Flame-retardant and fireproof sealant and preparation method thereof

A fireproof sealant and flame retardant technology, applied in adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve the problems of lack of flame retardant and fireproof effects, increase of flame retardants, poor flame retardant effect, etc.

Active Publication Date: 2022-01-04
东莞市山力高分子材料科研有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it lacks flame retardant and fire prevention effects, and continues to improve
[0004] In order to improve the fire prevention effect of silicone sealants, adding flame retardants to silicone sealants is a common solution; , its flame retardant effect is not good; to improve the flame retardant effect, it is necessary to greatly increase the amount of flame retardant; but the result of increasing the amount of flame retardant is that the bonding performance of silicone sealant decreases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant and fireproof sealant and preparation method thereof
  • Flame-retardant and fireproof sealant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The preparation of embodiment 1 flame retardant fireproof sealant

[0030] Composition in parts by weight of raw materials: 85 parts of polydimethylsiloxane; 8 parts of crosslinking agent; 1 part of catalyst; 3 parts of dispersant; 5 parts of plasticizer;

[0031] Described flame retardant is made up of zinc borate and magnesium carbonate that weight ratio is 4:1;

[0032] The preparation method of flame retardant and fireproof sealant: first put polydimethylsiloxane, dispersant and flame retardant into a high-speed mixer, and stir for 20 minutes under a vacuum of -0.06Mpa; then add a crosslinking agent and a catalyst, Stir for 150 minutes under a vacuum of -0.08Mpa to obtain the flame retardant and fireproof sealant.

Embodiment 2

[0033] The preparation of embodiment 2 flame retardant fireproof sealant

[0034] Composition in parts by weight of raw materials: 85 parts of polydimethylsiloxane; 8 parts of crosslinking agent; 1 part of catalyst; 3 parts of dispersant; 5 parts of plasticizer;

[0035] The flame retardant is a modified flame retardant, and the modified flame retardant is prepared by the following method: zinc borate and magnesium carbonate (the weight ratio of zinc borate and magnesium carbonate is 4:1) are dispersed in the volume Add N-(2-aminoethyl)-3-aminopropyltrimethoxysilane and sodium lignosulfonate to an aqueous ethanol solution with a fraction of 50% and stir evenly; then grind at a temperature of 50° C. for 8 hours; After the grinding is finished, the grinding slurry is dried to obtain the modified flame retardant; wherein, the total weight of zinc borate and magnesium carbonate and ethanol aqueous solution and N-(2-aminoethyl)-3-aminopropyltrimethyl The dosage ratio of oxysilane ...

experiment example 1

[0063] The flame-retardant and fire-proof sealants prepared in Examples 1 and 2 and Comparative Examples 1 to 5 were made into a sample strip with a length of 100mm, a width of 6mm, and a thickness of 3mm; refer to GB / T 2406.2-2009 to test the flame-retardant and fire-proof sealant sample in The minimum oxygen concentration (oxygen index) required to maintain balanced combustion in the oxygen-nitrogen mixed flow; the higher the oxygen index, the better the fire and flame retardant effect; the test results are shown in Table 1.

[0064] Table 1. Fireproof effect test of flame retardant and fireproof sealant

[0065]

[0066]

[0067] As can be seen from the test data in Table 1, the flame retardant and fireproof effect of the flame retardant and fireproof sealant of embodiment 1 is obviously better than that of comparative examples 1 and 2, which shows that the preparation of flame retardant and fireproof sealant with polydimethylsiloxane is a raw material. Glue, adding a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of sealant preparation, and particularly discloses a flame-retardant and fireproof sealant and a preparation method thereof. The flame-retardant and fireproof sealant is prepared from the following raw material components in parts by weight: 80-100 parts of polydimethylsiloxane; 5-10 parts of a cross-linking agent; 0.5-2 parts of a catalyst; 3-6 parts of a dispersant; 1-10 parts of a plasticizer; and 1-5 parts of a flame retardant. The flame retardant is composed of zinc borate and anhydrous magnesium carbonate. Research shows that in the process of preparing the flame-retardant and fireproof sealant by taking polydimethylsiloxane as a raw material, the flame retardant composed of zinc borate and anhydrous magnesium carbonate is added, and a certain fireproof and flame-retardant effect can be achieved under the condition that only a small amount of flame retardant is added.

Description

technical field [0001] The invention relates to the technical field of sealant preparation, in particular to a flame-retardant and fireproof sealant and a preparation method thereof. Background technique [0002] Sealant is an adhesive used to fill the configuration gap to play a sealing role. It needs to be deformed with the shape of the sealing surface, not easy to flow, and has a certain degree of cohesion; it can prevent leakage, waterproof, vibration and sound insulation, etc. At least one or more effects. [0003] Silicone sealant is a paste made of polydimethylsiloxane as the main raw material, supplemented with crosslinking agent, filler, plasticizer, coupling agent and catalyst in a vacuum state. Chinese invention patent 201110223644.3 discloses an acidic silicone sealant, which uses α-ω-dihydroxy-terminated polysiloxane: 50-80 parts, cross-linking agent: 2-10 parts, filler: 2-15 parts, Catalyst: 0.1-0.2 parts, plasticizer: 1-20 parts, adhesion promoter: 0-5 parts...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J183/04C09J11/04
CPCC09J183/04C09J11/04C08K2003/387C08K2003/267C08K3/38C08K3/26C08K9/06C08K9/08
Inventor 罗伟雄
Owner 东莞市山力高分子材料科研有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap