve the effects of smooth surface, accurate product size, and high material utilization rate

Inactive Publication Date: 2005-06-08
吴小凤
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This is also the main reason why the cost of plywood is higher than that of MDF
[0006] (2) It is difficult to control the quality of the production process
[0007] ① Large thickness deviation
Due to factors such as wood species, tree age and moisture content, the thickness of the veneer cut out by rotary cutting is inconsistent after drying, which brings difficulties to the formation of boards
At the same time, the wood species and tree age are different, and the compression rate is not consistent when they are formed under the same pressure, which will easily cause uneven thickness of the plywood.
[0008] ② Large fluctuations in intensity
[0009] ③Large warping deformation
[0018] (1) The process of fiber separation and drying consumes a lot of energy
[0019] (2) Low strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fibre veneer board and its production method
  • Fibre veneer board and its production method
  • Fibre veneer board and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Single-sided wood-grain decorative fiberboard: choose veneer with better texture, such as beech, willow, walnut, etc., glue on one side, and glue the glued side to the fiber layer, see figure 1 shown.

Embodiment 2

[0049] Double-sided wood grain decorative fiberboard: the veneer used for the bottom board and the front panel, the inner surface of which is glued and bonded with the middle fiber layer, as shown in Figure 2.

Embodiment 3

[0051] Two-layer veneer strong fiberboard:

[0052] The order of arrangement from bottom to surface is: veneer (longitudinal), inner surface glued → fiber layer → veneer (horizontal), double-sided glued → fiber layer. See Figure 3.

[0053] The veneer is arranged vertically or horizontally or vertically and horizontally, which can be determined according to the stress situation during use, and most of them should be vertically and horizontally arranged.

[0054] Between the veneer and the veneer, a layer of fiber layer should be laid. Because after the wood is peeled and dried, it is inevitable that there will be cracks. Defects such as holes and wood grain grooves, if the veneers are bonded to each other, will form voids, reduce strength, and are not beautiful. If there is a fiber layer between the veneers, the fiber can fill these gaps, the reinforcing effect is remarkable, and the strength is high and stable.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A fibrous plyboard is prepared from at least one single board, and at least one fibrous layer through providing single board(s), providing fibres, shaping raw board, prepressing, hot pressing, and post-treating.

Description

technical field [0001] The invention relates to the technical field of multilayer composite boards, in particular to a fiber-reinforced board. Background technique [0002] At present, the most widely used wood-based panels are mainly plywood and medium density fiberboard (hereinafter referred to as MDF). Both have pros and cons. [0003] Plywood is made by cutting logs into veneers of a certain thickness, drying (reducing the moisture content to below 14%), sizing, arranging boards to form blanks (generally vertical and horizontal lamination), and pressing. The advantages are simple equipment, short process flow, low energy consumption in the production process, basically no three wastes, light product quality (density is generally around 0.5, related to wood species and molding pressure), high strength (most of the static bending strength can reach 50Mpa or more), use a good veneer as the bottom, and the panel has a very beautiful wood texture after sanding. [0004] Pl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/04B32B21/00
Inventor 吴小凤
Owner 吴小凤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com