A decorative paint, environmental protection technology, applied in the direction of coating, can solve the problems of environmental pollution, tire loss, waste of resources, etc., to achieve the effect of good adhesion, low cost and fast drying

Pending Publication Date: 2022-05-10
QINGDAO XINGGUO PAINT CHEM
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, with the improvement of human living standards, every family has 1 to 2 cars, and car tires need to be replaced every 5 to 8 kilometers. A large number of tires are thrown away and left idle, causing a lot of resources to be wasted , and cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A preparation method of water-based environment-friendly tire decorative paint, comprising:

[0026] Add the dispersant to the water and mix evenly to obtain the first solution;

[0027] Add titanium dioxide, silica powder, and heavy calcium powder to the first solution in sequence, and mix evenly to obtain the second solution;

[0028] Adding a defoamer to the second solution and grinding to obtain a third solution;

[0029] Add acrylic acid emulsion and other additives to the third solution, and mix well to obtain the fourth solution;

[0030] Add color paste to the fourth solution to adjust various colors, filter and pack the product.

[0031] In some embodiments, a high-speed stirrer is used for mixing the dispersant at a speed of 400 r / min.

[0032] In some embodiments, the mixing speed of titanium dioxide, silica powder, and heavy calcium powder is above 1000 r / min, and the mixture is stirred for 15-20 minutes.

[0033] In some embodiments, the mixing speed of...

Embodiment 1

[0037] Recipe (parts)

[0038] Purified water: 19.5 5040 dispersant: 0.45

[0039] Rutile titanium dioxide: 12.7 1250 mesh wollastonite powder: 13

[0040] 2500 mesh calcite powder: 11 silicone 202 defoamer: 0.25

[0041] Acrylic emulsion: 37.5 Alcohol ester twelve (film-forming aid): 1.5

[0042] Fungicide: 0.25 Propylene Glycol: 1.1

[0043] Association type increaser DR180: 0.75

[0044] Various water-based colorants: 2.

[0045] process flow

[0046] ①Clean the container first and put in pure water according to the formula.

[0047] ② Weigh out 5040 dispersant and put it into the container.

[0048] ③ Turn on the high-speed mixer and adjust the speed to 400r / min.

[0049] ④ Add titanium dioxide, silica powder, heavy calcium powder (calcite powder) slowly in turn, stir at high speed (above 1000r / min) for 15 minutes, add defoamer and start grinding into another container.

[0050] ⑤ Add acrylic emulsion and other additives, disperse and stir at high speed (above 100...

Embodiment 2

[0053] Recipe (parts)

[0054] Purified water: 25 5040 Dispersant: 0.4

[0055] Rutile titanium dioxide: 15 1250 mesh wollastonite powder: 10.5

[0056] 2500 mesh calcite powder: 10 Silicone 202 defoamer: 0.2

[0057] Acrylic emulsion: 35 Alcohol ester dodeca (film-forming aid): 1.2

[0058] Fungicide: 0.2 Propylene Glycol: 1

[0059] Association type increaser DR180: 0.5

[0060] Various water-based colorants: 1.

[0061] process flow

[0062] ①Clean the container first and put in pure water according to the formula.

[0063] ② Weigh out 5040 dispersant and put it into the container.

[0064] ③ Turn on the high-speed mixer and adjust the speed to 400r / min.

[0065] ④ Add titanium dioxide, silica powder, heavy calcium powder (calcite powder) slowly in turn, stir at high speed (above 1000r / min) for 15 minutes, add defoamer and start grinding into another container.

[0066] ⑤ Add acrylic emulsion and other additives, disperse and stir at high speed (above 1000r / min) fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of coating decoration, and relates to a water-based environment-friendly tire decorative paint, which is prepared from the following raw materials in parts by weight: 15 to 20 parts of water, 0.4 to 0.5 part of dispersing agent, 10 to 13 parts of rutile titanium dioxide, 10 to 15 parts of wollastonite powder, 10 to 12 parts of calcite powder, 0.2 to 0.3 part of organic silicon defoaming agent, 35 to 40 parts of acrylic emulsion, 1.2 to 2 parts of coalescing agent, 0.2 to 0.3 part of sterilizing agent, 1 to 1.2 parts of propylene glycol, 0.5 to 1 part of associated turning-over agent and 1 to 3 parts of water-based color paste. The water paint is non-toxic, odorless, free of heavy metal, easy to coat, fast to dry, durable, good in adhesive force, weather-proof and free of falling off. Waste is turned into wealth, and single and ugly black tires are turned into various bright ornaments. And the paint is very suitable for children to do it yourself (DIY) at home or in a kindergarten, gives full play to imagination, can be painted by themselves, becomes a body-building toy, is safe and environment-friendly, is also used for various outdoor flowerpots and other ornaments such as handicrafts and sofas, and brings new colors to the ornaments.

Description

technical field [0001] The invention belongs to the field of coating decoration, in particular to a water-based environment-friendly tire decoration paint. Background technique [0002] The information disclosed in this background section is only intended to increase the understanding of the general background of the present invention, and is not necessarily taken as an acknowledgment or any form of suggestion that the information constitutes the prior art already known to those skilled in the art. [0003] At present, with the improvement of human living standards, every family has 1 to 2 cars, and car tires need to be replaced every 5 to 8 kilometers. A large number of tires are thrown away and left idle, causing a lot of resources to be wasted , and cause environmental pollution. [0004] Therefore, it is urgent to invent a kind of environment-friendly tire decoration paint, which can turn waste into treasure, and turn the single ugly black tire into various bright decor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D7/61C09D7/63
CPCC09D133/00C09D7/61C09D7/63C08K2003/2241C08K2003/265C08K3/22C08K3/34C08K3/26C08K5/053
Inventor 刘慧慧刘彩霞刘泊辰安佰鹤刘炳义
Owner QINGDAO XINGGUO PAINT CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap