Non-aqueous electrolyte battery

A non-aqueous electrolyte and battery technology, applied in the direction of non-aqueous electrolyte batteries, non-aqueous electrolyte batteries, non-aqueous electrolytes, etc., can solve the problems of insufficient improvement of cycle characteristics, reduced battery characteristics, and weak covering films

Inactive Publication Date: 2005-03-09
SANYO ELECTRIC CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] In addition, as shown in the above-mentioned patent document 2, when only α-angelica lactone is added to the electrolyte, since the covering film (SEI) formed on the surface of the carbon negative electrode is very weak, it is difficult to sufficiently suppress the carbon negative electrode. side reactions associated with organic solvents
This causes a problem that the cycle characteristics are not sufficiently improved.
[0014] In addition, as shown in the above-mentioned patent document 3, when using a non-aqueous electrolytic solution in which a cyclic carbonate having a carbon-carbon unsaturated bond such as VC is added to a cyclic carboxylate, it is possible to obtain Lithium secondary battery with excellent charge and discharge characteristics, but when a large amount of cyclic carboxylate or VC is used, the capacity will decrease due to reduction and decomposition, and the negative electrode surface coating film with hardness and thickness more than required will be formed ( Problems such as degradation of battery characteristics due to SEI) and gas generation due to SEI decomposition during high-temperature storage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-aqueous electrolyte battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Hereinafter, an embodiment of the present invention will be described, but the present invention is not limited to the embodiment, and can be implemented with appropriate changes within a range that does not change the object of the present invention. and, figure 1 It is a partially cutaway perspective view schematically showing a state in which the main part of the non-aqueous electrolyte battery of the present invention is cut longitudinally.

[0023] 1. Fabrication of positive electrode

[0024] Lithium cobalt oxide (LiCoO 2 ) powder, acetylene black as a conductive agent, and fluororesin as a binder were mixed at a mass ratio of 90:5:5 to prepare a positive electrode mixture. N-methyl-2-pyrrolidone (NMP) was added to this positive electrode mixture and mixed to form a slurry. Thereafter, the slurry was applied to both surfaces of a positive electrode current collector made of aluminum foil by a doctor blade method to form a positive electrode mixture layer. Then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

A non-aqueous electrolyte battery with improved cyclic characteristics and battery capacity at high temperature and capable of suppressing the evolution of gas during storage at high temperature while maintaining favorable cyclic performance, wherein vinylene carbonate (VC) and alpha-angelica lactone (4-hydroxy-3-pentenic acid gamma-lactone) are contained in the electrolyte, and whereby a highly soft and flexible coating film with alpha-angelica lactone is formed on the surface of the negative electrode without reducing the initial charging efficiency of the battery. Since a mixed coating film comprising VC and alpha-angelica lactone is formed on the soft and flexible coating film and the mixed coating film has higher thermal stability at high temperature than that of the coating film formed only with VC, the cyclic characteristics of the battery at high temperature can be improved while enhancing the suppression of gas evolution during storage at high temperature.

Description

technical field [0001] The present invention relates to a negative electrode capable of reversibly inserting and detaching lithium, a positive electrode capable of reversibly inserting and detaching lithium at a noble potential, a separator separating these positive electrodes and negative electrodes, and a lithium salt formed by dissolving in an organic solvent A non-aqueous electrolyte battery composed of a solute electrolyte. Background technique [0002] In recent years, non-aqueous electrolyte batteries represented by lithium secondary batteries have been put into practical use as small, lightweight and high-capacity batteries, and are used in portable electronic devices such as small cameras, mobile phones, and notebook computers. In the power supply of communication equipment, etc. Such a lithium secondary battery is a battery configured as follows, that is, a material capable of intercalating and detaching lithium ions is used as the negative electrode active materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/05H01M6/16H01M10/052H01M10/0567H01M10/0569
CPCH01M10/0587H01M10/0567H01M10/0569H01M2004/027H01M2300/004H01M2300/0042H01M10/0525Y02E60/122H01M4/133H01M4/131Y02E60/10
Inventor 岩永征人大贺敬介大下竜司高桥昌利
Owner SANYO ELECTRIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com