Automobile paint cover glaze and preparation method thereof

A technology of automotive paint and top glaze, which is applied to biocide-containing paints, coatings, antifouling/underwater coatings, etc., can solve the problem of damaging the automotive paint surface, and achieve good cleaning effect and strong cleaning and decontamination capabilities Effect

Pending Publication Date: 2022-07-29
广东优贝科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glaze is a colorless or colored vitreous thin layer covering the surface of ceramic products. In the field of car cleaning, the use of glaze is also involved. In order to prolong the service life of the car paint surface, the prior art usually cleans the car , waxing, but too many times of cleaning will inevitably damage the car paint surface, so it is necessary to develop a car paint glaze, which can effectively remove the stains on the car paint surface and at the same time form a protective layer on the car surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automobile paint cover glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] see attached figure 1 As shown, an automobile paint surface glaze and a preparation method thereof include the following parts: 4 parts of carnauba wax; 8 parts of DC silicone oil; 7 parts of D80; 10 parts of D40; 2 parts of S-80; 7 parts of Z89 powder; 55 parts of ionized water; 0.5 part of triethanolamine; 0.02 part of kf-88 bactericide; wherein, D80 is D80 solvent oil, D40 is D40 solvent oil, and S-80 is S-80 emulsifier.

[0022] In this embodiment, the DC silicone oil includes the following parts: 4 parts of DC-350 silicone oil; 3 parts of DC-1000 silicone oil; 0.5 part of DC-12500 silicone oil; 0.5 part of DC-345 silicone oil.

[0023] The preparation method of the automobile paint finish glaze of the present embodiment comprises the following steps:

[0024] S1. Weigh carnauba wax, DC-350 silicone oil, DC-1000 silicone oil, DC-12500 silicone oil, DC-345 silicone oil, D80, D40, S-80, Z89 powder, deionized water, triethanolamine, kf-88 bactericide, then D80, D40, ...

Embodiment 2

[0033] see attached figure 1 As shown, a kind of automobile paint surface glaze and preparation method thereof, comprising the following parts: 5 parts of carnauba wax; 12 parts of DC silicone oil; 9 parts of D80; 14 parts of D40; 3 parts of S-80; 9 parts of Z89 powder; 65 parts of ionized water; 1 part of triethanolamine; 0.08 part of kf-88 bactericide; D80 is D80 solvent oil, D40 is D40 solvent oil, and S-80 is S-80 emulsifier.

[0034] In this embodiment, the DC silicone oil includes the following parts: 5 parts of DC-350 silicone oil; 4 parts of DC-1000 silicone oil; 1.5 parts of DC-12500 silicone oil; and 1.5 parts of DC-345 silicone oil.

[0035] The preparation method of the automobile paint finish glaze of the present embodiment comprises the following steps:

[0036] S1. Weigh carnauba wax, DC-350 silicone oil, DC-1000 silicone oil, DC-12500 silicone oil, DC-345 silicone oil, D80, D40, S-80, Z89 powder, deionized water, triethanolamine, kf-88 bactericide, then D80, ...

Embodiment 3

[0045] see attached figure 1 As shown, an automobile paint surface glaze and a preparation method thereof include the following parts: 4.5 parts of carnauba wax; 10 parts of DC silicone oil; 8 parts of D80; 12 parts of D40; 2.5 parts of S-80; 8 parts of Z89 powder; 60 parts of ionized water; 0.75 part of triethanolamine; 0.05 part of kf-88 bactericide; D80 is D80 solvent oil, D40 is D40 solvent oil, and S-80 is S-80 emulsifier.

[0046] In this embodiment, the DC silicone oil includes the following parts: 4.5 parts of DC-350 silicone oil; 3.5 parts of DC-1000 silicone oil; 1.0 part of DC-12500 silicone oil; 1.0 part of DC-345 silicone oil.

[0047] The preparation method of the automobile paint finish glaze of the present embodiment comprises the following steps:

[0048] S1. Weigh carnauba wax, DC-350 silicone oil, DC-1000 silicone oil, DC-12500 silicone oil, DC-345 silicone oil, D80, D40, S-80, Z89 powder, deionized water, triethanolamine, kf-88 bactericide, then D80, D40,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an automobile paint cover glaze and a preparation method thereof.The automobile paint cover glaze is prepared from carnauba wax, DC-350 silicone oil, DC-1000 silicone oil, DC-12500 silicone oil, DC-345 silicone oil, D80, D40, S-80, Z89 powder, deionized water, triethanolamine and a kf-88 bactericide, so that the prepared paint cover glaze has high cleaning and decontamination capacity and disinfection and sterilization effects and is colorless, odorless, non-toxic and non-corrosive; and a soft and smooth protective layer is formed on the surface of the automobile after cleaning.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to an automobile paint surface glaze and a preparation method thereof. Background technique [0002] Glaze is a colorless or colored vitreous thin layer covering the surface of ceramic products. In the field of car cleaning, the use of glaze will also be involved. In order to prolong the service life of the car paint surface, the existing technology usually cleans the car. , waxing, but too many times of cleaning will inevitably damage the car paint, so it is necessary to develop a car paint glaze, which can effectively remove the stains on the car paint and form a protective layer on the car surface. SUMMARY OF THE INVENTION [0003] In view of the deficiencies of the prior art, the purpose of the present invention is to provide a car paint finish glaze with good cleaning effect and sterilization and disinfection function and a preparation method thereof. [0004] In o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D191/06C09D7/63C09D5/14
CPCC09D183/04C09D7/63C09D5/14C08L83/04C08L91/06C08K5/17
Inventor 骆国清梁樱莉
Owner 广东优贝科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com