Weather-resistant and aging-resistant cement-based flexible facing brick manufacturing method and manufactured flexible facing brick

A cement-based and flexible-based technology, which is applied in the field of building decoration materials, can solve the problems of weather resistance, low aging resistance, waste, and large difference of flexible facing bricks, and achieve beautiful decorative effects, reduced maintenance costs, and excellent overall performance. Effect

Pending Publication Date: 2021-11-09
许敬修
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The weather resistance and aging resistance of the existing flexible decorative bricks are low. According to the national industry standard "Flexible Decorative Bricks"
[0003] It is required that the aging resistance time of its artificial aging resistance is only 500-1000h, which is much different from the service life of building exterior wall insulation > 25 years, and the difference is even greater than that of building service life > 50 years. , Multiple replacements within the life cycle of the building, resulting in waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The weather-resistant and aging-resistant cement-based flexible decorative brick consists of the following raw materials in parts by weight:

[0032] Cement-based decorative layer parts by weight Low alkalinity sulphoaluminate cement 45 600 mesh sericite powder treated by silanization 10 Silanized 100 mesh quartz sand 20 pigment 2 Naphthalene superplasticizer 0.4 Dispersant 1.0 Defoamer 0.1 Acrylic Emulsion 11.5 Deionized water 10

[0033] cement base parts by weight Low alkalinity sulphoaluminate cement 45 600 mesh sericite powder treated by silanization 10 Silanized 100 mesh quartz sand 20 Naphthalene superplasticizer 0.4 Dispersant 1.0 Defoamer 0.1 Acrylic Emulsion 11 Silanized 6mm glass fiber 0.5 Deionized water 12

Embodiment 2

[0035] The preparation method of this kind of weather-resistant and aging-resistant cement-based flexible decorative brick comprises the following steps, described in conjunction with Example 1:

[0036]The preparation of the cement-based decorative layer slurry: add corresponding parts of acrylate emulsion and deionized water into the mixing tank, start the mixer, slowly add corresponding parts of A pigment, corresponding parts The number of dispersants, the corresponding number of antifoaming agents, the corresponding number of naphthalene-based water reducers, and stir for 30 minutes; at the speed of 100r / min, slowly add the corresponding number of naphthalene-based water reducers, the corresponding number of Silanized 600-mesh sericite powder and the corresponding number of silanized 100-mesh quartz sand were stirred for 10 minutes; at a speed of 80 r / min, slowly added the corresponding number of cement and stirred for 3 minutes, so that A color Cement-based decorative lay...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

A weather-resistant and aging-resistant cement-based flexible facing brick disclosed by the invention comprises a cement-based decorative layer and a cement-based matrix. The cement-based decorative layer is prepared from, by weight, 30-80 parts of cement, 30-80 parts of fine aggregate, 0.6-6 parts of pigment, 6-40 parts of mixed glue solution of polymer emulsion or redispersible polymer glue powder and water, and 3-20 parts of water. The cement-based matrix is prepared from, by weight, 30-80 parts of cement, 30-120 parts of fine aggregate, 6-40 parts of mixed glue solution of polymer emulsion or redispersible polymer glue powder and water, and 5-40 parts of water. The flexible facing brick has the remarkable advantages of extremely excellent durability and weather resistance. After 2160 hours of all-weather aging test, the performance of the flexible facing brick is still the same as that of cement mortar and even slightly improved, while the existing product can only lasts 500-1000 hours. The flexible facing brick is exquisite in decoration effect, excellent in comprehensive performance, low in cost and suitable for building outer walls, inner walls and roofs.

Description

technical field [0001] The invention belongs to the technical field of production of building decoration materials, and in particular relates to a weather-resistant and aging-resistant cement-based flexible decorative brick and a manufacturing method thereof. Background technique [0002] The weather resistance and aging resistance of the existing flexible decorative bricks are low. According to the national industry standard "Flexible Decorative Bricks" [0003] It is required that the aging resistance time of its artificial aging resistance is only 500-1000h, which is much different from the service life of building exterior wall insulation > 25 years, and the difference is even greater than that of building service life > 50 years. , The building is replaced many times during the life cycle, resulting in waste. Therefore, it is of great significance to improve the weather resistance and aging resistance of flexible facing bricks. Contents of the invention [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B28/04C04B111/20
CPCC04B28/06C04B28/04C04B2111/00612C04B2111/20C04B14/20C04B14/06C04B2103/54C04B2103/302C04B2103/408C04B2103/50C04B24/2641C04B14/42
Inventor 许浒许敬修
Owner 许敬修
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com