Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of camellia fibers

A camellia and fiber technology, applied in the dyeing method, removing liquid/gas/steam with squeeze rollers, treating textile material carriers, etc., can solve the problems of high price and achieve the goals of increasing adhesion, reducing quantity, and increasing the amount of addition Effect

Inactive Publication Date: 2021-10-29
郑州诺肯新材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, camellia fiber is heavily dependent on Japanese imports, and the production process of Yamatobo in Japan is a blended spinning method. The camellia fiber produced is light pink and expensive
In order to meet the growing demand of domestic customers, we changed the process route and adopted the post-finishing method to produce camellia fiber, which has not yet been reported on industrialization in China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of camellia fibers
  • Preparation method of camellia fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0036] Example: as attached figure 1 Shown, a kind of preparation method of camellia fiber, described preparation method comprises the following steps:

[0037] (1) Preparation of camellia extract solution

[0038] Put the camellia extract powder in deionized water at 50°C, add dispersant and reactive dyes, stir with an electric mixer for 1 hour, let it stand for precipitation, take the supernatant, filter twice with a 200-mesh filter, and extract the camellia in the resulting mixed solution The solid content is 10%.

[0039] (2) Pengrun treatment of cationic viscose fiber

[0040] Wet the cationic viscose fiber with deionized water, spray it evenly on the surface of the fiber with a sprayer, and the temperature is 30°C to make the fiber absorb water evenly and expand the fiber. (3) Addition of camellia extract mixed solution

[0041] The cationic viscose fiber is loosened by an opener, and the viscose fiber after opening is placed on the first chain net 6 which rotates ci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of camellia fibers. The preparation method comprises the following steps that (1), a camellia extract solution is prepared; (2), swelling treatment is carried out on cationic viscose fibers; (3), camellia extract fibers are prepared; (4), soft water is sprayed; (5), a softening agent is sprayed; and (6), post-treatment is carried out. The preparation method of the fibers comprises the following steps that firstly, camellia extract powder is uniformly dispersed in deionized water, a dye is added for color matching to prepare the camellia extract mixed solution, and the camellia extract mixed solution is sprayed on the surface of the fiber subjected to swelling treatment in a spraying mode. No strong acid strong alkali is added in the process of absorbing the camellia extract, high temperature is not used, effective components in the camellia extract cannot be damaged, the content of the camellia extract in the prepared fiber is high, and the prepared composite fiber has good spot fading, whitening and skin nourishing performance.

Description

technical field [0001] The invention belongs to the field of light industry textiles, and in particular relates to a preparation method of camellia fiber. Background technique [0002] The textile industry is a traditional industry in China. With the rapid development of clothing, household and industrial textiles, the differentiation and individualization of textile products have become the focus of the development of various enterprises. Functional fibers as high-grade textile raw materials are generally improved by means of physical modification, chemical modification and molecular design to obtain fibers with specific properties, so that the original viscose fibers are stable in light and heat, conductive, Flame retardant, dyeing, antistatic, moisture absorption, fluffy, anti-pilling, anti-fouling and other aspects have been greatly improved. [0003] Regenerated cellulose fiber is made of natural cellulose (cotton, hemp, bamboo, tree, shrub) as raw material, without ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B1/02D06B15/02D06B23/04D06P1/38D06P1/44D06P3/66
CPCD06B1/02D06B23/04D06B15/02D06P1/445D06P1/38D06P3/66D10B2401/13
Inventor 骆祥伟张涛邱纯利樊超
Owner 郑州诺肯新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com