Permeable crystallization type waterproof agent doped in concrete

A technology of osmotic crystallization and concrete, which is applied in the field of concrete waterproofing agent, which can solve the problems of poor waterproofing effect, lack of multiple anti-seepage ability, slow concrete repair and healing rate, etc., and achieve the effect of improving strength and saving costs

Pending Publication Date: 2022-05-17
黑将军渗漏修缮工程(辽宁)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of permeable crystalline waterproofing agent mixed in concrete to solve the problems in the prior art that most of the concrete waterproofing agents have poor effects, the healing rate of concrete repair is slow, and they do not have the ability of multiple times of impermeability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permeable crystallization type waterproof agent doped in concrete
  • Permeable crystallization type waterproof agent doped in concrete
  • Permeable crystallization type waterproof agent doped in concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of permeable crystalline waterproofing agent mixed in concrete, in terms of mass percentage, the components and contents are as follows:

[0022] Rice husk ash 10%, modified diatomite 20%, nano-alumina 15%, calcium sulfate 3%, sodium aluminate 5%, sodium methyl silicate 10%, sodium polyacrylate 0.5%, polyvinyl alcohol 2% , sodium sulfate 5%, sodium bicarbonate 2%.

[0023] The specification requirements of each component are as follows:

[0024] Rice husk ash ≥ 325 mesh; modified diatomite 1250 mesh; nano-alumina specification 50nm; calcium sulfate, purity 98%; sodium aluminate, purity 98%; sodium methyl silicate, purity 95%; polyacrylic acid Sodium, food grade; polyvinyl alcohol, type 2488; sodium sulfate, 99% pure; sodium bicarbonate, food grade.

[0025] A kind of preparation method of osmotic crystalline waterproofing agent mixed in concrete, it is characterized in that, comprises the following steps:

[0026] Step (1), initial mixing and stirring:

[002...

Embodiment 2

[0031] A kind of permeable crystalline waterproofing agent mixed in concrete, in terms of mass percentage, the components and contents are as follows:

[0032] Rice husk ash 15%, modified diatomaceous earth 30%, nano-alumina 18%, calcium sulfate 4%, sodium aluminate 7%, sodium methyl silicate 15%, sodium polyacrylate 8%, polyvinyl alcohol 4% , Sodium Sulfate 7%, Sodium Bicarbonate 4%.

[0033] The specification requirements of each component are as follows:

[0034] Rice husk ash ≥ 325 mesh; modified diatomite 1250 mesh; nano-alumina specification 50nm; calcium sulfate, purity 98%; sodium aluminate, purity 98%; sodium methyl silicate, purity 95%; polyacrylic acid Sodium, food grade; polyvinyl alcohol, type 2488; sodium sulfate, 99% pure; sodium bicarbonate, food grade.

[0035] A kind of preparation method of osmotic crystalline waterproofing agent mixed in concrete, it is characterized in that, comprises the following steps:

[0036] Step (1), initial mixing and stirring: ...

Embodiment 3

[0041] A kind of permeable crystalline waterproofing agent mixed in concrete, in terms of mass percentage, the components and contents are as follows:

[0042] Rice husk ash 20%, modified diatomite 40%, nano-alumina 20%, calcium sulfate 5%, sodium aluminate 10%, sodium methyl silicate 20%, sodium polyacrylate 1%, polyvinyl alcohol 5% , sodium sulfate 8%, sodium bicarbonate 6%.

[0043] The specification requirements of each component are as follows:

[0044] Rice husk ash ≥ 325 mesh; modified diatomite 1250 mesh; nano-alumina specification 50nm; calcium sulfate, purity 98%; sodium aluminate, purity 98%; sodium methyl silicate, purity 95%; polyacrylic acid Sodium, food grade; polyvinyl alcohol, type 2488; sodium sulfate, 99% pure; sodium bicarbonate, food grade.

[0045] A kind of preparation method of osmotic crystalline waterproofing agent mixed in concrete, it is characterized in that, comprises the following steps:

[0046] Step (1), initial mixing and stirring:

[0047...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is applicable to the technical field of concrete waterproofing agents, and provides a concrete internally-doped permeable crystallization type waterproofing agent which comprises the following components: rice hull ash, modified diatomite, nano aluminum oxide, calcium sulfate, sodium aluminate, sodium methyl silicate, sodium polyacrylate, polyvinyl alcohol, sodium sulfate and sodium bicarbonate. In order to solve the problems of poor effect of most concrete waterproofing agents, low concrete repairing and healing rate and no repeated impermeability, the finished product obtained in the invention can improve the strength, the impermeability and the internal compactness of the concrete, the concrete structure can be automatically repaired and healed under the action of crystallization even if the concrete structure is locally damaged and leaked (the crack is less than 0.6 mm), and the concrete waterproof agent has the repeated impermeability and can be used for repairing and healing the concrete. The waterproof agent is prepared from the rice hull ash, so that fissure seepage caused by unstable size of a common concrete structure is essentially changed, the waterproof agent has a permanent waterproof effect, and the waterproof agent takes the rice hull ash as one of the main components, is environment-friendly and economical, and saves the cost.

Description

technical field [0001] The invention relates to the technical field of concrete waterproofing agent, in particular to a osmotic crystalline waterproofing agent mixed in concrete. Background technique [0002] Concrete waterproofing agent can significantly improve the impermeability and waterproof function of concrete, and the impermeability grade can reach above P25. At the same time, it has the functions of retarding, early strength, water reduction, and crack resistance, and can improve the workability of fresh mortar: it can replace lime Paste is especially suitable for concrete for bungalow roofs, large-volume waterproof concrete, hydraulic concrete, waterproof mortar, etc. It can completely cure roof leakage, wall dampness, and ground water seepage. It is currently the cheapest, ideal, and reliable preferred material. [0003] Most of the existing concrete waterproofing agents are poor in effect, the healing rate of concrete repair is slow, and they do not have the abil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/42C04B103/65
CPCC04B40/0039C04B2103/65C04B22/0006C04B22/06C04B22/143C04B22/0093C04B24/42C04B24/2641C04B24/2623C04B22/147C04B22/106Y02W30/91
Inventor 胡金亮高岩李实滕达赵群
Owner 黑将军渗漏修缮工程(辽宁)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com